Effect of nonionic side chain length of polycarboxylate-ether-based high-range water-reducing admixture on properties of cementitious systems

Abstract

Despite the large variations in the behaviors of water-reducing admixtures upon changes in their structures, most previous reports on the cement-admixture compatibility did not provide sufficient information on the structure of the admixture. Hence, the evaluation and generalization of the reports on the cement-admixture compatibility are challenging. In this study, three different polycarboxylate-ether-based water-reducing admixtures with the same free nonionic content, anionic/nonionic molar ratio, and main chain length and different side chain lengths were produced. The compatibility of these admixtures with a CEM I 42.5R-type cement was investigated. In addition, an analysis of variance was performed on the experiment results to evaluate the contributions of the admixture type, admixture/cement ratio, and elapsing time to the Marsh funnel flow time, mini-slump, slump flow, and compressive strength. The water-reducing admixtures having long or short side chains reduced the initial flow characteristics of the cementitious systems. However, the admixture having the shortest side chain was better with regard to flow retention. The side chain length of the admixture did not have significant effects on the compressive strength and water absorption capacity of the mortar mixtures and mini-slump performances of the cement paste mixtures. Regarding the behaviors of the admixtures in the cementitious systems, an optimal admixture side chain molecular weight is proposed.

Keywords

water-reducing admixture / side chain length / cement paste / fluidity / compressive strength

References

[1] Aïtcin P C, Flatt R J. Science and Technology of Concrete Admixtures. Cambridge: Woodhead Publishing Series in Civil and Structural Engineering, 2016

[2] Aïtcin P C. Admixtures: Essential components of modern concrete. Cement, Wapno, Beton, 2006, 5: 277–284

[3] Mehta P K, Monteiro P J M. Concrete: Microstructure, Properties, and Materials. 3rd ed. New York: McGraw-Hill, 2010

[4] Ramachandran V S. Concrete Admixtures Handbook. New Jersey: Noyes Publications, 1995

[5] Ran Q, Somasundaran P, Miao C, Liu J, Wu S, Shen J. Effect of the length of the side chains of comb-like copolymer dispersants on dispersion and rheological properties of concentrated cement suspensions. Journal of Colloid and Interface Science, 2009, 336(2): 624–633

[6] Felekoğlu B, Sarıkahya H. Effect of chemical structure of polycarboxylate-based superplasticizers on workability retention of self-compacting concrete. Construction & Building Materials, 2008, 22(9): 1972–1980

[7] Winnefeld F, Becker S, Pakusch J, Götz T. Effects of the molecular architecture of comb-shaped superplasticizers on their performance in cementitious systems. Cement and Concrete Composites, 2007, 29(4): 251–262

[8] Neville A M. Properties of Concrete. London: John Wiley & Sons Inc., 1997

[9] Hirata T. Cement Dispersant. JP Patent 84, 2022. 1981

[10] Lim G G, Hong S S, Kim D S, Lee B J, Rho J S. Slump loss control of cement paste by adding polycarboxylic type slump-releasing dispersant. Cement and Concrete Research, 1999, 29(2): 223–229

[11] Hanehara S, Yamada K. Rheology and early age properties of cement systems. Cement and Concrete Research, 2008, 38(2): 175–195

[12] Ran Q, Somasundaran P, Miao C, Liu J, Wu S, Shen J. Adsorption mechanism of comb polymer dispersants at the cement/water interface. Journal of Dispersion Science and Technology, 2010, 31(6): 790–798

[13] Janowska-Renkas E. The effect of superplasticizers’ chemical structure on their efficiency in cement pastes. Construction & Building Materials, 2013, 38: 1204–1210

[14] Peng X, Li X, Chen D, Ma D. Effect of side chains on the dispersing properties of polycarboxylate-type superplasticizers in cement systems. Magazine of Concrete Research, 2013, 65(7): 422–429

[15] Zhao Y, Nian F, Pang H, Huang J, Zhao H, Wang K, Liao B. Regulating the arm structure of star-shaped polycarboxylate superplasticizers as a means to enhance cement paste workability. Journal of Applied Polymer Science, 2018, 135(21): 46312

[16] Feng H, Pan L, Zheng Q, Li J, Xu N, Pang S. Effects of molecular structure of polycarboxylate superplasticizers on their dispersion and adsorption behavior in cement paste with two kinds of stone powder. Construction & Building Materials, 2018, 170: 182–192

[17] Bedard C, Mailvaganam N P. The use of chemical admixtures in concrete. Part I: Admixture-cement compatibility. Journal of Performance of Constructed Facilities, 2005, 19(4): 263–266

[18] Bonen D, Sarkar S L. The superplasticizer adsorption capacity of cement pastes, pore solution composition, and parameters affecting flow loss. Cement and Concrete Research, 1995, 25(7): 1423–1434

[19] Roberts L R. Dealing with cement admixture interactions. In: The 23rd Annual Convention of the Institute of Concrete Technology. Telford, 1995

[20] Jiang S, Kim B G, Aïtcin P C. Importance of adequate soluble alkali content to ensure cement/superplasticizer compatibility. Cement and Concrete Research, 1999, 29(1): 71–78

[21] Jolicoeur C, Nkinamubanzi P C, Simard M A, Piotte M. Progress in understanding the functional properties of superplasticizers in fresh concrete. In: The 4th CANMET/ACI International Conference on Superplasticizers and Other Chemical Admixtures. Montreal, 1994, 63–88

[22] Ramachandran V S. Concrete Admixtures Handbook. New Delhi: Standard Publishers, 2002

[23] Mardani-Aghabaglou A, Felekoğlu B, Ramyar K. Effect of cement C3A content on properties of cementitious systems containing high-range water-reducing admixture. Journal of Materials in Civil Engineering, 2017, 29(8): 04017066

[24] Mardani-Aghabaglou A, Son A E, Felekoğlu B, Ramyar K. Effect of cement fineness on properties of cementitious materials containing high range water reducing admixture. Journal of Green Building, 2017, 12(1): 142–167

[25] Mardani-Aghabaglou A, Boyacı O C, Hosseinnezhad H, Felekoğlu B, Ramyar K. Effect of gypsum type on properties of cementitious materials containing high range water reducing admixture. Cement and Concrete Composites, 2016, 68: 15–26

[26] Mardani-Aghabaglou A, Tuyan M, Yılmaz G, Arıöz Ö, Ramyar K. Effect of different types of superplasticizer on fresh, rheological and strength properties of self-consolidating concrete. Construction & Building Materials, 2013, 47: 1020–1025

[27] Altun M G, Özen S, Mardani-Aghabaglou A. Effect of side chain length change of polycarboxylate-ether based high range water reducing admixture on properties of self-compacting concrete. Construction & Building Materials, 2020, 246: 118427

[28] Aïtcin P C. High Performance Concrete. New York: E&FN SPON, 2004

[29] Wedding P A, Kantro D L. Influence of water-reducing admixtures on properties of cement paste—A miniature slump test. Cement, Concrete and Aggregates, 1980, 2(2): 95–102

[30] EFNARC. Specification and Guidelines for Self-Compacting Concrete. London, UK: European Federation for Specialist Construction Chemicals and Concrete Systems, 2002

[31] Mollah M Y A, Adams W J, Schennach R, Cocke D L. A review of cement-superplasticizer interactions and their models. Advances in Cement Research, 2000, 12(4): 153–161

[32] Ferrari L, Kaufmann J, Winnefeld F, Plank J. Multi-method approach to study influence of superplasticizers on cement suspensions. Cement and Concrete Research, 2011, 41(10): 1058–1066

[33] Qiu X, Peng X, Yi C, Deng Y. Effect of side chains and sulfonic groups on the performance of polycarboxylate-type superplasticizers in concentrated cement suspensions. Journal of Dispersion Science and Technology, 2011, 32(2): 203–212

[34] Sakai E, Yamada K, Ohta A. Molecular structure and dispersion-adsorption mechanisms of comb-type superplasticizers used in Japan. Journal of Advanced Concrete Technology, 2003, 1(1): 16–25

[35] Guo J, Guo Y. New Development of Chemical Admixtures for Concrete Its Application. Beijing: Beijing Institute of Technology Press, 2009, 172–177 (in Chinese)

[36] Wang X, Zhang J, Yang Y, Shu X, Ran Q. Effect of side chains in block polycarboxylate superplasticizers on early-age properties of cement paste. Journal of Thermal Analysis and Calorimetry, 2018, 133(3): 1439–1446

[37] Plank J, Sachsenhauser B. Impact of molecular structure on zeta potential and adsorbed conformation of α-allyl-w-methoxypolyethylene glycol-maleic anhydride superplasticizers. Journal of Advanced Concrete Technology, 2006, 4(2): 233–239

[38] Xiong W, Wang D, Zuo Y, Wang Z, Wu Z. Ready-mixed Concrete. Beton Chinese Edition, 2008

[39] Zingg A, Winnefeld F, Holzer L, Pakusch J, Becker S, Figi R, Gauckler L. Interaction of polycarboxylate-based superplasticizers with cements containing different C3A amounts. Cement and Concrete Composites, 2009, 31(3): 153–162

[40] Kong F, Pan L, Wang C, Zhang D, Xu N. Effects of polycarboxylate superplasticizers with different molecular structure on the hydration behavior of cement paste. Construction & Building Materials, 2016, 105: 545–553

[41] Yamada K, Takahashi T, Hanehara S, Matsuhisa M. Effects of the chemical structure on the properties of polycarboxylate-type superplasticizer. Cement and Concrete Research, 2000, 30(2): 197–207

[42] Li Y, Yang C, Zhang Y, Zheng J, Guo H, Lu M. Study on dispersion, adsorption and flow retaining behaviors of cement mortars with TPEG-type polyether kind polycarboxylate superplasticizers. Construction & Building Materials, 2014, 64: 324–332

[43] Anagnostopoulos C A. Effect of different superplasticisers on the physical and mechanical properties of cement grouts. Construction & Building Materials, 2014, 50: 162–168

[44] Jolicoeur C, Simard M A. Chemical admixture-cement interactions: Phenomenology and physico-chemical concepts. Cement and Concrete Composites, 1998, 20(2–3): 87–101

[45] Tadros M E, Skalny J A N, Kalyoncu R S. Early hydration of tricalcium silicate. Journal of the American Ceramic Society, 1976, 59(7‐8): 344–347

[46] Thomas N L, Birchall J D. The retarding action of sugars on cement hydration. Cement and Concrete Research, 1983, 13(6): 830–842

[47] Allen A J, Thomas J J. Analysis of C-S-H gel and cement paste by small-angle neutron scattering. Cement and Concrete Research, 2007, 37(3): 319–324

[48] Ouyang X, Jiang X, Qiu X, Yang D, Pang Y. Effect of molecular weight of sulfanilic acid-phenol-formaldehyde condensate on the properties of cementitious system. Cement and Concrete Research, 2009, 39(4): 283–288

[49] Qian S, Yao Y, Wang Z, Cui S, Liu X, Jiang H, Guo Z, Lai G, Xu Q, Guan J. Synthesis, characterization and working mechanism of a novel polycarboxylate superplasticizer for concrete possessing reduced viscosity. Construction & Building Materials, 2018, 169: 452–461

RIGHTS & PERMISSIONS

Higher Education Press