Fresh and hardened properties of high-strength concrete incorporating byproduct fine crushed aggregate as partial replacement of natural sand

Abstract

This paper presents the fresh and hardened properties of high-strength concrete comprising byproduct fine crushed aggregates (FCAs) sourced from the crushing of three different types of rocks, namely granophyre, basalt, and granite. The lowest void contents of the combined fine aggregates were observed when 40% to 60% of natural sand is replaced by the FCAs. By the replacement of 40% FCAs, the slump and bleeding of concrete with a water-to-cement ratio of 0.45 decreased by approximately 15% and 50%, respectively, owing to the relatively high fines content of the FCAs. The 28 d compressive strength of concrete was 50 MPa when 40% FCAs were used. The slight decrease in tensile strength from the FCAs is attributed to the flakiness of the particles. The correlations between the splitting tensile and compressive strengths of normal concrete provided in the AS 3600 and ACI 318 design standards are applicable for concrete using the FCAs as partial replacement of sand. The maximum 56 d drying shrinkage is 520 microstrains, which is significantly less than the recommended limit of 1000 microstrains by AS 3600 for concrete. Therefore, the use of these byproduct FCAs can be considered as a sustainable alternative option for the production of high-strength green concrete.

Keywords

fine crushed aggregates / quarry dust / compressive strength / splitting tensile strength / drying shrinkage

References

[1] Saha A K, Sarker P K. Sustainable use of ferronickel slag fine aggregate and fly ash in structural concrete: Mechanical properties and leaching study. Journal of Cleaner Production, 2017, 162: 438–448

[2] Roderick Y, McEwan D, Wheatley C, Alonso C. Comparative Study of Building Energy Performance Assessment between LEED, BREEAM and Green Star. West of Scotland Science Park, Glasgow, Kelvin Campus, IES, 2009

[3] Saha A K, Sarker P K, Golovanevskiy V. Thermal properties and residual strength after high temperature exposure of cement mortar using ferronickel slag aggregate. Construction & Building Materials, 2019, 199: 601–612

[4] Saha A, Sarker P. Mechanical properties of concrete using ferronickel slag as fine aggregate and supplementary cementitious material. Concrete in Australia, 2018, 44(4): 40–44

[5] Hudson B. Modification to the fine aggregate angularity test. In: Proceedings of the Seventh Annual International Centre for Aggregates Research Symposium. Austin, TX: Taylor & Francis, 1999

[6] Hudson B. Manufactured sand: Destroying some myths. Quarry, 1997, 125: 57–62

[7] AS 2758.1. Aggregates and Rock for Engineering Purposes-Concrete Aggregates. Sydney: Standards Australia, 2014

[8] Quiroga P N, Ahn N, Fowler D W. Concrete mixtures with high micro fines. ACI Materials Journal, 2006, 103(4): 258–264

[9] Marek C. Importance of fine aggregate shape and grading on properties of concrete. In: Proceedings of the Third Annual International Center for Aggregates Research. Austin, TX: University of Texas Library, 1995

[10] Çelik T, Marar K. Effects of crushed stone dust on some properties of concrete. Cement and Concrete Research, 1996, 26(7): 1121–1130

[11] Li B, Wang J, Zhou M. Effect of limestone fines content in manufactured sand on durability of low-and high-strength concretes. Construction & Building Materials, 2009, 23(8): 2846–2850

[12] Kroh T A. Use of manufactured sand as a replacement material for dredged sand in mortar. Dissertation for the Doctoral Degree. Cardiff: Cardiff University, 2010

[13] Hameed M S, Sekar A S S. Properties of green concrete containing quarry rock dust and marble sludge powder as fine aggregate. Journal of Engineering and Applied Science, 2009, 4(4): 83–89

[14] Ukpata J O, Ephraim M E. Flexural and tensile strength properties of concrete using lateritic sand and quarry dust as fine aggregate. Journal of Engineering and Applied Sciences (Asian Research Publishing Network), 2012, 7(3): 324–331

[15] Bahoria B V, Parbat D K, Nagarnaik P B, Waghe U P, Principal Y C C E. Sustainable utilization of Quarry dust and waste plastic fibers as a sand replacement in conventional concrete. In: International Conference on Sustainable Civil Infrastructure. Hyderabad, Telangana: ICSCI, 2014

[16] Franklin E K, Vikas S, Agarwal V C, Denis A F, Ehsan A. Stone dust as partial replacement of fine aggregate in concrete. Journal of Academia and Industrial Research, 2014, 3(3): 148–151

[17] Singh S K, Srivastava V, Agarwal V C, Kumar R, Mehta P K. An experimental investigation on stone dust as partial replacement of fine aggregate in concrete. Journal of Academia and Industrial Research, 2014, 3(5): 229–232

[18] Cheah C B, Lim J S, Ramli M B. The mechanical strength and durability properties of ternary blended cementitious composites containing granite quarry dust (GQD) as natural sand replacement. Construction & Building Materials, 2019, 197: 291–306

[19] Gunasekaran K, Praksah Chandar S, Annadurai R, Satyanarayanan K S. Augmentation of mechanical and bond strength of coconut shell concrete using quarry dust. European Journal of Environmental and Civil Engineering, 2017, 21(5): 629–640

[20] NZS 3111. Method for Determining Voids Content, Flow Time and Percentage over Size Material in Sand. Wellington: Standards New Zealand, 1989

[21] AS 1012.3.1. Methods of Testing Concrete Determination of Properties Related to the Consistency of Concrete—Slump Test. Sydney: Standard Australia, 2014

[22] AS 1012.2. Methods of Testing Concrete Method 2: Preparing Concrete Mixes in the Laboratory. Sydney: Standard Australia, 2014

[23] AS 1012.9. Methods of Testing Concrete—Determination of the Compressive Strength of Concrete Specimens. Sydney: Standard Australia, 1999

[24] AS 1012.10. Methods of Testing Concrete—Determination of Indirect Tensile Strength of Concrete Cylinders. Sydney: Standard Australia, 2000

[25] AS 1012.13. Methods of Testing Concrete—Determination of the Drying Shrinkage of Concrete for Samples Prepared in the Field or in the Laboratory. Sydney: Standard Australia, 2000

[26] Goldsworthy S. Manufactured sands in Portland cement concrete. In: Proceedings of the Third Annual International Center for Aggregates Research. Austin, TX: University of Texas Library, 2005

[27] Kwan A, Mora C. Effects of various, shape parameters on packing of aggregate particles. Magazine of Concrete Research, 2001, 53(2): 91–100

[28] Wills M H. How aggregate particle shape influences concrete mixing water requirement and strength. Journal of Materials, 1967, 2(4): 843–865

[29] Koehler E, Jeknavorian A, Chun B, Zhou P. Ensuring Concrete Performance for Various Aggregates. In: The 17th Annual ICAR Symposium. Austin, TX: Resurchify, 2009

[30] Cepuritis R, Jacobsen S, Pedersen B, Mørtsell E. Crushed sand in concrete—Effect of particle shape in different fractions and filler properties on rheology. Cement and Concrete Composites, 2016, 71: 26–41

[31] Krieger I M, Dougherty T J. A mechanism for non-Newtonian flow in suspensions of rigid spheres. Transactions of the Society of Rheology, 1959, 3(1): 137–152

[32] Neville A M. Properties of Concrete. 4th ed. New York: Wiley, 1995

[33] Goble C F, Cohen M D. Influence of aggregate surface area on mechanical properties of mortar. ACI Materials Journal, 1999, 96(6): 657–662

[34] Aitcin P, Mindess S. High-performance concrete: Science and applications. Capitulo, 1998, 10: 477–512

[35] Donza H, Cabrera O. The influence of kinds of fine aggregate on mechanical properties of high strength concrete. In: The Fourth International Symposium on Utilization of High-Strength/High-Performance Concrete. Paris: British Library Conference Proceedings, 1996

[36] Ukpata J O, Ephraim M E. Flexural and tensile strength properties of concrete using lateritic sand and quarry dust as fine aggregate. Journal of Engineering and Applied Sciences (Asian Research Publishing Network), 2012, 7(3): 324–331

[37] AS 3600. Concrete structures. Sydney: Standard Australia, 2009

[38] ACI 318. Building Code Requirements For Structural Concrete. Michigan: American concrete institute, 1999

[39] Tangchirapat W, Jaturapitakkul C. Strength, drying shrinkage, and water permeability of concrete incorporating ground palm oil fuel ash. Cement and Concrete Composites, 2010, 32(10): 767–774

RIGHTS & PERMISSIONS

Higher Education Press