Control of pinhole defects formation in semi-flexible coaxial cable by vertical tin-plating process

Abstract

Holistic tin-plating on the outer conductor is one of the key processes in the manufacture of semi-flexible coaxial cable, which is widely applied to the third generation (3G) mobile communication system. However, in the traditional horizontal tin-plating process, disadvantages such as the pinhole defects and low productivity effect cannot be avoided. In this paper, a vertical tin-plating process was proposed to reduce the pinhole defects and improve the tin-coating quality. Compared with the traditional horizontal tin-plating process, the immersion length was reduced from 300–400 mm to 10–100 mm and the tin-plating time was reduced from 7 s to 3 s in the proposed method. The experimental results indicate that immersion length and time are key parameters for the tin-plating quality. With this new tin-plating process, the experimental results show that the pinhole defects can be eliminated effectively by controlling the immersion depth below 100 mm and tin-plating time at 3 s. The thickness of tin-coating increased from not more than 5 μm to 12.3 μm with the proposed vertical tin-plating process. Meanwhile, the thickness of the intermetallic compounds (IMCs) layer between the tin-coating and copper wires was reduced from 3.26 μm to 0.62 μm if the immersion time decreased from 30 s to 1 s. Besides, a self-developed flux, which possesses a boiling point or decomposed temperature of active components over 300 °C, exhibits a better efficiency in reducing the pinhole formation.

Keywords

3G communication network / semi-flexible coaxial cable / vertical tin-plating / pinhole defect

References

[1] Fan Qiang. Process of overall tin-plating on semi-flexible coaxial cable[J]. Optical Fiber and Electric Cable and Their Applications, 2010(2): 5–28 (in Chinese).

[2] Zhong Xiuqing. A new coaxial cable-The SFX type semiflexible coaxial cable with tin dipped braid[J]. Optical Fiber and Electric Cable and Their Applications, 1999(4):6 (in Chinese).

[3] Cheng Fangjie. Vertical Tin-Plating Device for Forming Tin-plated Shielding Layer on Semi-flexible Coaxial Cable: China, CN101603166A[P]. 2009-12-16(in Chinese).

[4] Park M. S., Arróyave R. Computational investigation of intermetallic compounds (Cu6Sn5 and Cu3Sn) growth during solid-state aging process[J]. Computational Materials Science, 2011, 50(5): 1692-1700.

[5] Yang M., Li M., Wang L., et al. Growth behavior of Cu₆Sn₅ grains formed at an Sn_3.5Ag/Cu interface[J]. Materials Letters, 2011, 65(10): 1506-1509

[6] Zhao N., Ma H. T., Wang L. Microstructure, mechanical property and interfacial reaction of Sn-Cu based multicomponent lead-free solders[J]. Rare Metal Materials and Engineering, 2009, 38(S1): 107-111.

[7] Chan Y. C., So A. C. K., Lai J. K. L. Growth kinetic studies of Cu-Sn intermetallic compound and its effect on shear strength of LCCC SMT solder joints[J]. Materials Science and Engineering: B, 1998, 55(1/2): 5-13.

[8] Yu D. Q., Wu C. M. L., Law C. M. T., et al. Intermetallic compounds growth between Sn-3.5Ag lead-free solder and Cu substrate by dipping method[J]. Journal of Alloys and Compounds, 2005, 392(1/2): 192-199.

[9] Yoon J. W., Lee Y. H., Kim D. G., et al. Intermetallic compound layer growth at the interface between Sn-Cu-Ni solder and Cu substrate[J]. Journal of Alloys and Compounds, 2004, 381(1/2): 151-157.

[10] Shin C. K., Baik Y. J., Huh J. Y. Effects of microstructural evolution and intermetallic layer growth on shear strength of ball-grid-array Sn-Cu solder joints[J]. Journal of Electronic Materials, 2001, 30(10): 1323-1331.

[11] Harcuba P., Janeček M. Microstructure changes and physical properties of the intermetallic compounds formed at the interface between Sn-Cu solders and a Cu substrate due to a minor addition of Ni[J]. Journal of Electronic Materials, 2010, 39(12): 2553-2557.

[12] Park M. S., Arroyave R. Formation and growth of intermetallic compound Cu6Sn5 at early stages in lead-free soldering[J]. Journal of Electronic Materials, 2010, 39(12): 2574-2582.

[13] Yoon J. W., Jung S. B. Interfacial reactions between Sn-0.4Cu solder and Cu substrate with or without ENIG plating layer during reflow reaction[J]. Journal of Alloys and Compounds, 2005, 396(1/2): 122-127.

[14] Li G. Y., Chen B. L. Formation and growth kinetics of interfacial intermetallics in Pb-free solder joint[J]. IEEE Transactions on Components and Packaging Technologies, 2003, 26(3): 651-658.

[15] Jiang L., Chawla N. Mechanical properties of Cu6Sn5 intermetallic by micropillar compression testing[J]. Scripta Materialia, 2010, 63(5): 480-483.