Best operating conditions to produce hydroxyapatite nanoparticles by means of a spinning disc reactor

Abstract

In this work, Mg²⁺ doped hydroxyapatite (Mg-HAP) nanoparticles were produced by a reaction-precipitation process by using a spinning disc reactor (SDR) at high rotational speed. The production process of these nanoparticles consisted of the neutralization reaction between two aqueous solutions of calcium chloride and ammonia orthophosphate at room temperature. By operating at pH= 10, a high purity Mg-HAP nanoparticles were obtained. In particular, they were 51 nm in average size when the two reagents were fed over the disc symmetrically at 3 cm from the disc center and a rotational speed of the disc reactor equal to 1400 r/min was adopted.

Keywords

hydroxyapatite / nanoparticles / spinning disc reactor

References

[1] WebsterT J, Massa-SchlueterE, SmithJ, SlamovichE. Osteoblast response to hydroxyapatite doped with divalent and trivalent cations. Biomaterials, 2004, 25(11): 2111-2121

[2] PinaS, OlheroS, GheduzziS, MilesA, FerreiraJ. Influence of setting liquid composition and liquid-to-powder ratio on properties of a Mg-substituted calcium phosphate cement. Acta Biomaterialia, 2009, 5(4): 1233-1240

[3] LandiE, LogroscinoG, ProiettiL, TampieriA, SandriM, SiproS. Biomimetic Mg-substituted hydroxyapatite: from synthesis to in vivo behavior. Journal of Materials Science. Materials in Medicine, 2008, 19(1): 239-247

[4] Jahnen-DechentW, KettelerM. Magnesium basics. Clinical Kidney Journal, 2012, 5(Suppl 1): i3-i14

[5] LandiE, TampieriA, CelottiG, LangenatiR, SandriM, SiproS. Nucleation of hydroxyapatite in synthetic body fluid dense and porous scaffold development: from synthesis to in vivo behavior. Biomaterials, 2005, 26: 2835-2845

[6] BigiA, FaliniG, ForestiE, GazzanoM, RipamontiA, RoveriN. Magnesium influence on hydroxyapatite crystallization. Journal of Inorganic Biochemistry, 1993, 49(1): 69-78

[7] GibsonI R, BonfieldW. Preparation and characterization of magnesium/carbonate co-substituted hydroxyapatite. Journal of Materials Science. Materials in Medicine, 2002, 13(7): 685-693

[8] BigiA, FaliniG, ForestiE, GazzanoM, RipamontiA, RoveriN. Rietveld structure refinements of calcium hydroxyapatite containing magnesium. Acta Crystallographica. Section B, Structural Science, 1996, B52(1): 87-92

[9] CorreiaR N, MagalhanesM C F, MarquesP A, SenosA M. Wet synthesis and characterization of modified hydroxyapatite powders. Journal of Materials Science. Materials in Medicine, 1996, 7: 501

[10] FanovichM A, CastroM S, Porto LopezJ M. Analysis of the microstructural evolution in hydroxyapatite ceramics by electrical characterisation. Ceramics International, 1999, 25(6): 517-522

[11] BigiA, MarchettiF, RipamontiA, RoveriN, ForestiE. Magnesium and strontium interaction with carbonate-containing hydroxyapatite in aqueous medium. Journal of Inorganic Biochemistry, 1981, 15(4): 317-327

[12] AdzilaS, RameshS, SpoyanI, TanC Y, HamdiM, TengW D. Mechanochemical synthesis of magnesium doped hydroxyapatite: Powder characterization. Applied Mechanics and Materials, 2013, 372: 62-65

[13] RyuH S, HongK S, LeeJ K, KimD J, LeeJ H, ChangB S, LeeD H, LeeC K, ChungS S. Magnesia-doped HA/beta-TCP ceramics and evaluation of their biocompatibility. Biomaterials, 2004, 25(3): 393-401

[14] TautzenbergerA, KuvtunA, IgnatiusA. Nanoparticles and their potential for application in bone. International Journal of Nanomedicine, 2012, 7: 4545-4557

[15] BaffiG, CafieroM L, ChianeseA, JachuckR J. Process intensification: Precipitation of barium sulphate using a spinning disc reactor (SDR). Industrial & Engineering Chemistry Research, 2002, 41(21): 5240-5246

[16] de CaprariisB, Di RitaM, StollerM, VerdoneN, ChianeseA. Reaction-precipitation by a spinning disc reactor: Influence of hydrodynamics on nanoparticles production. Chemical Engineering Science, 2012, 76: 73-80

[17] SalimiM N, BridsonR H, GroverL M, LeekeG A. Effect of processing conditions on the formation of hydroxyapatite nanoparticles. Powder Technology, 2012, 218: 109-118

[18] LiJ, ChenY P, YinY, YaoF, YaoK. Modulation of nano-hydroxyapatite size via formation on chitosan-gelatin network film in situ. Biomaterials, 2007, 28(5): 781-790

[19] LandiE, TampieriA, Mattioli-BelmonteM, CelottiG, SandriM, GiganteA, FavaP, BiaginiG. Biomimetic Mg- and Mg,CO₃-substituted hydroxyapatites: Synthesis characterization and in vitro behaviour. Journal of the European Ceramic Society, 2006, 26(13): 2593-2601

[20] FadeevI V, ShvornevaL I, BarinovS M, OrlovskiiV P. Synthesis and structure of magnesium-substituted hydroxyapatite. Inorganic Materials, 2003, 39(9): 947-950

[21] SilversteinR M, WebsterF X. KeimLeD J. Spectrometric Identification of Organic Compounds. John Wiley & Sons, 2005, 82-108

RIGHTS & PERMISSIONS

2014 Higher Education Press and Springer-Verlag Berlin Heidelberg