Development of mix design method based on statistical analysis of different factors for geopolymer concrete

Abstract

The present study proposes the mix design method of Fly Ash (FA) based geopolymer concrete using Response Surface Methodology (RSM). In this method, different factors, including binder content, alkali/binder ratio, NS/NH ratio (sodium silicate/sodium hydroxide), NH molarity, and water/solids ratio were considered for the mix design of geopolymer concrete. The 2D contour plots were used to setup the mix design method to achieve the target compressive strength. The proposed mix design method of geopolymer concrete is divided into three categories based on curing regime, specifically one ambient curing (25 °C) and two heat curing (60 and 90 °C). The proposed mix design method of geopolymer concrete was validated through experimentation of M30, M50, and M70 concrete mixes at all curing regimes. The observed experimental compressive strength results validate the mix design method by more than 90% of their target strength. Furthermore, the current study concluded that the required compressive strength can be achieved by varying any factor in the mix design. In addition, the factor analysis revealed that the NS/NH ratio significantly affects the compressive strength of geopolymer concrete.

Graphical abstract

Keywords

geopolymer concrete / mix design / fly ash / response surface methodology / compressive strength / stress−strain

References

[1] Rashad A M, Sadek D M, Hassan H A. An investigation on blast-furnace stag as fine aggregate in alkali-activated slag mortars subjected to elevated temperatures. Journal of Cleaner Production, 2016, 112: 1086–1096

[2] Ali M B, Saidur R, Hossain M S. A review on emission analysis in cement industries. Renewable and Sustainable Energy Reviews, 2011, 15: 2252–2261

[3] DavidovitsJ. Geopolymer Institute Library. Technical Paper #24, False-CO₂-Values. Saint-Quentin: Geopolymer institute library, 2015

[4] Gunasekara C, Law D W, Setunge S. Long term permeation properties of different fly ash geopolymer concretes. Construction & Building Materials, 2016, 124: 352–362

[5] Kong D L Y, Sanjayan J G, Sagoe-Crentsil K. Factors affecting the performance of metakaolin geopolymers exposed to elevated temperatures. Journal of Materials Science, 2008, 43(3): 824–831

[6] Davidovits J. Geopolymers. Journal of Thermal Analysis, 1991, 37(8): 1633–1656

[7] Bernal S A, Mejía De Gutiérrez R, Pedraza A L, Provis J L, Rodriguez E D, Delvasto S. Effect of binder content on the performance of alkali-activated slag concretes. Cement and Concrete Research, 2011, 41(1): 1–8

[8] Hardjito D, Wallah S E, Sumajouw D M J, Rangan B. V: Fly ash-based geopolymer concrete. Australian Journal of Structrural Engineering, 2005, 6(1): 77–86

[9] Verma M, Dev N. Sodium hydroxide effect on the mechanical properties of flyash-slag based geopolymer concrete. Structural Concrete, 2021, 22(S1): E368–E379

[10] Noushini A, Castel A. The effect of heat-curing on transport properties of low-calcium fly ash-based geopolymer concrete. Construction & Building Materials, 2016, 112: 464–477

[11] Hassan A, Arif M, Shariq M. Effect of curing condition on the mechanical properties of fly ash-based geopolymer concrete. SN Applied Sciences, 2019, 1(12): 1694

[12] Kong D L Y, Sanjayan J G. Effect of elevated temperatures on geopolymer paste, mortar and concrete. Cement and Concrete Research, 2010, 40(2): 334–339

[13] Mallikarjuna Rao G, Gunneswara Rao T D. A quantitative method of approach in designing the mix proportions of fly ash and GGBS-based geopolymer concrete. Australian Journal of Civil Engineering, 2018, 16(1): 53–63

[14] Nath P, Sarker P K. Effect of GGBFS on setting, workability and early strength properties of fly ash geopolymer concrete cured in ambient condition. Construction & Building Materials, 2014, 66: 163–171

[15] Nagajothi S, Elavenil S. Effect of GGBS addition on reactivity and microstructure properties of ambient cured fly ash based geopolymer concrete. Silicon, 2021, 13: 507–516

[16] Li N, Shi C, Zhang Z, Zhu D, Hwang H J, Zhu Y, Sun T. A mixture proportioning method for the development of performance-based alkali-activated slag-based concrete. Cement and Concrete Composites, 2018, 93: 163–174

[17] Pavithra P, Srinivasula Reddy M, Dinakar P, Hanumantha Rao B, Satpathy B K, Mohanty A N. A mix design procedure for geopolymer concrete with fly ash. Journal of Cleaner Production, 2016, 133: 117–125

[18] Patankar S V, Ghugal Y M, Jamkar S S. Mix design of fly ash based geopolymer concrete. In: Proceeding of Advances in Structural Engineering: Materials, Volume Three. Springer New Delhi, 2015, 1619–1634

[19] FerdousM WKayaliOKhennaneA. A detailed procedure of mix design for fly ash based geopolymer concrete. In: Proceedings of the Fourth Asia-Pacific Conference on FRP in Structures (APFIS 2013). Melbourne: International Institute for FRP in Construction, 2013

[20] Anuradha R, Sreevidya V, Venkatasubramani R, Rangan B V. Modified guidelines for geopolymer concrete mix design using indian standard. Asian Journal of Civil Engineering, 2012, 13: 357–368

[21] Talha Junaid M, Kayali O, Khennane A, Black J. A mix design procedure for low calcium alkali activated fly ash-based concretes. Construction & Building Materials, 2015, 79: 301–310

[22] Luan C, Shi X, Zhang K, Utashev N, Yang F, Dai J, Wang Q. A mix design method of fly ash geopolymer concrete based on factors analysis. Construction & Building Materials, 2021, 272: 121612

[23] Bondar D, Ma Q, Soutsos M, Basheer M, Provis J L, Nanukuttan S. Alkali activated slag concretes designed for a desired slump, strength and chloride diffusivity. Construction & Building Materials, 2018, 190: 191–199

[24] Hadi M N S, Farhan N A, Sheikh M N. Design of geopolymer concrete with GGBFS at ambient curing condition using Taguchi method. Construction & Building Materials, 2017, 140: 424–431

[25] Karthik S, Saravana K, Mohan R. A Taguchi approach for optimizing design mixture of geopolymer concrete incorporating fly ash. Ground Granulated Blast Furnace Slag and Silica Fume, Crystals, 2021, 11: 1079

[26] Riahi S, Nazari A, Zaarei D, Khalaj G, Bohlooli H, Kaykha M M. Compressive strength of ash-based geopolymers at early ages designed by Taguchi method. Materials & Design, 2012, 37: 443–449

[27] Olivia M, Nikraz H. Properties of fly ash geopolymer concrete designed by Taguchi method. Materials & Design, 2012, 36: 191–198

[28] Lokuge W, Wilson A, Gunasekara C, Law D W, Setunge S. Design of fly ash geopolymer concrete mix proportions using Multivariate Adaptive Regression Spline model. Construction & Building Materials, 2018, 166: 472–481

[29] Gunasekara C, Atzarakis P, Lokuge W, Law D W, Setunge S. Novel analytical method for mix design and performance prediction of high calcium fly ash geopolymer concrete. Polymers, 2021, 13(6): 900

[30] Vu-Bac N, Lahmer T, Keitel H, Zhao J, Zhuang X, Rabczuk T. Stochastic predictions of bulk properties of amorphous polyethylene based on molecular dynamics simulations. Mechanics of Materials, 2014, 68: 70–84

[31] Vu-Bac N, Lahmer T, Zhang Y, Zhuang X, Rabczuk T. Stochastic predictions of interfacial characteristic of polymeric nanocomposites (PNCs). Composites. Part B, Engineering, 2014, 59: 80–95

[32] Vu-Bac N, Lahmer T, Zhuang X, Nguyen-Thoi T, Rabczuk T. A software framework for probabilistic sensitivity analysis for computationally expensive models. Advances in Engineering Software, 2016, 100: 19–31

[33] Vu-Bac N, Silani M, Lahmer T, Zhuang X, Rabczuk T. A unified framework for stochastic predictions of mechanical properties of polymeric nanocomposites. Computational Materials Science, 2015, 96: 520–535

[34] Hamdia K M, Silani M, Zhuang X, He P, Rabczuk T. Stochastic analysis of the fracture toughness of polymeric nanoparticle composites using polynomial chaos expansions. International Journal of Fracture, 2017, 206(2): 215–227

[35] Vu-Bac N, Rafiee R, Zhuang X, Lahmer T, Rabczuk T. Uncertainty quantification for multiscale modeling of polymer nanocomposites with correlated parameters. Composites. Part B, Engineering, 2015, 68: 446–464

[36] Box G E P, Wilson K B. On the experimental attainment of optimum conditions. Journal of the Royal Statistical Society. Series B. Methodological, 1951, 13(1): 1–38

[37] MyersR HMontgomeryD CAnderson-CookC M. Response Surface Methodology: Process and Product Optimization Using Designed Experiments. New Jersey: Wiley, 2016

[38] Habibi A, Ramezanianpour A M, Mahdikhani M, Bamshad O. RSM-based evaluation of mechanical and durability properties of recycled aggregate concrete containing GGBFS and silica fume. Construction & Building Materials, 2021, 270: 121431

[39] Koç . Kaymak-Ertekin. Response surface methodology and food processing applications. GIDA—Journal of Food, 2010, 35: 63–70

[40] Aydar A Y, Bagdatlioglu N, Köseoglu O. Effect of ultrasound on olive oil extraction and optimization of ultrasound-assisted extraction of extra virgin olive oil by response surface methodology (RSM). Grasas y Aceites, 2017, 68(2): 189

[41] AndresonM. Stat-Ease. v11. Adequate Precision. Sate Ease Inc. Available at the website of Stat-Ease

[42] Deb P S, Nath P, Sarker P K. The effects of ground granulated blast-furnace slag blending with fly ash and activator content on the workability and strength properties of geopolymer concrete cured at ambient temperature. Materials & Design, 2014, 62: 32–39

[43] Xie Z, Xi Y. Hardening mechanisms of an alkaline-activated class F fly ash. Cement and Concrete Research, 2001, 31(9): 1245–1249

[44] IS. 10262-2019: Concrete Mix Proportioning—Guidelines. New Delhi: Indian Stand, 2019

[45] IS. 3812: Specification for Pulverized fuel ash. Part-1: For Use as Pozzolana in Cement, Cement Mortar and Concrete. New Delhi: Indian Stand, 2013, 1–12

[46] IS:383: Specification for CoarseFineAggreagtes from Natural Sources for Concrete. New Delhi: Indian Stand, 2002

[47] Serag Faried A, Sofi W H, Taha A Z, El-Yamani M A, Tawfik T A. Mix design proposed for geopolymer concrete mixtures based on ground granulated blast furnace slag. Australian Journal of Civil Engineering, 2020, 18(2): 205–218

[48] Somna K, Jaturapitakkul C, Kajitvichyanukul P, Chindaprasirt P. NaOH-activated ground fly ash geopolymer cured at ambient temperature. Fuel, 2011, 90(6): 2118–2124

[49] Rabczuk T, Belytschko T. A three-dimensional large deformation meshfree method for arbitrary evolving cracks. Computer Methods in Applied Mechanics and Engineering, 2007, 196(29−30): 2777–2799

[50] Rabczuk T, Belytschko T. Cracking particles: A simplified meshfree method for arbitrary evolving cracks. International Journal for Numerical Methods in Engineering, 2004, 61(13): 2316–2343

[51] Albidah A, Alqarni A S, Abbas H, Almusallam T, Al-Salloum Y. Behavior of Metakaolin-Based geopolymer concrete at ambient and elevated temperatures. Construction & Building Materials, 2022, 317: 125910

[52] Noushini A, Aslani F, Castel A, Gilbert R I, Uy B, Foster S. Compressive stress−strain model for low-calcium fly ash-based geopolymer and heat-cured Portland cement concrete. Cement and Concrete Composites, 2016, 73: 136–146

[53] Xie J, Wang J, Rao R, Wang C, Fang C. Effects of combined usage of GGBS and fly ash on workability and mechanical properties of alkali activated geopolymer concrete with recycled aggregate. Composites Part B: Engineering, 2019, 164: 179–190

RIGHTS & PERMISSIONS

Higher Education Press