Adhesion behavior of plasma sprayed thermal barrier coatings on Al-6061 and cast iron substrates

Abstract

In this work an investigation was carried out on adhesion strength and micro-hardness of plasma sprayed coatings on Al-6061 and cast iron substrate materials. For the adhesion test, ASTM C633, and for the micro hardness, ASTM E384 standards were used. From the results obtained it was found that the main failure locations were in the bond coat-substrate interface, which is considered as adhesion strength. The various parameters affecting adhesion strength are also discussed.

Keywords

adhesion strength / micro-hardness plasma spraying / thermal barrier coating

References

[1] AWS. Thermal Spraying: Practice, Theory and Application. Miami, FL: American Welding Society, 1985

[2] Sobolev V V, Guilemany J M, Nutting J, . Development of substrate-coating adhesion in thermal spraying. International Materials Reviews, 1997, 42(3): 117-136

[3] Houben J M. Relationship between the adhesion of plasma sprayed coatings to the process parameters size, velocity and heat content of the spray particles. Dissertation for the Doctoral Degree. The Netherlands: Eindhoven University of Technology Eindhoven, 1988

[4] Harmsworth P D, Stevens R. Microstructure of zirconia-yttria plasma-sprayed thermal barrier coatings. Journal of Materials Science, 1992, 27: 616-624

[5] Bartuli C, Bertamini L, Matera S, . Investigation of the formation of an amorphous film at the ZrO₂-Y₂O₃/NiCoCrAlY interface of thermal barrier coatings produced by plasma spraying. Materials Science and Engineering: A, 1995, 199: 229-237

[6] Bahbou M F, Nylén P, Wigren J. Effect of grit blasting and spraying angle on the adhesion strength of a plasma-sprayed coating. Journal of Thermal Spray Technology, 2004, 13(4): 508-514

[7] Berndt C C. Cracking progresses in thermally sprayed ceramic coatings. Materials Science Forum, 1988, 34-36: 457-461

[8] Era H, Otsubo F, Uchida T, . A modified shear test for adhesion evaluation of thermal sprayed coating. Materials Science and Engineering: A, 1998, 251(1-2): 166-172

[9] Zhu Y L, Ma S N, Xu B S. Finite-element evaluation and improvement of a test procedure for coating shear bond strength determination. Journal of Thermal Spray Technology, 1999, 8(2): 328-332

[10] Siegman S, Dvorak M, Grutzner H, . In: Lugscheider E, ed. Thermal Spray Connects: Explore its Surface Potential, Proceedings of the International Thermal Spray Conference ITSC, Basel, Switzerland, ASM International/DVS, Dusseldorf, Germany, 2005, 823

[11] Hadad M, Marot G, Lesage J, . In: Lugscheider E, ed. Thermal Spray Connects: Explore its Surface Potential, Proceedings of the International Thermal Spray Conference ITSC, Basel, Switzerland, ASM International/DVS, Dusseldorf, Germany, 2005, 759

[12] Trevisan R E, Fals H C, Lima C R C. Critical evaluation of adhesion tests in plasma sprayed metal-ceramic coatings. CIT Information Tecnologica (Chile), 2000, 11(4): 103–112

[13] ASTM. Standard test method for adhesion and cohesion strength of thermal spray coating. ASTM standard C-633-01. West Conshocken, PA, USA: ASTM International, 2001

[14] Janos B Z, Lugscheider E, Remer P. Effect of thermal aging on the erosion resistance of air plasma sprayed zirconia thermal barrier coatings. Surface and Coatings Technology, 1999, 113: 278-285

[15] Haynes J A, Ferber M K, Porter W D, . Mechanical properties and fracture behavior of interfacial alumina scales on plasma-sprayed thermal barrier coatings. Materials at High Temperatures, 1999, 16(2): 49-69

[16] Lima C R C, Guilemany J M. Adhesion improvements of thermal barrier coatings with HVOF thermally sprayed bond coats. Surface and Coatings Technology, 2007, 201(8): 4694-4701

[17] Limarga A M, Widjaja S, Yip T H. Mechanical properties and oxidation resistance of plasma-sprayed multilayered Al₂O₃/ZrO₂ thermal barrier coatings. Surface and Coatings Technology, 2005, 197: 93-102

[18] ASTM. Standard test method for micro indentation hardness of materials. ASTM E384. West Conshocken, PA, USA: ASTM International, 2005

RIGHTS & PERMISSIONS

Higher Education Press and Springer-Verlag Berlin Heidelberg