Stress corrosion cracking of L360NS pipeline steel in sulfur environment

Abstract

Slow strain rate test (SSRT) and tensile fracture observation are applied to study the stress corrosion cracking (SCC) of L360NS pipeline steel. 5.0 wt. % sodium chloride solution containing elemental sulfur and 0.5 wt. % glacial acetic acid solution containing elemental sulfur are used. The results show that brittle fracture mainly occurs on the samples in high sulfur environment. In the sulfur suspension solution, the SCC sensitivity of L360NS pipeline steel increases along elemental sulfur content. In sulfur melting cladding condition, obvious corrosion can be observed with a large amount of corrosion pits appearing on the gauge section of the sample. The corrosion products are Fe_1+xS, black easily detached, and H₂. In sulfur suspension and sulfur melting cladding conditions, stress oriented hydrogen induced cracking (SOHIC) is the main cracking, which is caused by the joint effect of SCC and hydrogen induced cracking (HIC).

Keywords

Sour gas field / Elemental sulfur / SSRT / SCC

Acknowledgments

The Authors gratefully acknowledge the support from the National Natural Science foundation of China (No. 51474181) and Open Fund (PLN1516) of State Key Laboratory of Oil and Gas Reservoir Geology and Exploitation (Southwest Petroleum University).

References

[1] C. Shen, Z. Zhang, C. Zhang, The development of BG2250-125 Ni-based alloy tubing used in severe sour oil field, J. Eng. Sci. 12 (10) (2010) 35-38.

[2] C. Mendibide, T. Sourmail, C. Mendibide, Composition optimization of high-strength steels for sulfide stress cracking resistance improvement, J. Corros. Sci. 51 (12) (2009) 2878-2884.

[3] J. Kittel, V. Smanio, M. Fregonese, et al., Hydrogen induced cracking (HIC) testing of low alloy steel in sour environment: impact of time of exposure on the extent of damage, J. Corros. Sci. 52 (4) (2010) 1386-1392.

[4] V. Smanio, M. Fregonese, J. Kittel, et al., Wet hydrogen sulfide cracking of steel monitoring by acoustic emission: discrimination of AE sources, J. J. Mater. Sci. 45 (20) (2010) 5534-5542.

[5] E.M. Moore, Hydrogen-induced damage in sour wet crude pipelines, J. J. Petroleum Technol. 36 (4) (1984) 613-618.

[6] G. Svenningsen, A. Palencsar, J. Kvarekva, Investigation of iron sulfide surface layer growth in aqueous H2S/CO₂ environments, C. NACE International, 2009.

[7] S.B. Maldonadozagal, P.J. Boden, Hydrolysis of elemental sulphur in water and its effect on the corrosion of mild steel, J. Br. Corros. J. 17 (3) (1982) 116-120.

[8] X.H. Zhao, Y. Han, Z.Q. Bai, et al., The experiment research of corrosion behavior about Ni-based alloys in simulant solution containing H2S/CO2, J. Electrochem. Acta 56 (22) (2011) 7725-7731.

[9] H. Ockelmann, F.E. Blount, Ten Years' Experience with Sour Gas Production in Germany, C. Society of Petroleum Engineers, 1973.

[10] S.J. Li, F.P. Yang, F.J. Liu, A discussion on the sulphur deposition in the ground surface gathering and transmission system of the Puguang gas field, J. Nat. Gas. Ind. 31 (03) (2011) 75-79.

[11] A.B. Chesnoy, D.J. Pack, S 8 threatens natural gas operations environment, J. Oil Gas J. 95 (17) (1997) 74-79.

[12] D.J. Pack, Elemental Sulphur Formation in Natural Gas Transmission Pipelines, C. The University of Western, Australia, 2005.

[13] J.S. Qian, C.F. Chen, S.Y. Li, et al., Effect of element son corrosion behavior of nickel-base alloy G 3 in high temperature and high pressure environments containing H2S/CO2, J. Chin. J. Nonferrous Metals 22 (8) (2012) 2214-2222.

[14] C.Y. Gu, Q.F. Di, Z.H. Wang, Stress corrosion performance of N80 steel in formation water, J. Acta Pet. Sin. 27 (2) (2006) 141-144.

[15] M. Girgis, Challenges in Highly Sour Gas Environment Containing Elemental Sulphur, C. Society of Petroleum Engineers, 2008.

[16] B.E. Roberts, The effect of sulfur deposition on gas-well inflow performance, J. Spe Reserv. Eng. 12 (2) (1997) 118-123.

[17] N. Hands, B. Oz, B. Roberts, et al., Advances in the Prediction andManagement of Elemental Sulfur Deposition Associated with Sour Gas Production from Fractured Carbonate Reservoirs, C. Society of Petroleum Engineers, 2002.

[18] T. Gu, S.Q. Huo, F. Li, et al., Research and application of anti-corrosion technology in sour gas fields, J. Chem. Eng. Oil Gas 37 (S1) (2008) 63-72.

[19] J. Chen, L.L. Nie, J. Miao, et al., Corrosion behavior of X65 steel in element sulfur environment at different temperatures, J. Journal of Xian Technological University 11 (1) (2013) 1-20.

[20] Z.D. Liu, M.X. Lu, T. Gu, et al., Corrosion influencing factors of gathering and transportation system in sour gas fields under the presence of elemental sulfur, J. Corros. Prot. 33 (S1) (2012) 85-91.

[21] H. Guo, G.F. Li, X. Cai, et al., Effect of applied potentials on stress corrosion cracking of X70 pipeline steel in near-neutral-pH solutions, J. J. Chin. Soc. Corros. Prot. 24 (4) (2004) 208-212.

[22] S.B. Maldonado, P.J. Boden,The mechanism of corrosion of mild steel by elemental sulphur/water suspensions, in:C. 8th International Congress on Metallic Corrosion, 1981.

[23] Z. Liang, X. Li, C. Du, et al., Effect of applied potentials on stress corrosion cracking of X70 pipeline steel in alkali solution, J. Mater. Des. 30 (6) (2011) 2259-2263.

[24] P.F. Wang, C.F. Li, B. Wang, et al., Effect of CO₂ on H2S corrosion behaviors of casing steel, J. Journal of Southwest Petroleum University 11 (2007) 139-142.

[25] D.D. Macdonald, B. Roberts, J.B. Hyne, The corrosion of carbon steel by wet elemental sulphur, J. Corros. Sci. 18 (5) (1978) 411-425.

[26] O.I. Zvirko, S.F. Savula, V.M. Tsependa, et al., Stress corrosion cracking of gas pipeline steels of different strength, J. Proced. Struct. Integr. 2 (2016) 509-516.

[27] V. АVoloshyn, О.І. Zvirko, P.Y. Sydor, Influence of the compositions of neutral soil media on the corrosion cracking of pipe steel, J. Mater. Sci. 50 (5) (2015) 671-675.