Preparation and characterization of ZrB 2 -SiC ultra-high temperature ceramics by microwave sintering

Abstract

ZrB₂-SiC ultra-high temperature ceramic composites reinforced by nano-SiC whiskers and SiC particles were prepared by microwave sintering at 1850°C. XRD and SEM techniques were used to characterize the sintered samples. It was found that microwave sintering can promote the densification of the composites at lower temperatures. The addition of SiC also improved the densification of ZrB₂-SiC composites and almost fully dense ZrB₂-SiC composites were obtained when the amount of SiC increased up to 30vol.%. Flexural strength and fracture toughness of the ZrB₂-SiC composites were also enhanced; the maximum strength and toughness reached 625 MPa and 7.18 MPa·m^1/2, respectively.

Keywords

ultra-high temperature ceramics (UHTCs) / zirconium diboride / silicon carbide / mechanical properties / microwave sintering