Passivity degradation of nuclear materials in reduced sulfur environments: A review

Abstract

This paper reviews sulfur-induced passivity degradation of nuclear materials with emphasis on steam generator(SG)alloys. The state of arts on this topic concerning thermodynamic calculation and experimental data has been reviewed. Thermodynamic calculation results indicate that the distribution of sulfur species strongly depends on pH and temperature. Experimental data show that solution pH, temperature and solution chemistries can significantly affect the electrochemical behaviors of SG materials and the underlying degradation mechanisms. Some issues when conducting corrosion tests at high temperature should be paid attention to, such as the dissolution of the autoclave, which may affect the facticity of the experimental results.

Keywords

nuclear materials / steam generator / sulfur / passivity degradation / mechanism / high temperature

References

[1] Nuclear Power in China[EB/OL]. http://www.worldnuclear.org/info/Country-Profiles/Countries-A-F/China—Nuclear-Power/. 2016-04.

[2] Pressurized Water Reactors[EB/OL]. http://www.nrc.gov/reactors/pwrs.html. 2015-01-15.

[3] Xia D H, Luo J L, Gao Z M, et al. Monitoring the diffusion layer during passive film breakdown on Alloy 800 with digital holography [J]. Acta Metallurgica Sinica(English Letters), 2015, 28(9): 1170-1174.

[4] Pandey M D, Datla S, Tapping R L, et al. The estimation of lifetime distribution of Alloy 800 steam generator tubing [J]. Nuclear Engineering and Design, 2009, 239(10): 1862-1869.

[5] Zhu R K, Luo J L. Investigation of stress-enhanced surface reactivity on Alloy 800 using scanning electrochemical microscopy [J]. Electrochemistry Communications, 2010, 12(12): 1752-1755.

[6] Xia D H, Song S Z, Zhu R K, et al. A mechanistic study on thiosulfate-enhanced passivity degradation of Alloy 800 in chloride solutions [J]. Electrochimica Acta, 2013, 111(6): 510-525.

[7] Xia D H, Zhu R K, Behnamian Y, et al. pH effect on sulfurinduced passivity degradation of Alloy 800 in simulated crevice chemistries [J]. Journal of the Electrochemical Society, 2014, 161(4): C201-C214.

[8] Liu X H, Wu X Q, Han E H. Electrochemical and surface analytical investigation of the effects of Zn concentrations on characteristics of oxide films on 304 stainless steel in borated and lithiated high temperature water [J]. Electrochimica Acta, 2013, 108: 554-565.

[9] Xia D H, Sun Y F, Fan H Q. Characterization of passive film formed on 304 SS in simulated alkaline water chemistries containing sulfur at 300 °C [J]. Transactions of Tianjin University, 2015, 21(6): 554-561.

[10] Lu B T, Tian L P, Zhu R K, et al. Effects of dissolved Ca²⁺ and Mg²⁺on passivity of UNS N08800 alloy in simulated crevice chemistries with and without Pb contamination at 300°C [J]. Corrosion Science, 2015, 100: 1-11.

[11] Xia D H, Sun Y F, Shen C, et al. A mechanistic study on sulfur-induced passivity degradation on Alloy 800 in simulated alkaline crevice chemistries at temperatures ranging from 21°C to 300°C [J]. Corrosion Science, 2015, 100: 504-516.

[12] Luo B, Xia D H. Characterization of pH effect on corrosion resistance of nuclear steam generator tubing alloy by in-situ scanning electrochemical microscopy [J]. Acta Physico-Chimica Sinica, 2014, 30(1): 59-66.

[13] Xia D H, Yang L X. A mechanistic study on semiconductivity conversion of passive films under varying sulfate to chloride concentration ratios [J]. Acta Physico-Chimica Sinica, 2014, 30(8): 1465-1473.

[14] Huang M. Test Plan for ACR-1000 Crevice Chemistry Experiments[R], 2008.

[15] Staehle R W, Gorman J A. Quantitative assessment of submodes of stress corrosion cracking on the secondary side of steam generator tubing in pressurized water reactors: Part 3 [J]. Corrosion, 2004, 60(2): 115-180.

[16] Choudhary L, Macdonald D D, Alfantazi A. Role of thiosulfate in the corrosion of steels: A review [J]. Corrosion, 2015, 71(9): 1147-1168.

[17] Bailar J C, Emeleus H J, Nyholm R, et al. Comprehensive Inorganic Chemistry, 1973, Oxford: Pergamon Press.

[18] Xia D H, Luo J L. Corrosion behavior of Alloy 690 in simulated alkaline water chemistries containing sulfur at 300°C [J]. Acta Physico-Chimica Sinica, 2015, 31(3): 467-475.

[19] Xia D H, Luo J L. Passivity degradation of Alloy 800 in simulated crevice chemistries [J]. Transactions of Tianjin University, 2015, 21(3): 234-243.

[20] Marcus P, Protopopoff E. Potential-pH diagrams for sulfur and oxygen adsorbed on chromium in water [J]. Journal of the Electrochemical Society, 1997, 144(5): 1586-1590.

[21] Marcus P, Protopopoff E. Potential-pH diagrams for adsorbed species: Application to sulfur adsorbed on iron in water at 25°C and 300°C [J]. Journal of the Electrochemical Society, 1990, 137(9): 2709-2712.

[22] Marcus P, Protopopoff E. Potential pH diagrams for sulfur and oxygen adsorbed on nickel in water at 25°C and 300°C [J]. Journal of the Electrochemical Society, 1993, 140(6): 1571-1575.

[23] Marcus P, Protopopoff E. Thermodynamics of thiosulfate reduction on surfaces of iron, nickel and chromium in water at 25°C and 300°C [J]. Corrosion Science, 1997, 39(9): 1741-1752.

[24] Marcus P. Corrosion Mechanisms in Theory and Practice, 2011, 3

[25] Belo M D, Hakiki N E, Ferreira M G S. Semiconducting properties of passive films formed on nickel-base alloys type Alloy 600: Influence of the alloying elements [J]. Electrochimica Acta, 1999, 44(14): 2473-2481.

[26] Weingartner H, Franck E U. Supercritical water as a solvent [J]. Angewandte Chemie-International Edition, 2005, 44(18): 2672-2692.

[27] Xia D H, Zhu R K, Behnamian Y, et al. Understanding the interaction of thiosulfate with Alloy 800 in aqueous chloride solutions using SECM [J]. Journal of Electroanalytical Chemistry, 2015, 744: 77-84.

[28] Fu C W, Wang J H, Gao Z M, et al. Corrosion process detection of tinplate in deaerated functional beverage by EIS[J]. Transactions of Tianjin University, 2013, 19(4): 235-240.

[29] Xia D H, Song S Z, Wang J H, et al. Fast evaluation of degradation degree of organic coatings by analyzing electrochemical impedance spectroscopy data [J]. Transactions of Tianjin University, 2012, 18(1): 15-20.

[30] Xia D H, Song S Z, Behnamian Y. Detection of corrosion degradation using electrochemical noise(EN): Review of signal processing methods for identifying corrosion forms [J]. Corrosion Engineering, Science and Technology, 2015.

[31] Xia D H, Behnamian Y. Electrochemical noise: A review of experimental setup, instrumentation and DC removal [J]. Russian Journal of Electrochemistry, 2015, 51(7): 593-601.

[32] Li J, Kong W, Zheng H, et al. Portable 4-channel electrochemical noise test system [J]. Transactions of Tianjin University, 2014, 20(2): 144-150.

[33] Shi J B, Xia D H, Wang J H, et al. Degradation process of coated tinplate by phase space reconstruction theory [J]. Transactions of Tianjin University, 2013, 19(2): 92-97.

[34] Xia D H, Wang H H, Wang K, et al. A novel electrochemical noise sensor applied to detect food safety [J].. Russian Journal of Electrochemistry, 2014, 50(6): 599-602.

[35] Macdonald D D, Sharifi-Asl S. Volt equivalent diagrams as a means of displaying the electrochemical thermodynamics of the sulfur-water system [J]. Corrosion Science, 2014, 81: 102-109.

[36] Xia D H, Fan H Q, Yang L X, et al. Semiconductivity conversion of passive films on Alloy 800 in chloride solutions containing various concentrations of thiosulfate [J]. Journal of the Electrochemical Society, 2015, 162(9): C482-C486.

[37] Thomas A E. Investigation of thiosulfate adsorption on 316 stainless steel in neutral solutions by radioactive labeling, electrochemistry, and auger electron spectroscopy [J]. Journal of the Electrochemical Society, 1995, 142(2): 476-484.

[38] Xia D H, Behnamian Y, Feng H N, et al. Semiconductivity conversion of Alloy 800 in sulphate, thiosulphate, and chloride solutions [J]. Corrosion Science, 2014, 87: 265-277.

[39] Xia D H, Behnamian Y, Yang L, et al. Semiconductivity of steam generator tubing alloys in simulated crevice chemistries containing lead and sulphur [J]. Corrosion Engineering, Science and Technology, 2016, 51(1): 37-50.

[40] Xia D H, Behnamian Y, Chen X Y, et al. A mechanistic study of sulfur-induced passivity degradation of Alloy 800 in a simulated alkaline crevice environment at 300°C [J]. Journal of Solid State Electrochemistry, 2015, 19(12): 3567-3578.

[41] Rahman M M, Czaun M, Takafuji M, et al. Synthesis, selfassembling properties, and atom transfer radical polymerization of an alkylated L-phenylalanine-derived monomeric organogel from silica: A new approach to prepare packing materials for high-performance liquid chromatography[J]. Chemistry-A European Journal, 2008, 14(4): 1312-1321.

[42] McCafferty E. A surface charge model of corrosion pit initiation and of protection by surface alloying [J]. Journal of the Electrochemical Society, 1999, 146(8): 2863-2869.

[43] Ha H Y, Kwon H S. Effects of pH levels on the surface charge and pitting corrosion resistance of Fe [J]. Journal of the Electrochemical Society, 2012, 159(9): C416-C421.

[44] Baes Charles F, Mesmer Robert E. The Hydrolysis of Cations, 1976, USA: Wiley.

[45] Tsai W T, Wu T F. Pitting corrosion of Alloy 690 in thiosulfate-containing chloride solutions [J]. Journal of Nuclear Materials, 2000, 277(2/3): 169-174.

[46] Newman R C, Isaacs H S, Alman B. Effects of sulfur compounds on the pitting behavior of type 304 stainless steel in near-neutral chloride solutions [J]. Corrosion, 1982, 38(5): 261-265.

[47] Roberge R. Effect of the nickel content in the pitting of stainless-steels in low chloride and thiosulfate solutions [J]. Corrosion, 1988, 44(5): 274-280.

[48] Faichuk M G, Ramamurthy S, Lau W M. Electrochemical behaviour of Alloy 600 tubing in thiosulphate solution [J]. Corrosion Science, 2011, 53(4): 1383-1393.

[49] Zhang W, Carcea A G, Newman R C. Pitting of steamgenerator tubing alloys in solutions containing thiosulfate and sulfate or chloride [J]. Faraday Discussions, 2015, 180: 233-249.

[50] Frankel G, Thornton G, Street S, et al. Localised corrosion: General discussion [J]. Faraday Discussions, 2015, 180: 381-414.

[51] Kuang W, Wu X, Han E H, et al. Effect of nickel ion from autoclave material on oxidation behaviour of 304 stainless steel in oxygenated high temperature water [J]. Corrosion Science, 2011, 53(3): 1107-1114.

[52] Kirillov P L. Supercritical water cooled reactors [J]. Thermal Engineering, 2008, 55(5): 361-364.

[53] Brunner G. Near critical and supercritical water. Part I. Hydrolytic and hydrothermal processes [J]. The Journal of Supercritical Fluids, 2009, 47(3): 373-381.

[54] Kritzer P. Corrosion in high-temperature and supercritical water and aqueous solutions: A review [J]. Journal of Supercritical Fluids, 2004, 29(1/2): 1-29.