Sputtered Stainless Steel on Silicon Photoanode for Stable Seawater Splitting in Photoelectrochemical Flow Cell

Abstract

Photoelectrochemical (PEC) seawater splitting is a promising method for the direct utilization of solar energy and abundant seawater resources for hydrogen production. Photoelectrodes are susceptible to various ions in seawater and complicated competitive reactions, resulting in the failure of photoelectrodes. This paper proposes the design and fabrication of different sputtered stainless steel (SS) films deposited on silicon photoanodes, completely isolating the electrolytes and semiconductor substrate. Upon coupling with the PEC flow cell, the back-illuminated photoanode coated with 316 SS cocatalyst achieves stable operation for 70 h in natural seawater with a highly alkaline KOH (30 wt.%, 7.64 mol/L) electrolyte due to the remarkable protection effect of the substrate from stainless steel, while the PEC seawater splitting system achieves a record hydrogen production rate of 600 μmol/(h·cm²). An appropriate Ni/Fe ratio in the SS ensures remarkable oxygen evolution activity, while chromic oxide ensures the effective anticorrosion effect by adjusting the microenvironment of the photoanodes. Moreover, fabricating PEC flow cells with photoanodes coated with SS cocatalysts are a viable strategy for PEC seawater splitting.

Keywords

Flow cell / Seawater splitting / Stainless steel / Chloridion / Photoelectrochemical

References

[1] Hu CL, Zhang L, Gong JL Recent progress made in the mechanism comprehension and design of electrocatalysts for alkaline water splitting. Energy Environ Sci, 2019, 12(9): 2620-2645.

[2] Lagadec MF, Grimaud A Water electrolysers with closed and open electrochemical systems. Nat Mater, 2020, 19(11): 1140-1150.

[3] Zheng Y, Qiao SZ Direct seawater splitting to hydrogen by a membrane electrolyzer. Joule, 2023, 7(1): 20-22.

[4] Wang T, Gong JL Sacrificing nothing to reduce CO₂. Nat Energy, 2020, 5(9): 642-643.

[5] Wan GD, Yang YQ, Zhu HZ, et al. Selectively constructing sandwich-like heterostructure of CdS/PbTiO₃/TiO₂ to improve visible-light photocatalytic H₂ evolution. Sci China Mater, 2022, 65(12): 3428-3434.

[6] Dionigi F, Reier T, Pawolek Z, et al. Design criteria, operating conditions, and nickel–iron hydroxide catalyst materials for selective seawater electrolysis. Chemsuschem, 2016, 9(9): 962-972.

[7] Dresp S, Ngo Thanh T, Klingenhof M, et al. Efficient direct seawater electrolysers using selective alkaline NiFe-LDH as OER catalyst in asymmetric electrolyte feeds. Energy Environ Sci, 2020, 13(6): 1725-1729.

[8] Tong WM, Forster M, Dionigi F, et al. Electrolysis of low-grade and saline surface water. Nat Energy, 2020, 5(5): 367-377.

[9] Zhou P, Navid IA, Ma YJ, et al. Solar-to-hydrogen efficiency of more than 9% in photocatalytic water splitting. Nature, 2023, 613(7942): 66-70.

[10] Obata K, Takanabe K A permselective CeO _x coating to improve the stability of oxygen evolution electrocatalysts. Angew Chem Int Ed, 2018, 57(6): 1616-1620.

[11] Bhardwaj AA, Vos JG, Beatty MES, et al. Ultrathin silicon oxide overlayers enable selective oxygen evolution from acidic and unbuffered pH-neutral seawater. ACS Catal, 2021, 11(3): 1316-1330.

[12] Luo WJ, Yang ZS, Li ZS, et al. Solar hydrogen generation from seawater with a modified BiVO₄ photoanode. Energy Environ Sci, 2011, 4(10): 4046-4051.

[13] Gao RT, Guo XT, Liu SJ, et al. Ultrastable and high-performance seawater-based photoelectrolysis system for solar hydrogen generation. Appl Catal B, 2022, 304.

[14] Hu S, Shaner MR, Beardslee JA, et al. Amorphous TiO₂ coatings stabilize Si, GaAs, and GaP photoanodes for efficient water oxidation. Science, 2014, 344(6187): 1005-1009.

[15] Wang HJ, Li X, Zhao XX, et al. A review on heterogeneous photocatalysis for environmental remediation: from semiconductors to modification strategies. Chin J Catal, 2022, 43(2): 178-214.

[16] Schäfer H, Beladi-Mousavi SM, Walder L, et al. Surface oxidation of stainless steel: oxygen evolution electrocatalysts with high catalytic activity. ACS Catal, 2015, 5(4): 2671-2680.

[17] Schäfer H, Sadaf S, Walder L, et al. Stainless steel made to rust: a robust water-splitting catalyst with benchmark characteristics. Energy Environ Sci, 2015, 8(9): 2685-2697.

[18] Wang ZP, Lin ZP, Shen SJ, et al. Advances in designing heterojunction photocatalytic materials. Chin J Catal, 2021, 42(5): 710-730.

[19] Todoroki N, Wadayama T Heterolayered Ni–Fe hydroxide/oxide nanostructures generated on a stainless-steel substrate for efficient alkaline water splitting. ACS Appl Mater Interfaces, 2019, 11(47): 44161-44169.

[20] Li TS, Liu L, Zhang B, et al. An investigation on the continuous and uniform thin membrane passive film formed on sputtered nanocrystalline stainless steel. Corros Sci, 2016, 104: 71-83.

[21] Yiu P, You JD, Wang ST, et al. Tunable hydrophilicity in a surface nano-textured stainless steel thin film deposited by DC magnetron sputtering. Appl Surf Sci, 2021, 555.

[22] Suryanto BHR, Wang Y, Hocking RK, et al. Overall electrochemical splitting of water at the heterogeneous interface of nickel and iron oxide. Nat Commun, 2019, 10(1): 5599.

[23] Schäfer H, Chevrier DM, Kuepper K, et al. X20CoCrWMo10-9//Co₃O₄: a metal–ceramic composite with unique efficiency values for water-splitting in the neutral regime. Energy Environ Sci, 2016, 9(8): 2609-2622.

[24] Kou TY, Wang SW, Li Y Perspective on high-rate alkaline water splitting. ACS Mater Lett, 2021, 3(2): 224-234.

[25] Louie MW, Bell AT An investigation of thin-film Ni–Fe oxide catalysts for the electrochemical evolution of oxygen. J Am Chem Soc, 2013, 135(33): 12329-12337.

[26] Rao RR, Corby S, Bucci A, et al. Spectroelectrochemical analysis of the water oxidation mechanism on doped nickel oxides. J Am Chem Soc, 2022, 144(17): 7622-7633.

[27] Kim JH, Hwang SM, Hwang I, et al. Seawater-mediated solar-to-sodium conversion by bismuth vanadate photoanode- photovoltaic tandem cell: solar rechargeable seawater battery. iScience, 2019, 19: 232-243.

[28] Wang SJ, Wang T, Liu B, et al. Spatial decoupling of light absorption and reaction sites in n-Si photocathodes for solar water splitting. Natl Sci Rev, 2020, 8(8): nwaa293.

[29] Zhao JH, Cai LL, Li H, et al. Stabilizing silicon photocathodes by solution-deposited Ni–Fe layered double hydroxide for efficient hydrogen evolution in alkaline media. ACS Energy Lett, 2017, 2(9): 1939-1946.

[30] Li D, Shi JY, Li C Transition-metal-based electrocatalysts as cocatalysts for photoelectrochemical water splitting: a mini review. Small, 2018, 14(23): 1704179.

[31] McCrory CCL, Jung S, Peters JC, et al. Benchmarking heterogeneous electrocatalysts for the oxygen evolution reaction. J Am Chem Soc, 2013, 135(45): 16977-16987.

[32] Trotochaud L, Young SL, Ranney JK, et al. Nickel-iron oxyhydroxide oxygen-evolution electrocatalysts: the role of intentional and incidental iron incorporation. J Am Chem Soc, 2014, 136(18): 6744-6753.

[33] Anantharaj S, Venkatesh M, Salunke AS, et al. High-performance oxygen evolution anode from stainless steel via controlled surface oxidation and Cr removal. ACS Sustain Chem Eng, 2017, 5(11): 10072-10083.

[34] Guo JX, Zheng Y, Hu ZP, et al. Direct seawater electrolysis by adjusting the local reaction environment of a catalyst. Nat Energy, 2023, 8(3): 264-272.

[35] Ayyub MM, Chhetri M, Gupta U, et al. Photochemical and photoelectrochemical hydrogen generation by splitting seawater. Chem A Eur J, 2018, 24(69): 18455-18462.

[36] Ma TF, Xu WW, Li BR, et al. The critical role of additive sulfate for stable alkaline seawater oxidation on nickel-based electrodes. Angew Chem Int Ed, 2021, 60(42): 22740-22744.

[37] Jadwiszczak M, Jakubow-Piotrowska K, Kedzierzawski P, et al. Highly efficient sunlight-driven seawater splitting in a photoelectrochemical cell with chlorine evolved at nanostructured WO₃ photoanode and hydrogen stored as hydride within metallic cathode. Adv Energy Mater, 2020, 10(3): 1903213.

[38] Wu B, Wang T, Liu B, et al. Stable solar water splitting with wettable organic-layer-protected silicon photocathodes. Nat Commun, 2022, 13(1): 1-10.

[39] Liu B, Feng SJ, Yang LF, et al. Bifacial passivation of n-silicon metal–insulator–semiconductor photoelectrodes for efficient oxygen and hydrogen evolution reactions. Energy Environ Sci, 2020, 13(1): 221-228.

[40] Li ZH, Luo L, Li M, et al. Photoelectrocatalytic C-H halogenation over an oxygen vacancy-rich TiO₂ photoanode. Nat Commun, 2021, 12(1): 6698.

[41] Klingenhof M, Hauke P, Kroschel M, et al. Anion-tuned layered double hydroxide anodes for anion exchange membrane water electrolyzers: from catalyst screening to single-cell performance. ACS Energy Lett, 2022, 7(10): 3415-3422.

[42] Zeradjanin AR, Menzel N, Strasser P, et al. Cover picture: role of water in the chlorine evolution reaction at RuO₂-based electrodes—understanding electrocatalysis as a resonance phenomenon. Chemsuschem, 2012, 5(10): 1849.

[43] Liu B, Wang T, Wang SJ, et al. Back-illuminated photoelectrochemical flow cell for efficient CO₂ reduction. Nat Commun, 2022, 13(1): 7111.

[44] Dong WJ, Xiao YX, Yang KR, et al. Pt nanoclusters on GaN nanowires for solar-assisted seawater hydrogen evolution. Nat Commun, 2023, 14(1): 179.