Influence of calcination temperature on TiO₂ nanotubes’ catalysis for TiO₂/UV/O₃ in landfill leachate solution

Abstract

The influence of calcination temperature on TiO₂ nanotubes’ catalysis for TiO₂/UV/O₃ was investigated. TiO₂ nanotubes (TNTs) were prepared via the sol-gel method and calcined at 300–700 °C, which were labeled as TNTs-300, TNTs-400, TNTs-500, TNTs-600 and TNTs-700, respectively. TNTs were characterized by transmission electron microscopy(TEM) and X-ray diffraction (XRD). It is found that TNTs calcined at 400 °C showed the best thermal stability. When the calcination temperature increased from 400 °C to 700 °C, the special structure of tubes was destroyed and gradually converted into nanorods and/or particles. The transformation from anatase to rutile occurred at 600 °C, and the rutile phase was enhanced when the calcination temperature was increased to over 600 °C. The calcination temperature’s influence on TNTs’ adsorption activity for chemical oxygen demand (COD) and catalytic activity for TiO₂/UV/O₃ was investigated in landfill leachate solution. In landfill leachate solution, the adsorption activity of COD decreased in the reduced order of TNTs-300, TNTs-400, TNTs-500, TNTs-600 and TNTs-700. In photocatalytic ozonation, TNTs-400 showed the best catalytic activity while TNTs-700 exhibited the worst. In other three processes, the COD removal of TNTs-300/UV/O₃ was higher than those of TNTs-500/UV/O₃ and TNTs-600/UV/O₃ in the first 20 min, and then became close to those of the latter two in the following 40 min. Compared with TNTs-300 and TNTs- 400, TNTs-600 had the best anti-fouling activity, while TNTs-500 and TNTs-700 had lower anti-fouling activity than the former three. In photocatalytic ozonation, the calcination temperature of 400 °C was appropriate when TNTs were obtained at the synthesis temperature of 105 °C.

Keywords

TiO₂ nanotubes / calcination temperature / photocatalytic ozonation / landfill leachate

References

[1] Černigoj U., Štangar U. L., Trebše P. Degradation of neonicotinoid insecticides by different advanced oxidation process and studying the effect of ozone on TiO₂ photocatalysis[J]. Appl Catal B: Environ, 2007, 75(3/4): 229-238.

[2] Agustina T. E., Ang H. M., Vareek V. K. A review of synergistic effect of photocatalysis and ozonation on wastewater treatment[J]. J Photochem Photobiol C: Photochem Rev, 2005, 6(4): 264-273.

[3] Giri R. R., Ozaki H., Ishida T., et al. Synergy of ozonation and photocatalysis to mineralize low concentration 2,4-dichlorophenoxyacetic acid in aqueous solution[J]. Chemosphere, 2007, 66(9): 1610-1617.

[4] Müller T. S., Sun Z., Gireesh Kumar M. P., et al. The combination of photocatalysis and ozonolysis as a new approach for cleaning 2, 4-dichlorophenoxyacetic acid polluted water[J]. Chemosphere, 1998, 36(9): 2043-2055.

[5] Hernández-Alonso M. D., Coronado J. M., Javier Maira A., et al. Ozone enhanced activity of aqueous titanium dioxide suspensions for photocatalytic oxidation of free cyanide ions[J]. Appl Catal B: Environ, 2002, 39(3): 257-267.

[6] Kopf P., Gilbert E., Eberle S. H. TiO₂ photocatalytic oxidation of monochloroacetic acid and pyridine: Influence of ozone[J]. J Photochem Photobiol A: Chem, 2000, 136(3): 163-168.

[7] Addamo M., Augugliaro V., García-López E., et al. Oxidation of oxalate ion in aqueous suspensions of TiO₂ by photocatalysis and ozonation[J]. Catal Today, 2005, 107–108 612-618.

[8] Wang S., Shiraishi F., Nakano K. A synergistic effect of photocatalysis and ozonation on decomposition of formic acid in an aqueous solution[J]. Chem Eng J, 2002, 87(2): 261-271.

[9] Sánchez L., Peral J., Domènech X. Aniline degradation by combined photocatalysis and ozonation[J]. Appl Catal B: Environ, 1998, 19(1): 59-65.

[10] Beltran F. J., Rivas F. J., Gimeno O. Comparison between photocatalytic ozonation and other oxidation processes for the removal of phenols from water[J]. J Chem Technol Biotechnol, 2005, 80 973-984.

[11] Farré M. J., Franch M. I., Malato S., et al. Degradation of some biorecalcitrant pesticides by homogeneous and heterogeneous photocatalytic ozonation[J]. Chemosphere, 2005, 58(8): 1127-1133.

[12] Li L., Zhu W., Chen L., et al. Photocatalytic oxidation and ozonation of catechol over carbon-black-modified nano-TiO₂ thin films supported on Al sheet[J]. Water Research, 2003, 37(15): 3646-3651.

[13] Pan L., Ji M., Wang M., et al. Preparation of titanium dioxide nanotube and its catalytic activity for ozonation[J]. J Chem Industry Eng, 2007, 58(11): 2787-2792.

[14] Ou H. H., Lo S. L. Review of titania nanotubes synthesized via the hydrothermal treatment: Fabrication, modification, and application[J]. Sep Purif Technol, 2007, 58(1): 179-191.

[15] State Environmental Protection Administration. Standard Methods for Water and Wastewater Monitoring and Analysis[M]. 2002 4th Ed. Beijing: Chinese Environmental Science Press.

[16] Qamar M., Yoon C. R., Oh H. J., et al. Preparation and photocatalytic activity of nanotubes obtained from titanium dioxide[J]. Catal Today, 2008, 131(1–4): 3-14.

[17] Tanaka K., Abe K., Hisanaga T. Photocatalytic water treatment on immobilized TiO₂ combined with ozonation[J]. J Photochem Photobiol A: Chem, 1996, 101(1): 85-87.

[18] Moraes S. G., Freire R. S., Durán N. Degradation and toxicity reduction of textile effluent by combined photocatalytic and ozonation processes[J]. Chemosphere, 2000, 40(4): 369-373.

[19] Vinu R., Madras G. Kinetics of simultaneous photocatalytic degradation of phenolic compounds and reduction of metal ions with nano-TiO₂[J]. Environ Sci Technol, 2008, 42 913-919.

[20] Nian J. N., Teng H. Hydrothermal synthesis of single-crystalline anatase TiO₂ nanorods with nanotubes as the precursor[J]. J Phys Chem B, 2006, 110 4193-4198.

[21] Tsai C. C., Teng H. Regulation of the physical characteristics of titania nanotube aggregates synthesized from hydrothermal treatment[J]. Chem Mater, 2004, 22 4352-4358.

[22] Yang Y. X., Ma J., Qin Q. D., et al. Degradation of nitrobenzene by nano-TiO₂ catalyzed ozonation[J]. Catal A: Chem, 2007, 267(1/2): 41-48.

[23] Lee C. K., Lin K. S., Wu C. F., et al. Effects of synthesis temperature on the microstructures and basic dyes adsorption of titanate nanotubes[J]. J Hazard Mater, 2008, 150(3): 494-503.

[24] Lindner M., Theurich J., Bahnemann D. W. Photocatalytic degradation of organic compounds: Accelerating the process efficiency[J]. Water Sci Technol, 1997, 35(4): 79-86.

[25] Blount M. C., Kim D. H., Falconer J. L. Transparent thinfilm TiO₂ photocatalysts with high activity[J]. Environ Sci Technol, 2001, 35 2988-2994.

[26] Hamill N. A., Hardacre C., Barth J. A. C., et al. Gas-phase photocatalytic oxidation of dichlorobutenes[J]. Environ Sci Technol, 2001, 35 2823-2827.

[27] Alberici R. M., Canela M. C., Eberlin M. N., et al. Catalyst deactivation in the gas phase destruction of nitrogen-containing organic compounds using TiO₂/UV-VIS[J]. Appl Catal B, 2001, 30(3/4): 389-397.

[28] Sawunyama P., Fujishima A., Hashimoto K. Photocatalysis on TiO₂ surfaces investigated by atomic force microscopy: Photodegradation of partial and full monolayers of stearic acid on TiO2[J]. Langmuir, 1999, 15 355l-3556.