Three-Dimensional Hexagram Gold Nanoparticles: Synthesis and Growth Mechanism

Abstract

This study explained a procedure to synthesize 3D hexagram gold nanoparticles using a specific morphologically controlled gold precursor reduction. Acetaldehyde acted as the reducing agent along with polyvinyl pyrrolidone as the stabilizing agent with a limited reaction temperature range observed to be near to 25 °C. The resulting special gold nanoparticles were physically characterized and observed to possess an average planar size of 420 nm, an average central thickness of 200 nm, and an average edge thickness of 18 nm. Furthermore, a mechanism model was proposed to describe the oriented growth of gold nanoparticles employing published accounts of the mechanisms involved in the growth of gold hexagonal nanoplates. Moreover, the two major factors that controlled the morphology of synthesized gold nanoparticles were elaborated to provide reference for future fabrication methods of metal nanoparticles in both academia and industry.

Keywords

Gold hexagram nanoparticles / Growth mechanism / Oriented growth / Morphological control

References

[1] Narayanan R, El-Sayed MA. Catalysis with transition metal nanoparticles in colloidal solution: nanoparticle shape dependence and stability. J Phys Chem B, 2005, 109(26): 12663-12676.

[2] Hvolbæk B, Janssens TVW, Clausen BS, et al. Catalytic activity of Au nanoparticles. Nano Today, 2007, 2(4): 14-18.

[3] Chen MS, Goodman DW. Catalytically active gold on ordered titania supports. Chem Soc Rev, 2008, 37(9): 1860-1870.

[4] Zhu WL, Zhang YJ, Zhang HY, et al. Active and selective conversion of CO₂ to CO on ultrathin Au nanowires. J Am Chem Soc, 2014, 136(46): 16132-16135.

[5] Xu ML, Yang XK, Zhang YJ, et al. Enhanced methanol oxidation activity of Au@Pd nanoparticles supported on MWCNTs functionalized by MB under ultraviolet irradiation. Rare Met, 2015, 34(1): 12-16.

[6] Huang YF, Sefah K, Bamrungsap S, et al. Selective photothermal therapy for mixed cancer cells using aptamer-conjugated nanorods. Langmuir, 2008, 24(20): 11860-11865.

[7] Parab HJ, Chen HM, Lai TC, et al. Biosensing, cytotoxicity, and cellular uptake studies of surface-modified gold nanorods. J Phys Chem C, 2009, 113(18): 7574-7578.

[8] Grabinski C, Schaeublin N, Wijaya A, et al. Effect of gold nanorod surface chemistry on cellular response. ACS Nano, 2011, 5(4): 2870-2879.

[9] Wijaya A, Hamad-Schifferli K. Ligand customization and DNA functionalization of gold nanorods via round-trip phase transfer ligand exchange. Langmuir, 2008, 24(18): 9966-9969.

[10] Harry SR, Hicks DJ, Amiri KI, et al. Hairpin DNA coated gold nanoparticles as intracellular mRNA probes for the detection of tyrosinase gene expression in melanoma cells. Chem Commun, 2010, 46(30): 5557-5559.

[11] Gao D, Sheng Z, Han H. An ultrasensitive method for the detection of gene fragment from transgenics using label-free gold nanoparticle probe and dynamic light scattering. Anal Chim Acta, 2011, 696(1–2): 1-5.

[12] Ming T, Zhao L, Xiao M, et al. Resonance-coupling-based plasmonic switches. Small, 2010, 6(22): 2514-2519.

[13] Shao L, Woo KC, Chen H, et al. Angle- and energy-resolved plasmon coupling in gold nanorod dimers. ACS Nano, 2010, 4(6): 3053-3062.

[14] Zijlstra P, Chon JWM, Gu M. Five-dimensional optical recording mediated by surface plasmons in gold nanorods. Nature, 2009, 459(7245): 410-413.

[15] Sau TK, Rogach AL, Jäckel F, et al. Properties and applications of colloidal nonspherical noble metal nanoparticles. Adv Mater, 2010, 22(16): 1805-1825.

[16] Liao HG, Jiang YX, Zhou ZY, et al. Shape-controlled synthesis of gold nanoparticles in deep eutectic solvents for studies of structure-functionality relationships in electrocatalysis. Angewandte Chemie, 2008, 47(47): 9100-9103.

[17] Mahmoud MA, El-Sayed MA. Gold nanoframes: very high surface plasmon fields and excellent near-infrared sensors. J Am Chem Soc, 2010, 132(36): 12704-12710.

[18] Dertli E, Coskun S, Esenturk EN. Gold nanowires with high aspect ratio and morphological purity: synthesis, characterization, and evaluation of parameters. J Mater Res, 2013, 28(2): 250-260.

[19] Loubat A, Lacroix LM, Robert A, et al. Ultrathin gold nanowires: soft-templating versus liquid phase synthesis, a quantitative study. J Phys Chem C, 2015, 119(8): 4422-4430.

[20] Vigderman L, Zubarev ER. Starfruit-shaped gold nanorods and nanowires: synthesis and SERS characterization. Langmuir, 2012, 28(24): 9034-9040.

[21] Chen L, Ji F, Xu Y, et al. High-yield seedless synthesis of triangular gold nanoplates through oxidative etching. Nano Lett, 2014, 14(12): 7201-7206.

[22] Huang Y, Ferhan AR, Gao Y, et al. High-yield synthesis of triangular gold nanoplates with improved shape uniformity, tunable edge length and thickness. Nanoscale, 2014, 6(12): 6496-6500.

[23] Roh J, Back SH, Ahn DJ. Shape-persistent replica synthesis of gold/silver bimetallic nanoplates using tailored silica cages. Small, 2016, 12(10): 1322-1327.

[24] Daeha S, Choong IY, Im SC, et al. Shape adjustment between multiply twinned and single-crystalline polyhedral gold nanocrystals: decahedra, icosahedra, and truncated tetrahedra. J Phys Chem C, 2008, 112(7): 2469-2475.

[25] Li J, Chang M, Peng H, et al. Growth of elongated tetrahexahedral gold nanoparticles with high-index facets and their enhanced electrocatalytic properties. Mater Lett, 2014, 120: 216-218.

[26] Seo D, Park JC, Song H. Polyhedral gold nanocrystals with Oh symmetry: from octahedra to cubes. J Am Chem Soc, 2006, 128(46): 14863-14870.

[27] Zhang J, Liu H, Wang Z, et al. Synthesis of gold regular octahedra with controlled size and plasmon resonance. Appl Phys Lett, 2007, 90(16): 3295-3303.

[28] Liu M, Guyot-Sionnest P. Mechanism of silver(I)-assisted growth of gold nanorods and bipyramids. J Phys Chem B, 2005, 109(47): 22192-22200.

[29] Smith DK, Korgel BA. The importance of the CTAB surfactant on the colloidal seed-mediated synthesis of gold nanorods. Langmuir, 2008, 24(3): 644-649.

[30] Murphy CJ, Sau TK, Gole AM, et al. Anisotropic metal nanoparticles: synthesis, assembly, and optical applications. J Phys Chem B, 2005, 109(29): 13857-13870.

[31] Zhu C, Peng HC, Zeng J, et al. Facile synthesis of gold wavy nanowires and investigation of their growth mechanism. J Am Chem Soc, 2012, 134(50): 20234-20237.

[32] Lofton C, Sigmund W. Mechanisms controlling crystal habits of gold and silver colloids. Adv Func Mater, 2005, 15(7): 1197-1208.