Dealumination and desilication for Al-rich HZSM-5 zeolite via steam-alkaline treatment and its application in methanol aromatization

Abstract

The hierarchical HZSM-5 was prepared via dealumination and desilication of commercial Al-rich HZSM-5, and characterized by X-ray diffraction, ²⁷Al magic-angle spinning nuclear magnetic resonance, inductively coupled plasma mass spectrometry, scanning electron microscope, transmission electron microscope, N₂ adsorption-desorption, NH₃ temperature-programmed desorption, performed thermogravimetric and Raman spectrum. The results showed that partial framework of HZSM-5 was removed after steam treatment at 0.15 MPa, 500°C for 3 h. HZSM-5 with high specific surface area and much mesoporosity was obtained by the subsequent alkaline treatment. The regulation of acid quantity was achieved by altering the concentration of alkaline. Dealumination and desilication of Al-rich HZSM-5 zeolites became more effective using a combination of steam and alkaline treatments than using alkaline treatment alone. Methanol aromatization reaction was employed to evaluate the catalytic performance of treated HZSM-5 at 0.15 MPa, 450°C and MHSV of 1.5 h⁻¹. The results indicated that after steam treatment, HZSM-5 further treated with 0.2 mol/L NaOH exhibits the best catalytic performance: the selectivity of aromatics reached 42.1% and the lifetime of catalyst attained 212 h, which are much better than untreated HZSM-5.

Key words： steam treatment; alkaline treatment; hierarchical ZSM-5; methanol aromatization

Acknowledgements

The funding from the National Natural Science Foundation of China (Grant No. 21776076) and Technology admin. of Department of PetroChina Company Limited are gratefully acknowledged.

References

1 Wen Z, Xia T, Liu M, Cao Q, Xu Y, Zhu K, Zhu X. Alkaline modification of ZSM-5 catalysts for methanol aromatization: The effect of the alkaline concentration. Frontiers of Chemical Science and Engineering, 2015, 9(4): 450–460, 460

2 Wang F, Xiao W, Gao L, Xiao G. The growth mode of ZnO on HZSM-5 substrates by atomic layer deposition and its catalytic property in the synthesis of aromatics from methanol. Catalysis Science & Technology, 2016, 6(9): 3074–3086

3 Shen X, Kang J, Niu W, Wang M, Zhang Q, Wang Y. Impact of hierarchical pore structure on the catalytic performances of MFI zeolites modified by ZnO for the conversion of methanol to aromatics. Catalysis Science & Technology, 2017, 7(16): 3598–3612

4 Xing L, Wei Z, Wen Z, Zhu X. Catalytic study for methanol aromatization over hierarchical ZSM-5 zeolite synthesized by kaolin. Petroleum Science and Technology, 2017, 9(24): 1–6

5 Yang F, Zhong J, Liu X, Zhu X. A novel catalytic alkylation process of syngas with benzene over the cerium modified platinum supported on HZSM-5 zeolite. Applied Energy, 2018, 226: 22–30

6 Wang N, Qian W, Shen K, Su C, Wei F. Bayberry-like ZnO/MFI zeolite as high performance methanol-to-aromatics catalyst. Chemical Communications, 2015, 52(10): 2011–2014

7 Xu C, Jiang B, Liao Z, Wang J, Huang Z, Yang Y. Effect of metal on the methanol to aromatics conversion over modified ZSM-5 in the presence of carbon dioxide. RSC Advances, 2017, 7(18): 10729–10736

8 Ilias S, Bhan A. Mechanism of the catalytic conversion of methanol to hydrocarbons. ACS Catalysis, 2013, 44(3): 18–31

9 Hickman D A, Schmidt L D. Syngas formation by direct catalytic oxidation of methane. Science, 1993, 259(5093): 343–346

10 Asadullah M, Ito S, Kunimori K, Yamada M, Tomishige K. Biomass gasification to hydrogen and syngas at low temperature: Novel catalytic system using fluidized-bed reactor. Journal of Catalysis, 2002, 208(2): 255–259

11 Castellanos-Beltran I J, Assima G P, Lavoie J M. Effect of temperature in the conversion of methanol to olefins (MTO) sing an extruded SAPO-34 catalyst. Frontiers of Chemical Science and Engineering, 2018, 12(2): 1–13

12 Martinez-Espin J S, Mortén M, Janssens T V W, Svelle S, Beato P, Olsbye U. New insights into catalyst deactivation and product distribution of zeolites in the methanol-to-hydrocarbons (MTH) reaction with methanol and dimethyl ether feeds. Catalysis Science & Technology, 2017, 7(13): 2700–2716

13 Song B, Li Y, Cao G, Sun Z, Han X. The effect of doping and steam treatment on the catalytic activities of nano-scale H-ZSM-5 in the methanol to gasoline reaction. Frontiers of Chemical Science and Engineering, 2017, 11(4): 1–11

14 Wei Z, Zhu K, Xing L, Yang F, Li Y, Xu Y, Zhu X. Steam-assisted transformation of natural kaolin to hierarchical ZSM-11 using tetrabutylphosphonium hydroxide as structure-directing agent: Synthesis, structural characterization and catalytic performance in the methanol-to-aromatics reaction. RSC Advances, 2017, 7(39): 24015–24021

15 Mikkelsen Ø, Kolboe S. The conversion of methanol to hydrocarbons over zeolite H-β. Microporous and Mesoporous Materials, 1999, 29(1-2): 173–184

16 Ravishankar R, Bhattacharya D, Jacob N E, Sivasanker S. Characterization and catalytic properties of zeolite MCM-22. Microporous Materials, 1995, 4(1): 83–93

17 Kokotailo G T, Lawton S L, Olson D H, Meier W M. Structure of synthetic zeolite ZSM-5. Nature, 1978, 272(5652): 437–438

18 Gao Y, Zheng B, Wu G, Ma F, Liu C. Effect of the Si/Al ratio on the performance of hierarchical ZSM-5 zeolites for methanol aromatization. RSC Advances, 2016, 6(87): 83581–83588

19 Zhang G, Zhang X, Bai T, Chen T, Fan W. Coking kinetics and influence of reaction-regeneration on acidity, activity and deactivation of Zn/HZSM-5 catalyst during methanol aromatization. Journal of Energy Chemistry, 2015, 24(1): 108–118

20 Kim J, Choi M, Ryoo R. Effect of mesoporosity against the deactivation of MFI zeolite catalyst during the methanol-to-hydrocarbon conversion process. Journal of Catalysis, 2010, 269(1): 219–228

21 Iwakai K, Tago T, Konno H, Nakasaka Y, Masuda T. Preparation of nano-crystalline MFI zeolite via hydrothermal synthesis in water/surfactant/organic solvent using fumed silica as the Si source. Microporous and Mesoporous Materials, 2011, 141(1-3): 167–174

22 Shen K, Wang N, Qian W, Cui Y, Wei F. Atmospheric pressure synthesis of nanosized ZSM-5 with enhanced catalytic performance for methanol to aromatics reaction. Catalysis Science & Technology, 2014, 4(11): 3840–3844

23 Liu Z, Wu D, Ren S, Chen X, Qiu M, Wu X, Yang C, Zeng G, Sun Y. Solvent-free synthesis of c-axis oriented ZSM-5 crystals with enhanced methanol to gasoline catalytic activity. ChemCatChem, 2016, 8(21): 3317–3322

24 Verboekend D, Pérez-Ramírez J. Design of hierarchical zeolite catalysts by desilication. Catalysis Science & Technology, 2011, 1(6): 879–890

25 Chal R, Gerardin C, Bulut M, Donk S. Cheminform abstract: Overview and industrial assessment of synthesis strategies towards zeolites with mesopores. ChemCatChem, 2011, 3(1): 67–81

26 Schwieger W, Machoke A G, Weissenberger T, Inayat A, Selvam T, Klumpp M, Inayat A. Hierarchy concepts: Classification and preparation strategies for zeolite containing materials with hierarchical porosity. ChemInform, 2016, 45(12): 3353–3376

27 Sun M, Chen C, Chen L, Su B. Hierarchically porous materials: Synthesis strategies and emerging applications. Frontiers of Chemical Science and Engineering, 2016, 10(3): 301–347

28 Mei C, Wen P, Liu Z, Liu H, Wang Y, Yang W, Xie Z, Hua W, Gao Z. Selective production of propylene from methanol: Mesoporosity development in high silica HZSM-5. Journal of Catalysis, 2008, 258(1): 243–249

29 Dyballa M, Obenaus U, Rosenberger M, Fischer A, Jakob H, Klemm E, Hunger M. Post-synthetic improvement of H-ZSM-22 zeolites for the methanol-to-olefin conversion. Microporous and Mesoporous Materials, 2016, 233: 26–30

30 Schmidt F, Lohe M R, Büchner B, Giordanino F, Bonino F, Kaskel S. Improved catalytic performance of hierarchical ZSM-5 synthesized by desilication with surfactants. Microporous and Mesoporous Materials, 2013, 165: 148–157

31 Tempelman C H L, Rodrigues V O, Eck E R H, Magusin P C M M, Hensen E J M. Desilication and silylation of Mo/HZSM-5 for methane dehydroaromatization. Microporous and Mesoporous Materials, 2015, 203: 259–273

32 Ong L H, Dömök M, Olindo R, Veen A C, Lercher J A. Dealumination of HZSM-5 via steam-treatment. Microporous and Mesoporous Materials, 2012, 164: 9–20

33 Zhao L, Shen B, Gao J, Xu C. Investigation on the mechanism of diffusion in mesopore structured ZSM-5 and improved heavy oil conversion. Journal of Catalysis, 2008, 258(1): 228–234

34 Gopalakrishnan S, Zampieri A, Schwieger W. Mesoporous ZSM-5 zeolites via alkali treatment for the direct hydroxylation of benzene to phenol with N₂O. Journal of Catalysis, 2008, 260(1): 193–197

35 Xing J, Song L, Zhang C, Zhou M, Yue L, Li X. Effect of acidity and porosity of alkali-treated ZSM-5 zeolite on eugenol hydrodeoxygenation. Catalysis Today, 2015, 258(1): 90–95

36 Qi R, Fu T, Wan W, Li Z. Pore fabrication of nano-ZSM-5 zeolite by internal desilication and its influence on the methanol to hydrocarbon reaction. Fuel Processing Technology, 2016, 155: 191–199

37 Svelle S, Sommer L, Barbera K, Vennestrøm P N R, Olsbye U, Lillerud K P, Bordiga S, Pan Y, Beato P. How defects and crystal morphology control the effects of desilication. Catalysis Today, 2011, 168(1): 38–47

38 Groen J C, Zhu W, Brouwer S, Huynink S J, Kapteijn F K, Moulijn J A, Pérez-Ramírez J. Direct demonstration of enhanced diffusion in mesoporous ZSM-5 zeolite obtained via controlled desilication. Journal of the American Chemical Society, 2007, 129(2): 355–360

39 Groen J C, Peffer L A A, Moulijn J A, Pérez-Ramírez J. Mechanism of hierarchical porosity development in MFI zeolites bydesilication: the role of aluminium as a pore-directing agent. Chemistry (Weinheim an der Bergstrasse, Germany), 2010, 11(17): 4983–4994

40 Groen J C, Jansen C J, Moulijn J A, Pérez-Ramírez J. Optimal aluminum-assisted mesoporosity development in MFI zeolites by desilication. Journal of Physical Chemistry B, 2004, 35(45): 13062–13065

41 Groen J C, Moulijn J A, Pérez-Ramírez J. Desilication: On the controlled generation of mesoporosity in MFI zeolites. Journal of Materials Chemistry, 2006, 16(22): 2121–2131

42 Yang S, Yu C, Yu L, Miao S, Zou M, Jin C, Zhang D, Xu L, Huang S. Bridging dealumination and desilication for the synthesis of hierarchical MFI zeolites. Angewandte Chemie, 2017, 129(41): 12553–12556

43 Parker W O, Jr Angelis A, Flego C, Millini R, Perego C, Zanardi S. Unexpected destructive dealumination of zeolite beta by silylation. Journal of Physical Chemistry C, 2010, 114(18): 8459–8468

44 Wagner G W, Fry R A. Observation of distinct surface Al^IV sites and phosphonate binding modes in g-alumina and concrete by high-field ²⁷Al and ³¹P MAS NMR. Journal of Physical Chemistry C, 2009, 113(30): 13352–13357

45 Wei Z, Chen L, Cao Q, Wen Z, Zhou Z, Xu Y, Zhu X. Steamed Zn/ZSM-5 catalysts for improved methanol aromatization with high stability. Fuel Processing Technology, 2017, 162: 66–77

46 Verboekend D, Mitchell S, Milina M, Groen J C, Pérez-Ramírez J. Full compositional flexibility in the preparation of mesoporous MFI zeolites by desilication. Journal of Physical Chemistry C, 2011, 115(29): 14193–14203

47 Li Y, Wen Z, Wei Z, Yang F, Zhu X. Study on catalytic alkylation of benzene with methanol over ZSM-22 and ZSM-35. China Petroleum Processing and Petrochemical Technology, 2017, 19(4): 38–46 (in Chinese)

48 Zhu H, Liu Z, Kong D, Wang Y, Xie Z. Synthesis and catalytic performances of mesoporous zeolites templated by polyvinyl butyral gel as the mesopore directing agent. Journal of Physical Chemistry C, 2008, 112(44): 17257–17264

49 Castaño P, Elordi G, Olazar M, Aguayoa T A, Pawelec B, Bilbao J. Insights into the coke deposited on HZSM-5, Hb and HY zeolites during the cracking of polyethylene. Applied Catalysis B: Environmental, 2011, 104(1): 91–100

50 Rojo-Gama D, Signorile M, Bonino F, Bordiga S, Olsbye U, Lillerud K P, Beato P, Svelle S. Structure-deactivation relationships in zeolites during the methanol-to-hydrocarbons reaction: Cmplementary assessments of the coke content. Journal of Catalysis, 2017, 351: 33–48

51 Vogelaar B M, Langeveld A D, Eijsbouts S, Moulijn J A. Analysis of coke deposition profiles in commercial spent hydroprocessing catalysts using Raman spectroscopy. Fuel, 2007, 86(7): 1122–1129

52 Ferrari A C, Robertson J. Interpretation of Raman spectra of disordered and amorphous carbon. Physical Review. B, 2000, 61(20): 14095–14107