Experimental investigation of evolutive mode-I and mode-II fracture behavior of fiber-reinforced cemented paste backfill: Effect of curing temperature and curing time

Abstract

The curing temperature-dependent cement hydration causes the nonlinear evolution of fracture behavior and properties of fiber-reinforced cemented paste backfill (CPB) and thus influences the stability of mine backfill materials in deep mines. Therefore, the coupled effect of curing temperature (20, 35, and 45 °C) and cement hydration at different curing times (3, 7, and 28 d) on the mode-I and mode-II fracture behavior and properties of fiber-reinforced CPB is investigated. A comprehensive experimental testing program consisting of semicircular bend tests, direct shear tests, measurement of volumetric water content and matric suction, TG/DTG tests, and SEM observation is carried out. The results show that the coupled thermochemical effect results in strongly nonlinear development of pre- and post-peak behavior of fiber-reinforced CPB. Moreover, the results discover a positive linear correlation between fracture toughness and shear strength parameters and also reveal the vital role played by matric suction in the formation of fracture toughness. Furthermore, predictive functions are developed to estimate the coupled thermochemical effect on the development of K_Ic and K_IIc. Therefore, the findings and the developed mathematical tools have the potential to promote the successful application of fiber-reinforced CPB technology in deep underground mines.

Graphical abstract

Keywords

fiber reinforcement / cemented paste backfill / fracture behavior / underground mine / cement hydration

References

[1] Yılmaz T, Ercikdi B. Predicting the uniaxial compressive strength of cemented paste backfill from ultrasonic pulse velocity test. Nondestructive Testing and Evaluation, 2016, 31(3): 247–266

[2] Sari M, Yilmaz E, Kasap T, Guner N U. Strength and microstructure evolution in cemented mine backfill with low and high pH pyritic tailings: Effect of mineral admixtures. Construction & Building Materials, 2022, 328: 127109

[3] Ercikdi B, Külekci G, Yılmaz T. Utilization of granulated marble wastes and waste bricks as mineral admixture in cemented paste backfill of sulphide-rich tailings. Construction & Building Materials, 2015, 93: 573–583

[4] Libos I L S, Cui L. Time- and temperature-dependence of compressive and tensile behaviors of polypropylene fiber-reinforced cemented paste backfill. Frontiers of Structural and Civil Engineering, 2021, 15(4): 1025–1037

[5] Yılmaz T, Ercikdi B. Effect of construction and demolition waste on the long-term geo-environmental behaviour of cemented paste backfill. International Journal of Environmental Science and Technology, 2022, 19(5): 3701–3714

[6] Cavusoglu I, Yilmaz E, Yilmaz A O. Sodium silicate effect on setting properties, strength behavior and microstructure of cemented coal fly ash backfill. Powder Technology, 2021, 384: 17–28

[7] Qi C, Guo L, Wu Y, Zhang Q, Chen Q. Stability evaluation of layered backfill considering filling interval, backfill strength and creep behavior. Minerals (Basel), 2022, 12(2): 1–16

[8] Zhang H, Cao S, Yilmaz E. Influence of 3D-printed polymer structures on dynamic splitting and crack propagation behavior of cementitious tailings backfill. Construction & Building Materials, 2022, 343: 128137

[9] Li J, Cao S, Yilmaz E, Liu Y. Compressive fatigue behavior and failure evolution of additive fiber-reinforced cemented tailings composites. International Journal of Minerals Metallurgy and Materials, 2022, 29(2): 345–355

[10] Xue G, Yilmaz E, Song W, Cao S. Mechanical, flexural and microstructural properties of cement-tailings matrix composites: Effects of fiber type and dosage. Composites. Part B, Engineering, 2019, 172: 131–142

[11] Yi X W, Ma G W, Fourie A. Centrifuge model studies on the stability of fibre-reinforced cemented paste backfill stopes. Geotextiles and Geomembranes, 2018, 46(4): 396–401

[12] ZhaoZCaoSYilmazE. Effect of layer thickness on flexural property and microstructure of 3D printed rhomboid polymer reinforced cemented tailings composites. International Journal of Minerals Metallurgy and Materials, 2023, 30: 236–249

[13] Chakilam S, Cui L. Effect of polypropylene fiber content and fiber length on the saturated hydraulic conductivity of hydrating cemented paste backfill. Construction & Building Materials, 2020, 262: 120854

[14] Cao S, Yilmaz E, Yin Z, Xue G, Song W, Sun L. CT scanning of internal crack mechanism and strength behavior of cement-fiber-tailings matrix composites. Cement and Concrete Composites, 2021, 116: 103865

[15] Wang A, Cao S, Yilmaz E. Effect of height to diameter ratio on dynamic characteristics of cemented tailings backfills with fiber reinforcement through impact loading. Construction & Building Materials, 2022, 322: 126448

[16] Chen X, Shi X, Zhang S, Chen H, Zhou J, Yu Z, Huang P. Fiber-reinforced cemented paste backfill: The effect of fiber on strength properties and estimation of strength using nonlinear models. Materials (Basel), 2020, 13(3): 1–20

[17] Wang Y, Yu Z, Wang H. Experimental investigation on some performance of rubber fiber modified cemented paste backfill. Construction & Building Materials, 2021, 271: 121586

[18] Yi X, Ma G, Fourie A. Compressive behaviour of fibre-reinforced cemented paste backfill. Geotextiles and Geomembranes, 2015, 43(3): 207–215

[19] Wang C, Ren Z, Huo Z, Zheng Y, Tian X, Zhang K, Zhao G. Properties and hydration characteristics of mine cemented paste backfill material containing secondary smelting water-granulated nickel slag. Alexandria Engineering Journal, 2021, 60(6): 4961–4971

[20] Torabi A R, Pirhadi E. Extension of the virtual isotropic material concept to mixed mode I/II loading for predicting the last-ply-failure of U-notched glass/epoxy laminated composite specimens. Composites. Part B, Engineering, 2019, 176: 107287

[21] Torabi A R, Majidi H R, Cicero S, Ibáñez-Gutiérrez F T, Fuentes J D. Experimental verification of the Fictitious Material Concept for tensile fracture in short glass fibre reinforced polyamide 6 notched specimens with variable moisture. Engineering Fracture Mechanics, 2019, 212: 95–105

[22] Ajayi O, Le Pen L, Zervos A, Powrie W. A behavioural framework for fibre-reinforced gravel. Geotechnique, 2017, 67(1): 56–68

[23] Jahanbakhsh P, Saberi K F, Soltaninejad M, Hashemi S H. Laboratory investigation of modified roller compacted concrete pavement (RCCP) containing macro synthetic fibers. International Journal of Pavement Research and Technology, 2022, 1–15

[24] Wang W, Kang H, Li N, Guo J, Girma D Y, Liu Y. Experimental investigations on the mechanical and microscopic behavior of cement-treated clay modified by nano-MgO and fibers. International Journal of Geomechanics, 2022, 22(6): 04022059

[25] Dong Q, Liang B, Jia L, Jiang L. Effect of sulfide on the long-term strength of lead-Zinc tailings cemented paste backfill. Construction & Building Materials, 2019, 200: 436–446

[26] Libos I L S, Cui L. Effects of curing time, cement content, and saturation state on mode-I fracture toughness of cemented paste backfill. Engineering Fracture Mechanics, 2020, 235: 107174

[27] Liu J, Li Y, Qiao L. Analytical solutions of stress intensity factors for a centrally cracked brazilian disc considering tangential friction effects. Rock Mechanics and Rock Engineering, 2022, 55(4): 2459–2470

[28] Xu W, Cao P. Fracture behaviour of cemented tailing backfill with pre-existing crack and thermal treatment under three-point bending loading: Experimental studies and particle flow code simulation. Engineering Fracture Mechanics, 2018, 195: 129–141

[29] Wang X, Yu J, Li Q, Yu Y, Lv H. Study on the crack evolution process and stress redistribution near crack tip in soil. International Journal of Geomechanics, 2022, 22(1): 04021255

[30] Liu J, Zhao L, Chang F, Chi L. Mechanical properties and microstructure of multilayer graphene oxide cement mortar. Frontiers of Structural and Civil Engineering, 2021, 15(4): 1058–1070

[31] Raffaldi M J, Seymour J B, Richardson J, Zahl E, Board M. Cemented paste backfill geomechanics at a narrow-vein underhand cut-and-fill mine. Rock Mechanics and Rock Engineering, 2019, 52(12): 4925–4940

[32] Fang K, Fall M. Effects of curing temperature on shear behaviour of cemented paste backfill-rock interface. International Journal of Rock Mechanics and Mining Sciences, 2018, 112: 184–192

[33] Fang K, Ren L, Jiang H. Development of Mode I and Mode II fracture toughness of cemented paste backfill: Experimental results of the effect of mix proportion, temperature and chemistry of the pore water. Engineering Fracture Mechanics, 2021, 258: 108096

[34] YilmazEFallM. Paste Tailings Management. Cham: Springer International, 2017

[35] Fang K, Fall M. Chemically induced changes in the shear behaviour of interface between rock and tailings backfill undergoing cementation. Rock Mechanics and Rock Engineering, 2019, 52(9): 3047–3062

[36] Libos I L S, Cui L, Liu X. Effect of curing temperature on time-dependent shear behavior and properties of polypropylene fiber-reinforced cemented paste backfill. Construction & Building Materials, 2021, 311: 125302

[37] Koohestani B, Belem T, Koubaa A, Bussière B. Experimental investigation into the compressive strength development of cemented paste backfill containing nano-silica. Cement and Concrete Composites, 2016, 72: 180–189

[38] Ayatollahi M R, Aliha M R M. Fracture parameters for a cracked semi-circular specimen. International Journal of Rock Mechanics and Mining Sciences, 2004, 41: 20–25

[39] Lim I L, Johnston I W, Choi S K. Stress intensity factors for semi-circular specimens under three-point bending. Engineering Fracture Mechanics, 1993, 44(3): 363–382

[40] MatsudaS. Theoretical approach to determine dynamic fatigue strength characteristics of ceramics under variable loading rates on the basis of SCG concept. International Journal of Fracture, 2019, 215(1−2): 175−182

[41] Torabi A R, Jabbari M, Akbardoost J. Scaling effects on notch fracture toughness of graphite specimens under mode I loading. Engineering Fracture Mechanics, 2020, 235: 107153

[42] Huang S, Yan E, Fang K, Li X. Effects of binder type and dosage on the mode I fracture toughness of cemented paste backfill-related structures. Construction & Building Materials, 2021, 270: 121854

[43] Feng G, Kang Y, Wang X. Fracture failure of granite after varied durations of thermal treatment: An experimental study. Royal Society Open Science, 2019, 6(7): 190144

[44] Ayatollahi M R, Aliha M R M. Wide range data for crack tip parameters in two disc-type specimens under mixed mode loading. Computational Materials Science, 2007, 38(4): 660–670

[45] Torabi A R, Jabbari M, Akbardoost J. Mixed mode notch fracture toughness assessment of quasi-brittle polymeric specimens at different scales. Theoretical and Applied Fracture Mechanics, 2020, 109: 102682

[46] Torabi A R, Pirhadi E. Translaminar notch fracture toughness expressions for composite laminates. Theoretical and Applied Fracture Mechanics, 2022, 119: 103332

[47] Fang K, Cui L. Experimental investigation of fiber content and length on curing time-dependent mode-I fracture behavior and properties of cemented paste backfill and implication to engineering design. Fatigue & Fracture of Engineering Materials & Structures, 2022, 45(11): 3302–3318

[48] Torabi A R, Rahimi A S, Ayatollahi M R. Tensile fracture analysis of a ductile polymeric material weakened by U-notches. Polymer Testing, 2017, 64: 117–126

[49] Torabi A R, Rahimi A S, Ayatollahi M R. Fracture study of a ductile polymer-based nanocomposite weakened by blunt V-notches under mode I loading: Application of the Equivalent Material Concept. Theoretical and Applied Fracture Mechanics, 2018, 94: 26–33

[50] Torabi A R, Rahimi A S, Ayatollahi M R. Elastic-plastic fracture assessment of CNT-reinforced epoxy/nanocomposite specimens weakened by U-shaped notches under mixed mode loading. Composites. Part B, Engineering, 2019, 176: 107114

[51] Torabi A R, Rahimi A S, Ayatollahi M R. Mixed mode I/II fracture prediction of blunt V-notched nanocomposite specimens with nonlinear behavior by means of the Equivalent Material Concept. Composites. Part B, Engineering, 2018, 154: 363–373

[52] Rahimi A S, Ayatollahi M R, Torabi A R. Ductile failure analysis of blunt V-notched epoxy resin plates subjected to combined tension-shear loading. Polymer Testing, 2018, 70: 57–66

[53] Aliha M R M, Saghafi H. The effects of thickness and Poisson’s ratio on 3D mixed-mode fracture. Engineering Fracture Mechanics, 2013, 98: 15–28

[54] Yuan X, Tian Y, Liu Q, Liu S, Dou Q, Aliha M R M. K_Ic and K_IIc measurement for hot mix asphalt mixtures at low temperature: Experimental and theoretical study using the semicircular bend specimen with different thicknesses. Fatigue & Fracture of Engineering Materials & Structures, 2021, 44(3): 832–846

[55] Vizini V O S, Futai M M. Mode II fracture toughness determination of rock and concrete via Modified Direct Shear Test. Engineering Fracture Mechanics, 2021, 257: 108007

[56] Holthusen D, Batistão A C, Reichert J M. Amplitude sweep tests to comprehensively characterize soil micromechanics: Brittle and elastic interparticle bonds and their interference with major soil aggregation factors organic matter and water content. Rheologica Acta, 2020, 59(8): 545–563

[57] Barani O R, Khoei A R, Mofid M. Modeling of cohesive crack growth in partially saturated porous media: A study on the permeability of cohesive fracture. International Journal of Fracture, 2011, 167(1): 15–31

[58] Shen Z, Jiang M, Thornton C. Shear strength of unsaturated granular soils: Three-dimensional discrete element analyses. Granular Matter, 2016, 18(3): 1–13

[59] Rahimi-Aghdam S, Bažant Z P, Abdolhosseini Qomi M J. Cement hydration from hours to centuries controlled by diffusion through barrier shells of CSH. Journal of the Mechanics and Physics of Solids, 2017, 99: 211–224

[60] Dong P, Allahverdi A, Andrei C M, Bassim N D. Liquid cell transmission electron microscopy reveals C-S-H growth mechanism during Portland cement hydration. Materialia, 2022, 22: 101387

[61] Jiang H, Fall M, Li Y, Han J. An experimental study on compressive behaviour of cemented rockfill. Construction & Building Materials, 2019, 213: 10–19

[62] Yilmaz E, Belem T, Bussière B, Mbonimpa M, Benzaazoua M. Curing time effect on consolidation behaviour of cemented paste backfill containing different cement types and contents. Construction & Building Materials, 2015, 75: 99–111

[63] Pane I, Hansen W. Investigation of blended cement hydration by isothermal calorimetry and thermal analysis. Cement and Concrete Research, 2005, 35(6): 1155–1164

[64] Ahmadinezhad A, Jafarzadeh F, Sadeghi H. Combination of water head control and axis translation techniques in new unsaturated cyclic simple shear tests. Soil Dynamics and Earthquake Engineering, 2019, 126: 105818

[65] Lu S, Lu Y, Peng W, Ju Z, Ren T. A generalized relationship between thermal conductivity and matric suction of soils. Geoderma, 2019, 337: 491–497

[66] Cui L, Fall M. An evolutive elasto-plastic model for cemented paste backfill. Computers and Geotechnics, 2016, 71: 19–29

[67] Cui L, Fall M. A coupled thermo–hydro-mechanical–chemical model for underground cemented tailings backfill. Tunnelling and Underground Space Technology, 2015, 50: 396–414

[68] Fang K, Fall M. Shear behaviour of rock–tailings backfill interface: Effect of cementation, rock type, and rock surface roughness. Geotechnical and Geological Engineering, 2021, 39(3): 1753–1770

[69] Cui L, Fall M. Mechanical and thermal properties of cemented tailings materials at early ages: Influence of initial temperature, curing stress and drainage conditions. Construction & Building Materials, 2016, 125: 553–563

RIGHTS & PERMISSIONS

Higher Education Press