Creep life assessment of aero-engine recuperator based on continuum damage mechanics approach

Abstract

The creep life of an aeroengine recuperator is investigated in terms of continuum damage mechanics by using finite element simulations. The effects of the manifold wall thickness and creep properties of brazing filler metal on the operating life of the recuperator are analyzed. Results show that the crack initiates from the brazing filler metal located on the outer surface of the manifold with the wall thickness of 2 mm and propagates throughout the whole region of the brazing filler metal when the creep time reaches 34900 h. The creep life of the recuperator meets the requirement of 40000 h continuous operation when the wall thickness increases to 3.5 mm, but its total weight increases by 15%. Decreasing the minimum creep strain rate with the enhancement of the creep strength of the brazing filler metal presents an obvious effect on the creep life of the recuperator. At the same stress level, the creep rupture time of the recuperator is enhanced by 13 times if the mismatch between the minimum creep rate of the filler and base metal is reduced by 20%.

Graphical abstract

Keywords

creep / life assessment / brazed joint / continuum damage mechanics / aeroengine recuperator

References

[1] Salpingidou C , Misirlis D , Vlahostergios Z , Flouros M , Donus F , Yakinthos K . Conceptual design study of a geared turbofan and an open rotor aero engine with intercooled recuperated core. Proceedings of the Institution of Mechanical Engineers, Part G: Journal of Aerospace Engineering, 2018, 232(14): 2713–2720

[2] Ricco P , Skote M , Leschziner M A . A review of turbulent skin-friction drag reduction by near-wall transverse forcing. Progress in Aerospace Sciences, 2021, 123: 100713

[3] Wileman A J , Aslam S , Perinpanayagam S . A road map for reliable power electronics for more electric aircraft. Progress in Aerospace Sciences, 2021, 127: 100739

[4] Graver B, Rutherford D, Zheng S. CO₂ emissions from commercial aviation: 2013, 2018, and 2019. Available from International Council on Clean Transportation website, 2020

[5] Ferrari M L , Sorce A , Pascenti M , Massardo A F . Recuperator dynamic performance: experimental investigation with a microgas turbine test rig. Applied Energy, 2011, 88(12): 5090–5096

[6] McDonald C F , Massardo A F , Rodgers C , Stone A . Recuperated gas turbine aeroengines, Part I: early development activities. Aircraft Engineering and Aerospace Techology, 2008, 80(2): 139–157

[7] Boggia S , Rüd K . Intercooled recuperated gas turbine engine concept. In: Proceedings of the 41st AIAA/ASME/SAE/ASEE Joint Propulsion Conference & Exhibit. Tucson: AIAA, 2005, 4192

[8] Rolt A , Baker N . Intercooled turbofan engine design and technology research in the EU framework 6 NEWAC programme. In: Proceedings of International Symposium on Air Breathing Engines. Montreal: ISABE, 2009, 1351–1360

[9] Zhang C Y , Gümmer V . Performance assessment of recuperated rotorcraft powerplants: trade-off between fuel economy and weight penalty for both tubular and primary surface recuperators. Applied Thermal Engineering, 2020, 164: 114443

[10] Kyprianidis K G , Rolt A M . On the optimization of a geared fan intercooled core engine design. Journal of Engineering for Gas Turbines and Power, 2015, 137(4): 041201

[11] Salpingidou C , Vlahostergios Z , Misirlis D , Donnerhack S , Flouros M , Goulas A , Yakinthos K . Thermodynamic analysis of recuperative gas turbines and aero engines. Applied Thermal Engineering, 2017, 124: 250–260

[12] Vlahostergios Z , Misirlis D , Flouros M , Salpingidou C , Donnerhack S , Goulas A , Yakinthos K . Development, numerical investigation and experimental validation of a new recuperator design for aero engines applications. In: Proceedings of ASME Turbo Expo 2017: Turbomachinery Technical Conference & Exposition. Charlotte: ASME, 2017, V02BT41A035

[13] Kormann M , Schaber R . An intercooled recuperative aero engine for regional jets. In: Proceedings of ASME Turbo Expo 2014: Turbine Technical Conference and Exposition. Düsseldorf: ASME, 2014, V03AT07A021

[14] Schoenenborn H , Ebert E , Simon B , Storm P . Thermomechanical design of a heat exchanger for a recuperative aeroengine. Journal of Engineering for Gas Turbines and Power, 2006, 128(4): 736–744

[15] Goulas A , Donnerhack S , Flouros M , Misirlis D , Vlahostergios Z , Yakinthos K . Thermodynamics cycle analysis, pressure loss, and heat transfer assessment of a recuperative system for aero-engines. Journal of Engineering for Gas Turbines and Power, 2015, 137(4): 041205

[16] Zhang Y C , Jiang W C , Tu S T , Zhang X C , Zhou G Y . Analysis of creep crack growth behavior of the brazed joint using continuum damage mechanics approach. In: Proceedings of the ASME 2018 Pressure Vessels and Piping Conference. Prague: ASME, 2018, 51678: V06AT06A062

[17] Luo Y , Jiang W C , Zhang Y C , Zhou F , Tu S T . A new damage evolution model to estimate the creep fracture behavior of brazed joint under multiaxial stress. International Journal of Mechanical Sciences, 2018, 149: 178–189

[18] Tu S T . Emerging challenges to structural integrity technology for high-temperature applications. Frontiers of Mechanical Engineering in China, 2007, 2(4): 375–387

[19] Tu S T , Zhou G Y . Creep of brazed plate-fin structures in high temperature compact heat exchangers. Frontiers of Mechanical Engineering in China, 2009, 4(4): 355–362

[20] Zhang D J , Zeng M , Wang J W , Wang Q W . Creep analysis of cross wavy primary surface recuperator for microturbine system. In: Proceedings of ASME Turbo Expo: Power for Land, Sea, & Air. Berlin: ASME, 2008, 899–904

[21] Jiang W C , Gong J M , Chen H , Tu S T . The effect of filler metal thickness on residual stress and creep for stainless-steel plate–fin structure. International Journal of Pressure Vessels and Piping, 2008, 85(8): 569–574

[22] Shi D Q , Dong C L , Yang X G , Zhang L , Hou J B , Liu Y . Experimental investigations on creep rupture strength and failure mechanism of vacuum brazed joints of a DS superalloy at elevated temperature. Materials Science and Engineering: A, 2012, 545: 162–167

[23] Ma T , Chen Y T , Zeng M , Wang Q W . Stress analysis of internally finned bayonet tube in a high temperature heat exchanger. Applied Thermal Engineering, 2012, 43: 101–108

[24] Chen G , Wang G Z , Xuan F Z , Tu S T . Mismatch effect in creep properties on creep crack growth behavior in welded joints. Materials & Design, 2014, 63: 600–608

[25] Cadek J . Creep in Metallic Materials. Amsterdam: Elsevier, 1988, 372–692

[26] Kassner M E . Fundamentals of Creep in Metals and Alloys. 3rd ed. Oxford: Butterworth-Heinemann, 2015, 261–273

[27] Sklenička V , Kuchařová K , Král P , Kvapilová M , Svobodová M , Čmakal J . The effect of hot bending and thermal ageing on creep and microstructure evolution in thick-walled P92 steel pipe. Materials Science and Engineering: A, 2015, 644: 297–309

[28] Vrchovinsky V , Zrnik J , Kvackaj T , Wangyao P . Effect of final cold rolled microstructures on creep deformation behavior in nickel base alloy. Journal of Metals, Materials and Minerals, 2005, 15(2): 57–68

[29] Zhang Y C , Jiang W C , Tu S T , Zhang X C , Ye Y J . Creep crack growth behavior analysis of the 9Cr-1Mo steel by a modified creep-damage model. Materials Science and Engineering: A, 2017, 708: 68–76

[30] Zhang Y C , Yu X T , Jiang W C , Tu S T , Zhang X C . Elastic modulus and hardness characterization for microregion of Inconel 625/BNi-2 vacuum brazed joint by high temperature nanoindentation. Vacuum, 2020, 181: 109582

[31] Zhang Y C. Creep damage and crack growth analysis of the brazed joint under multi-axial stress state. Dissertation for the Doctoral Degree. Shanghai: East China University of Science and Technology, 2016 (in Chinese)

[32] Lai H S . Estimation of Ct of functionally graded materials under small scale creep stage. Composite Structures, 2016, 138: 352–360

[33] Lee K H . Analysis of a propagating crack tip in orthotropic functionally graded materials. Composites Part B: Engineering, 2016, 84: 83–97

[34] Zhang Y C , Jiang W C , Tu S T , Wen J F , Woo W . Using short-time creep relaxation effect to decrease the residual stress in the bonded compliant seal of planar solid oxide fuel cell―a finite element simulation. Journal of Power Sources, 2014, 255: 108–115

[35] Hyde T H, Xia L, Becker A A. Prediction of creep failure in aeroengine materials under multi-axial stress states. International Journal of Mechanical Sciences, 1996, 38(4): 385–401, 403

[36] Hyde C J , Hyde T H , Sun W , Becker A A . Damage mechanics based predictions of creep crack growth in 316 stainless steel. Engineering Fracture Mechanics, 2010, 77(12): 2385–2402

[37] Kim N H , Oh C S , Kim Y J , Davies C M , Nikbin K , Dean D W . Creep failure simulations of 316H at 550 °C: Part II—Effects of specimen geometry and loading mode. Engineering Fracture Mechanics, 2013, 105: 169–181

[38] Mehmanparast A , Davies C M , Webster G A , Nikbin K M . Creep crack growth rate predictions in 316H steel using stress dependent creep ductility. Materials at High Temperatures, 2014, 31(1): 84–94

[39] Hyde T H , Saber M , Sun W . Testing and modelling of creep crack growth in compact tension specimens from a P91 weld at 650 °C. Engineering Fracture Mechanics, 2010, 77(15): 2946–2957

[40] Zhang Y C , Jiang W C , Tu S T , Zhang X C , Ye Y J , Wang R Z . Experimental investigation and numerical prediction on creep crack growth behavior of the solution treated Inconel 625 superalloy. Engineering Fracture Mechanics, 2018, 199: 327–342

[41] Zhao L, Xu L Y, Han Y D, Jing H Y. Quantifying the constraint effect induced by specimen geometry on creep crack growth behavior in P92 steel. International Journal of Mechanical Sciences, 2015, 94–95: 63–74

[42] Yu Z Y , Wang X M , Liang H , Li Z X , Li L , Yue Z F . Thickness debit effect in Ni-based single crystal superalloys at different stress levels. International Journal of Mechanical Sciences, 2020, 170: 105357

[43] Kurata Y , Saito T , Tsuji H , Takatsu T , Shindo M , Nakajima H . Development of a filler metal for weldments of a Ni-Cr-W superalloy with high creep strength. JSME International Journal Series A: Solid Mechanics and Material Engineering, 2002, 45(1): 104–109

[44] Mayr P , Cerjak H , Jochum C , Pasternak J . Long-term creep behaviour of E911 heat resistant 9% Cr steel weldments fabricated with filler metals of different creep strength. In: Proceedings of ASME Pressure Vessels and Piping Conference. San Antonio: ASME, 2007, 675–680

[45] Baumgartner S , Posch G , Mayr P . Welding advanced martensitic creep-resistant steels with boron containing filler metal. Welding in the World, 2012, 56(7): 2–9

[46] NortonF H. The Creep of Steel at High Temperature. New York: McGraw-Hill, 1929

[47] Kim Y K , Kim D , Kim H K , Oh C S , Lee B J . An intermediate temperature creep model for Ni-based superalloys. International Journal of Plasticity, 2016, 79: 153–175

[48] Ma H L , Zhao B G , Wu G Z , Li Z , Gao Y L . A SnBiAgIn solder alloy with exceptional mechanical properties by rapid quenching. Journal of Materials Science: Materials in Electronics, 2021, 32(6): 8167–8173

Acknowledgements

The work was supported by the National Natural Science Foundation of China (Grant No. 51675181). The authors are also grateful for the Innovation Program of Shanghai Municipal Education Commission, China (Grant No. 2019-01-07-00-02-E00068).

RIGHTS & PERMISSIONS

2022 Higher Education Press