Synthesis, characterization and annealing of mechanically alloyed nanostructured FeAl powder

Abstract

Elemental powders of Fe and Al were mechanically alloyed using a high energy rate ball mill. A nanostructure disordered Fe(Al) solid solution was formed at an early stage. After 28 h of milling, it was found that the Fe(Al) solid solution was transformed into an ordered FeAl phase. During the entire ball milling process, the elemental phase co-existed with the alloyed phase. Ball milling was performed under toluene to minimise atmospheric contamination. Ball milled powders were subsequently annealed to induce more ordering. Phase transformation and structural changes during mechanical alloying (MEA) and subsequent annealing were investigated by X-ray diffraction (XRD). Scanning electron microscope (SEM) was employed to examine the morphology of the powders and to measure the powder particle size. Energy dispersive spectroscopy (EDS) was utilised to examine the composition of mechanically alloyed powder particles. XRD and EDS were also employed to examine the atmospheric and milling media contamination. Phase transformation at elevated temperatures was examined by differential scanning calorimeter (DSC). The crystallite size obtained after 28 h of milling time was around 18 nm. Ordering was characterised by small reduction in crystallite size while large reduction was observed during disordering. Micro hardness was influenced by Crystallite size and structural transformation.

Keywords

nanostructured powder / mechanical alloying / FeAl / disorder / order

References

[1] George E P, Baker I. Intermetallics: iron aluminides. In:<BibTranslator> Buschow K H J, Cahn R W, Flemings M C</BibTranslator>, , eds. The Encyclopaedia of Materials Science. Amsterdam: Elsevier, 2001, 4201–4205

[2] Tortorelli P F, DeVan J H. Behavior of iron aluminides in oxidizing and oxidizing/sulfidizing environments. Materials Science and Engineering: A, 1992, 153: 573–577

[3] Deevi S C, Sikka V K, Liu C T. Processing, properties, and applications of nickel and iron aluminides. Progress in Materials Science, 1997, 42: 177–192

[4] Deevi S C, Sikka V K. Nickel and iron aluminides: an overview on properties, processing, and applications. Intermetallics, 1996, 4: 357–375

[5] Koch C C. The synthesis of non-equilibrium structures by ball-milling. Materials Science Forum, 1992, 88-90: 243–262

[6] Suryanarayana C. Mechanical alloying and milling. Progress in Materials Science, 2001, 46: 1–184

[7] Gleiter H. Materials with ultrafine microstructures: Retrospectives and perspectives. Nanostructured Materials, 1992, 1: 1–19

[8] Suryanarayana C, Froes F H. The structure and mechanical properties of metallic nanocrystals. Metallurgical Transactions A, 1992, 23: 1071–1081

[9] Nieman G W, Weertman J R, Siegel R W. Mechanical behavior of nanocrystalline metals. Nanostructured Materials, 1992, 1: 185–190

[10] Siegel R W, Fougere G E. Mechanical properties of nanophase metals. Nanostructured Materials, 1995, 6: 205–216

[11] Karch J, Birringer R, Gleiter H. Ceramics ductile at low temperature. Nature, 1987, 330: 556–558

[12] McFadden S X, Mishra R S, Valiev R Z, . Low-temperature superplasticity in nanostructured nickel and metal alloys. Nature, 1999, 398: 684–686

[13] Birringer R. Nanocrystalline materials. Materials Science and Engineering: A, 1989, 117: 33–43

[14] Krasnowski M, Grabias A, Kulik T. Phase transformations during mechanical alloying of Fe-50%Al and subsequent heating of the milling product. Journal of Alloys and Compounds, 2006, 424: 119–127

[15] Amils X, Nogues J, Surinach S, . Structural, mechanical and magnetic properties of nanostructured FeAl alloys during disordering and thermal recovery. Nanostructured Materials, 1999, 11: 689–695

[16] Sebastian V, Lakshmi N, Venugopal K. Oxidation kinetics of the pack siliconized TiAl-based alloy and microstructure evolution of the coating. Intermetallics, 2007, 15: 1–7

[17] Zeng Q, Baker I. Magnetic properties and thermal ordering of mechanically alloyed Fe-40at%Al. Intermetallics, 2006, 14: 396–405

[18] Morris-Munoz M A, Dodge A, Morris D G. Structure, strength and toughness of nanocrystalline FeAl. Nanostructured Materials, 1999, 11: 873–885

[19] Shi H W, Guo D B, Ouyang Y F. Structural evolution of mechanically alloy nanocrystalline FeAl intermetallics. Journal of Alloys and Compounds, 2007

[20] Varin R A, Czujko T, Bystrzycki J, . Cold-work induced phenomena in B2 FeAl intermetallics. Materials Science and Engineering: A, 2002, 329-331: 213–221

Acknowledgements

The authors would like to acknowledge Dr. Surappa and Shri Krishnamurthy from the Materials Department at the Indian Institute of Science (IISc), Bangalore for providing the XRD facility.

RIGHTS & PERMISSIONS

2014 Higher Education Press and Springer-Verlag Berlin Heidelberg