Granulation mechanism and CO₂ capture performance of alkaline metal salt-promoted MgO sorbents

Abstract

Alkaline metal salt-promoted MgO sorbents are effective for CO₂ capture, but they face challenges with decreased CO₂ capture performance and powder elutriation in practical applications, arising due to the loss of pore structures and poor mechanical strength of alkaline metal salt-promoted MgO sorbent powder. Herein, granulation technology was employed to resolve the above problem. The optimized alkaline metal salt-promoted MgO sorbent pellets exhibited a CO₂ capture capacity of 11.46 mmol·g^–1 and a mechanical strength of 11.14 MPa. This mechanical strength was nearly three times greater than that of alkaline metal salt-promoted MgO sorbent pellets without granulation promoters. After 20 cycles, CO₂ capture capacity stabilized at 8.71 mmol·g^–1, while mechanical strength was maintained at 8.92 MPa. Through characterization, it was revealed that the pore structure generated by the pyrolysis of the granulation promoters notably increased the specific surface area, leading to high CO₂ capture capacity. Meanwhile, the strengthened mechanical strength of the alkaline metal salt-promoted MgO sorbent pellets was primarily due to the in situ formation of a γ-AlOOH sol-gel cluster skeleton. Thus, this study provides an effective technological pathway to enhance the performance of the alkaline metal salt-promoted MgO sorbent pellets for industrial applications.

Graphical abstract

Keywords

CO₂ capture / granulation promoters / granulation mechanism / alkaline metal salt-promoted MgO sorbent pellets / mechanical strength

References

[1] Jiang T , Zhang H , Xu Z , Zhao Y , Wang S . Scale-up production and process optimization of Zr-doped CaO-based sorbent for CO₂ capture. Asia-Pacific Journal of Chemical Engineering, 2020, 15(5): e2502

[2] Chen W H , Chen C Y . Water gas shift reaction for hydrogen production and carbon dioxide capture: a review. Applied Energy, 2020, 258: 114078

[3] Gao W , Zhou T , Gao Y , Wang Q . Enhanced water gas shift processes for carbon dioxide capture and hydrogen production. Applied Energy, 2019, 254: 113700

[4] Liu D , Hu Y , Feng Q , Fu R . Synthesis of spherical CaO pellets incorporated with Mg, Y, and Ce inert carriers for CO₂ capture. Environmental Science and Pollution Research International, 2024, 31(14): 21224–21234

[5] Omodolor I S , Otor H O , Andonegui J A , Allen B J , Alba-Rubio A C . Dual-function materials for CO₂ capture and conversion: a review. Industrial & Engineering Chemistry Research, 2020, 59(40): 17612–17631

[6] Li J , Wang T , Liu P , Li Z . Dynamic modelling and simulation of a post-combustion CO₂ capture process for coal-fired power plants. Frontiers of Chemical Science and Engineering, 2022, 16(2): 198–209

[7] Yu H , Wang X , Shu Z , Fujii M , Song C . Al₂O₃ and CeO₂-promoted MgO sorbents for CO₂ capture at moderate temperatures. Frontiers of Chemical Science and Engineering, 2018, 12(1): 83–93

[8] Najmi B , Bolland O , Colombo K E . Load-following performance of IGCC with integrated CO₂ capture using SEWGS pre-combustion technology. International Journal of Greenhouse Gas Control, 2015, 35: 30–46

[9] Yang X , Zhao L , Liu Y , Sun Z , Xiao Y . Carbonation performance of NaNO₃ modified MgO sorbents. Industrial & Engineering Chemistry Research, 2017, 56(1): 342–350

[10] Donat F , Müller C R . Prospects of MgO-based sorbents for CO₂ capture applications at high temperatures. Current Opinion in Green and Sustainable Chemistry, 2022, 36: 100645

[11] Lu H , Lu Y , Rostam-Abadi M . CO₂ sorbents for a sorption-enhanced water-gas-shift process in IGCC plants: a thermodynamic analysis and process simulation study. International Journal of Hydrogen Energy, 2013, 38(16): 6663–6672

[12] Liu Y , Li Z , Xu L , Cai N . Effect of sorbent type on the sorption enhanced water gas shift process in a fluidized bed reactor. Industrial & Engineering Chemistry Research, 2012, 51(37): 11989–11997

[13] Sun H , Zhang Y , Guan S , Huang J , Wu C . Direct and highly selective conversion of captured CO₂ into methane through integrated carbon capture and utilization over dual functional materials. Journal of CO₂ Utilization, 2020, 38: 262–272

[14] Dunstan M T , Donat F , Bork A H , Grey C P , Müller C R . CO₂ capture at medium to high temperature using solid oxide-based sorbents: fundamental aspects, mechanistic insights, and recent advances. Chemical Reviews, 2021, 121(20): 12681–12745

[15] Landuyt A , Kumar P V , Yuwono J A , Bork A H , Donat F , Abdala P M , Müller C R . Uncovering the CO₂ capture mechanism of NaNO₃-promoted MgO by ¹⁸O isotope labeling. JACS Au, 2022, 2(12): 2731–2741

[16] Tregambi C , Mancusi E , Solimene R , Pepe F . Modeling of an autothermal process for integrated carbon dioxide capture and methanation by magnesium looping (MgO/MgCO₃) and renewable hydrogen. Industrial & Engineering Chemistry Research, 2023, 62(51): 22016–22027

[17] Qiao Y , Wang J , Zhang Y , Gao W , Harada T , Huang L , Hatton T A , Wang Q . Alkali nitrates molten salt modified commercial MgO for intermediate-temperature CO₂ capture: optimization of the Li/Na/K ratio. Industrial & Engineering Chemistry Research, 2017, 56(6): 1509–1517

[18] Kim S M , Armutlulu A , Kierzkowska A M , Hosseini D , Donat F . Development of an effective bi-functional Ni-CaO catalyst-sorbent for the sorption-enhanced water gas shift reaction through structural optimization and the controlled deposition of a stabilizer by atomic layer deposition. Sustainable Energy & Fuels, 2020, 4(2): 713–729

[19] Dong H , Cui H , Zhou Z . Promoting effects of Li₃PO₄ and CaCO₃ on the intermediate-temperature CO₂ adsorption over molten NaNO₃-promoted MgO-based sorbents. Chemical Engineering Journal, 2022, 442: 136133

[20] Ruhaimi A H , Aziz M a A , Jalil A A . Magnesium oxide-based adsorbents for carbon dioxide capture: current progress and future opportunities. Journal of CO₂ Utilization, 2021, 43: 101357

[21] Cui H , Zhang Q , Hu Y , Peng C , Fang X , Cheng Z , Galvita V V , Zhou Z . Ultrafast and stable CO₂ capture using alkali metal salt-promoted MgO-CaCO₃ sorbents. ACS Applied Materials & Interfaces, 2018, 10(24): 20611–20620

[22] Harada T , Simeon F , Hamad E Z , Hatton T A . Alkali metal nitrate-promoted high-capacity MgO adsorbents for regenerable CO₂ capture at moderate temperatures. Chemistry of Materials, 2015, 27(6): 1943–1949

[23] Dal Pozzo A , Armutlulu A , Rekhtina M , Abdala P M , Müller C R . CO₂ uptake and cyclic stability of MgO-based CO₂ sorbents promoted with alkali metal nitrates and their eutectic mixtures. ACS Applied Energy Materials, 2019, 2(2): 1295–1307

[24] Teixeira P , Correia P , Pinheiro C I C . CO₂ capture by CaCO₃-MgO and CeO₂-MgO sorbents promoted by ternary alkali metal salts in a fixed bed reactor. Chemical Engineering Science, 2024, 289: 119856

[25] Guo Y F , Sun J , Wang R L , Li W , Zhao C , Li C , Zhang J . Recent advances in potassium-based adsorbents for CO₂ capture and separation: a review. Carbon Capture Science & Technology, 2021, 1: 100011

[26] Liu C , Lin Q , Han Y , Wu S . High-temperature attrition of nano CaO-based CO₂-reactive adsorbents in the calcium looping process. Industrial & Engineering Chemistry Research, 2020, 59(36): 16052–16058

[27] Zhou Y , Chen Y , Li W , Li K , Jia Z , Sun J , Zhao C . . High-temperature CO₂ uptake and mechanical strength enhancement of the calcium aluminate cement-bound carbide slag pellets. Energy & Fuels, 2021, 35(9): 8117–8125

[28] Sun J , Liu W , Hu Y , Wu J , Li M , Yang X , Wang W , Xu M . Enhanced performance of extruded-spheronized carbide slag pellets for high temperature CO₂ capture. Chemical Engineering Journal, 2016, 285: 293–303

[29] Zheng Y , Wu J , Zhang L , Guo Y , Xu Z , Huang Y , Huang P , Zhang Z , Zhao C . Unravelling the pore templating effect on CO₂ adsorption performance of alkali metal nitrates promoted MgO pellets. Chemical Engineering Journal, 2022, 450: 137944

[30] Zhang H , Jiang T , Yaseen H A S M , Zhao Y , Wang S , Ma X . Pelletization and attrition of CaO-based adsorbent for CO₂ capture. Asia-Pacific Journal of Chemical Engineering, 2021, 16(4): e2656

[31] Jiang T , Liu Z , Fang Z , Dramane T A , Zhao Y , Wang S , Ma X . Pelletizing and acid modifying of Zr-stabilized CaO-based sorbent for cyclic high-temperature CO₂ capture. Separation and Purification Technology, 2024, 344: 127309

[32] Zhang X , Liu W , Zhou S , Li Z , Sun J , Hu Y , Yang Y . A review on granulation of CaO-based sorbent for carbon dioxide capture. Chemical Engineering Journal, 2022, 446: 136880

[33] Ding Y , Zhao X , Chen L , Ma L , Liao Q , Zhu X , Wang H . Hydration activation of MgO pellets for CO₂ adsorption. Industrial & Engineering Chemistry Research, 2021, 60(14): 5310–5318

[34] Qin C , Yin J , An H , Liu W , Feng B . Performance of extruded particles from calcium hydroxide and cement for CO₂ capture. Energy & Fuels, 2012, 26(1): 154–161

[35] Qin C , Du H , Liu L , Yin J , Feng B . CO₂ capture performance and attrition property of CaO-based pellets manufactured from organometallic calcium precursors by extrusion. Energy & Fuels, 2014, 28(1): 329–339

[36] Hu Y , Liu X , Zhou Z , Liu W , Xu M . Pelletization of MgO-based sorbents for intermediate temperature CO₂ capture. Fuel, 2017, 187: 328–337

[37] Hu Y , Liu W , Peng Y , Yang Y , Sun J , Chen H , Zhou Z , Xu M . One-step synthesis of highly efficient CaO-based CO₂ sorbent pellets via gel-casting technique. Fuel Processing Technology, 2017, 160: 70–77

[38] Xu Z , Jiang T , Zhang H , Zhao Y , Ma X , Wang S . Efficient MgO-doped CaO sorbent pellets for high temperature CO₂ capture. Frontiers of Chemical Science and Engineering, 2021, 15(3): 698–708

[39] Chen H , Liu W , Sun J , Hu Y , Wang W , Yang Y , Yao S , Xu M . Routine investigation of CO₂ sorption enhancement for extruded-spheronized CaO-based pellets. Energy & Fuels, 2017, 31(9): 9660–9667

[40] Chen J , Duan L , Donat F , Müller C R . Assessment of the effect of process conditions and material characteristics of alkali metal salt promoted MgO-based sorbents on their CO₂ capture performance. ACS Sustainable Chemistry & Engineering, 2021, 9(19): 6659–6672

[41] Broda M , Manovic V , Anthony E J , Müller C R . Effect of pelletization and addition of steam on the cyclic performance of carbon-templated, CaO-based CO₂ sorbents. Environmental Science & Technology, 2014, 48(9): 5322–5328

[42] Hu Y , Lu H , Li H . Li₄SiO₄ pellets templated by rice husk for cyclic CO₂ capture: insight into the modification mechanism. Ceramics International, 2021, 47(22): 32060–32067

[43] Deng G , Zhou Z , Nie G , Huang C , Xu Z , Sun Z , Duan L . MgO-based granular sorbent pelletized by using ordered mesoporous silica as binder for low-temperature CO₂ capture. Energy & Fuels, 2024, 38(4): 3238–3250

[44] Cai Y , Liu W , Sun Z , Yang Y , Li P . Granulation of alkaline metal nitrate promoted MgO adsorbents and the low-concentration CO₂ capture performance in the fixed bed adsorber. Journal of CO₂ Utilization, 2022, 61: 102047

[45] Liyanapathirana C , Shahidi F . Optimization of extraction of phenolic compounds from wheat using response surface methodology. Food Chemistry, 2005, 93(1): 47–56

[46] Amiri M , Shahhosseini S , Ghaemi A . Optimization of CO₂ capture process from simulated flue gas by dry regenerable alkali metal carbonate based adsorbent using response surface methodology. Energy & Fuels, 2017, 31(5): 5286–5296

[47] Qu T , Zhang J , Song J , Jing J , Li W Y . Promotional effect of NaNO₃/NaNO₂ on CO₂ adsorption performance of MgO sorbents. Chemical Engineering Science, 2024, 299: 120503

[48] SongJ BQuTJingJ Y. Granulation of molten salt-promoted MgO adsorbents for intermediate-temperature CO₂ capture. In Proceedings of 21st International Conference on Carbon Dioxide Utilization. Dalian, 2024

[49] Song J , Qu T , Zhang J , Jia Y , Jing J , Li W Y . Enhancing cyclic stability and anti-sintering capacity of CaCO₃-MgO sorbents for CO₂ capture. Chemical Engineering Science, 2025, 309: 121433

[50] Wang K , Zhao Y , Clough P T , Zhao P , Anthony E J . Structural and kinetic analysis of CO₂ sorption on NaNO₂-promoted MgO at moderate temperatures. Chemical Engineering Journal, 2019, 372: 886–895

[51] Jin S , Ko K J , Lee C H . Direct formation of hierarchically porous MgO-based sorbent bead for enhanced CO₂ capture at intermediate temperatures. Chemical Engineering Journal, 2019, 371: 64–77

[52] Jin S , Ko K J , Song Y G , Lee K , Lee C H . Fabrication and kinetic study of spherical MgO agglomerates via water-in-oil method for pre-combustion CO₂ capture. Chemical Engineering Journal, 2019, 359: 285–297

[53] Li Y , Zhao C , Chen H , Liang C , Duan L , Zhou W . Modified CaO-based sorbent looping cycle for CO₂ mitigation. Fuel, 2009, 88(4): 697–704

[54] Xu B , Fu R , Liu Y , Hu Y . Fabrication of CaO pellets via polyvinyl alcohol (PVA) method for efficient CO₂ capture and solar energy storage. Separation and Purification Technology, 2024, 335: 126135

[55] Shefer K I , Cherepanova S V , Moroz É M , Gerasimov E Y , Tsybulya S V . Features of the real structure of pseudoboehmites: violations of the structure and layer packing caused by crystallization water. Journal of Structural Chemistry, 2010, 51(1): 132–141

[56] Adrián Z J , Merced M , Satoshi T . Maximum solid loading dispersion of pseudo-boehmite nano-fiber. Journal of The Australian Ceramic Society, 2015, 51(2): 40–46

RIGHTS & PERMISSIONS

Higher Education Press