Preparation of salt-activated cementitious materials from high-temperature activated iron tailings and micromechanism

Abstract

In this study, iron tailings were subjected to high-temperature activation at 600, 800, and 1 000 ℃, and then compounded with slag, cement, and sodium sulfate to prepare a salt‑activated cementitious material. The activation mechanism of the high-temperature activated iron tailings and their mechanism of action in the sodium sulfate-activated cementitious system were revealed by means of X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), and maximum intensity projection (MIP) characterization techniques. The results show that activation at 800 ℃ can transform kaolinite, chlorite, and nontronite in iron tailings into highly active amorphous substances, increasing the specific surface area and enhancing the pozzolanic activity. After incorporation of the activated iron tailings, the fluidity of the material decreases with increasing activation temperature, while the setting time first shortens and then slightly prolongs. Compared with the unactivated system, the material incorporating 800 ℃-activated iron tailings exhibits increases in compressive strength at 3, 7, and 28 d of 17.6%, 23.6%, and 21.9%, respectively, and increases in flexural strength of 15.0%, 15.6%, and 12.4%, respectively. This system has a porosity of 11.94% and a water absorption of 3.37%, with low proportions of capillary and large pores and a dense microstructure. Further microscopic analysis reveals that Na₂SO₄ reacts with Ca(OH)₂ to form NaOH, increasing the alkalinity of the paste and promoting the dissolution of active components from the iron tailings and slag. These dissolved components participate in the reaction, continuously generating ettringite and C-(A)-S–H gels. As the hydration age increases, the hydration products continuously accumulate, making the material structure gradually denser, thereby effectively enhancing the strength.

Keywords

Salt-activated cementitious materials / Iron tailings / High temperature activation / Mechanical properties / Microstructure

References

[1] Li Y, Li S, Zhao X, Pan X, Guo P. Separation and purification of high-purity quartz from high-silicon iron ore tailing: An innovative strategy for comprehensive utilization of tailings resources. Process Safety and Environmental Protection, 2023, 169: 142-148.

[2] Han F, Li L, Song S, Liu J. Early-age hydration characteristics of composite binder containing iron tailing powder. Powder Technology, 2017, 315: 322-331.

[3] Liu K, Wang S, Quan X, Jing W, Xu J, Zhao N, Liu B, Ying H. Industrial byproduct iron ore tailings as ecofriendly materials in the utilization of cementitious composites. Construction and Building Materials, 2023, 372. 130813

[4] Du Z, Ge L, Ng AHM, Zhu Q, Horgan FG, Zhang Q. Risk assessment for tailings dams in Brumadinho of Brazil using InSAR time series approach. Science of the Total Environment, 2020, 717. 137125

[5] Xu J, Chen P. Synergistic effect of iron tailings, steel slag and red mud cementitious materials on mechanical and microstructure properties. Journal of Building Engineering, 2024, 95. 110131

[6] Yang G, Liu F, Xie Q, Yang M, Li Y, Kumar ER, Sun J. Exploration of iron ore tailings with high volume in sustainable cement and ecofriendly cementitious material. Developments in the Built Environment, 2024, 19. 100482

[7] Jahami A. Ultra-low-carbon concrete using construction and demolition waste microfillers. Materials Letters, 2026.

[8] Vairagade VS, Das A, Bhandari PS. Optimization of concrete strength incorporating limestone powder and carbon nanotubes for enhancing structural performance. Steps For Civil, Constructions and Environmental Engineering, 2025, 341229.

[9] Jahami A, Chamseddine F, Salhab AA, Ibrahim M, Zaiter B, Isleem HF. Enhancing concrete properties with steel waste: A comprehensive review of GGBS, SS, and steel waste utilization. Innovative Infrastructure Solutions, 2024, 910391.

[10] Jahami A, Dayaa L, Assaad JJ, Baalbaki O, Khatib J. Flexural strength of structural beams cast using combined normal-weight and lightweight concrete mixtures. Buildings, 2024, 14123787

[11] Jahami, A., Mouzanar, H., Mahfouz, S., Khatib, J., & Sonebi, M. (2023). Effect of graphene as additive on the mechanical properties of concrete. NanoWorld Journal, 9(Special Issue 2), S87-S92. https://doi.org/10.17756/nwj.2023-s2-015.

[12] Huang K, Jiang Y, Cai G, Chen R, Li Z, Huang K, Liu L, Huang X. Study on mix ratio optimization, microstructure evolution, and economic benefits of iron tailings-fly ash-limestone powder ternary geopolymer. Journal of Cleaner Production, 2026, 542. 147514

[13] Zeng J, Zhang K, Sun W, Zeng Y, Zou Z. Mechanics and microstructure analysis of geopolymer utilizing ilmenite tailing and metakaolin powder as alkali-activated materials. Case Studies in Construction Materials, 2024, 21. e03567

[14] Xu H, Yin H, Lu S, Pei G. Effect of freeze-thaw cycles on bending properties and microstructure of slag-fly ash based geopolymer cemented iron tailings sand. Case Studies in Construction Materials, 2025, 23. e04962

[15] Habert G, Ouellet-Plamondon C. Recent update on the environmental impact of geopolymers. RILEM Technical Letters, 2016, 1: 17.

[16] Sandanayake M, Gunasekara C, Law D, Zhang G, Setunge S. Greenhouse gas emissions of different fly ash based geopolymer concretes in building construction. Journal of Cleaner Production, 2018, 204: 399-408.

[17] Adesina A, Kaze CR. Physico-mechanical and microstructural properties of sodium sulfate activated materials: A review. Construction and Building Materials, 2021, 295. 123668

[18] Rashad AM, Bai Y, Basheer PM, Milestone NB, Collier NC. Hydration and properties of sodium sulfate activated slag. Cement and Concrete Composites, 2013, 37: 20-29.

[19] Velandia DF, Lynsdale CJ, Provis JL, Ramirez F. Effect of mix design inputs, curing and compressive strength on the durability of Na₂SO₄-activated high volume fly ash concretes. Cement and Concrete Composites, 2018, 91: 11-20.

[20] Chen, K. Y., Lyu, G. H., Wang, Z. F., Wang, Y. Q., & Xia, J. (2025). Development of a weakly alkaline alkali-activated mortar: use of sodium carbonate/sodium sulfate–magnesia for activating fly ash–slag mixture. Magazine of Concrete Research, 77(13-14), 780-791. https://doi.org/10.1680/jmacr.25.00020.

[21] Tang Z, Meng X, Han Y, Chen M, Gao P, Zhang Y. Hydration and properties of hydrogen-based mineral phase transformation iron ore tailings as supplementary cementitious material. Journal of Environmental Management, 2024, 356. 120594

[22] Saedi A, Jamshidi-Zanjani A, Darban AK. A review on different methods of activating tailings to improve their cementitious property as cemented paste and reusability. Journal of Environmental Management, 2020, 270. 110881

[23] Liu J, Ge X, Liu P, Song G, Hu Z. Experimental study on the preparation of cementitious materials from iron ore tailings by activation. Construction and Building Materials, 2023, 385. 131409

[24] Hernández-Ramos SM, Trejo-Arroyo DL, Cholico-González DF, Rodríguez-Torres GM, Zárate-Medina J, Vega-Azamar RE, León-Patiño CA, Ortíz-Lara N. Characterization and effect of mechanical and thermal activation in mining tailings for use as supplementary cementitious material. Case Studies in Construction Materials, 2024, 20. e02770

[25] Lee JW, Thomas LC, Schmidt SJ. Effects of heating conditions on the glass transition parameters of amorphous sucrose produced by melt-quenching. Journal of Agricultural and Food Chemistry, 2011, 59733113319.

[26] Duan S, Li L, Wang Z, Wang G, Zhou Z, Zhang J. Sodium sulfate promotes alkali-activated steel slag and granulated blast furnace slag: Engineering performance and micro-mechanism. Construction and Building Materials, 2025, 494. 143484

[27] Elimbi A, Tchakoute HK, Njopwouo D. Effects of calcination temperature of kaolinite clays on the properties of geopolymer cements. Construction and Building Materials, 2011, 25628052812.

[28] Huo W, Zhu Z, Sun H, Yang L, Zhang C. Estimating the relationships between initial constituent molar ratios and physical–mechanical properties of RCFP-GBFS based geopolymers. Construction and Building Materials, 2023, 406. 133409

[29] Wang H, Gu X, Xu X, Liu J, Zhu Z, Wang S. The effects of iron tailings on steel slag-based cementitious systems: Strength, hydration products, and volume stability. Journal of Building Engineering, 2024, 91. 109702

[30] Chen B, Pang L, Zhou Z, Chang Q, Fu P. Study on the activation mechanism and hydration properties of gold tailings activated by mechanical-chemical-thermal coupling. Journal of Building Engineering, 2022, 48. 104014

[31] Yao G, Liu Q, Wang J, Wu P, Lyu X. Effect of mechanical grinding on pozzolanic activity and hydration properties of siliceous gold ore tailings. Journal of Cleaner Production, 2019, 217: 12-21.

[32] Wan Q, Rao F, Song S. Reexamining calcination of kaolinite for the synthesis of metakaolin geopolymers-roles of dehydroxylation and recrystallization. Journal of Non-Crystalline Solids, 2017, 460: 74-80.

[33] Lin H, Yin Z, Li S. Optimization of cementitious material with thermal-activated lead–zinc tailings based on response surface methodology. Materials, 2024, 17122926

[34] Zhou L, Gou M, Hou W, Zhao M, Zhao J, Shen Z. Effect of thermal activation and particle size on cementitious activity of bauxite tailings. Environmental Science and Pollution Research, 2022, 29527896078972.

[35] Qiu X, Yao J, He Z, Li Y, Hu L, Zhang R, Chen J. Research on the preparation and performance characteristics of activated copper tailings grouting material based on solid waste synergy. Journal of Cleaner Production, 2025, 514. 145739

[36] Omur T, Akgün AE, Özkan AB, Kabay N. Valorization of raw and treated iron ore tailings in cement based materials: Insights on physicomechanical, microstructural, and environmental properties. Construction and Building Materials, 2026, 532. 146722

[37] Chen QS, Zhang QL, Fourie A, Chen X, Qi CC. Experimental investigation on the strength characteristics of cement paste backfill in a similar stope model and its mechanism. Construction and Building Materials, 2017, 154: 34-43.

[38] Feng Y, Li F, Qi W, Ren Q, Qi W, Duan G, Zheng K, Han Y, Pang H. Mechanical properties and microstructure of iron tailings cemented paste backfills using carbide slag-activated ground granulated blast-furnace slag as alternative binder. Minerals, 2022, 12121549

[39] Chen Q, Tao Y, Feng Y, Zhang Q, Liu Y. Utilization of modified copper slag activated by Na2SO4 and CaO for unclassified lead/zinc mine tailings based cemented paste backfill. Journal of Environmental Management, 2021, 290. 112608

[40] Zhang W, Hao X, Wei C, Zeng Q, Ma S, Liu X, Zhang Z, Webeck E. Synergistic enhancement of converter steelmaking slag, blast furnace slag, Bayer red mud in cementitious materials: Strength, phase composition, and microstructure. Journal of Building Engineering, 2022, 60. 105177

[41] Budak M, Maravelaki-Kalaitzaki P, Kallithrakas-Kontos N. Chemical characterization of Cretan clays for the design of restoration mortars. Microchimica Acta, 2008, 1623325331.

[42] Vargas F, Lopez M. Development of a new supplementary cementitious material from the activation of copper tailings: Mechanical performance and analysis of factors. Journal of Cleaner Production, 2018, 182: 427-436.

[43] Scholtzová E, Kucková L, Kožíšek J, Tunega D. Structural and spectroscopic characterization of ettringite mineral–combined DFT and experimental study. Journal of Molecular Structure, 2015, 1100: 215-224.

[44] Wu M, Zhang Y, Jia Y, She W, Liu G, Yang Z, Zhang Y, Zhang W, Sun W. Effects of sodium sulfate on the hydration and properties of lime-based low carbon cementitious materials. Journal of Cleaner Production, 2019, 220: 677-687.

[45] Li N, Farzadnia N, Shi C. Microstructural changes in alkali-activated slag mortars induced by accelerated carbonation. Cement and Concrete Research, 2017, 100: 214-226.

[46] Yusuf MO. Bond characterization in cementitious material binders using Fourier-transform infrared spectroscopy. Applied Sciences, 2023, 1353353

[47] Karim MR, Chowdhury FI, Zabed H, Saidur MR. Effect of elevated temperatures on compressive strength and microstructure of cement paste containing palm oil clinker powder. Construction and Building Materials, 2018, 183: 376-383.

[48] Wang S, Pan H, Xiao C, Zhao Q, Wang J. Preparation and mix proportion optimization of red mud-fly ash-based cementitious material synergistic activated by carbide slag and MSWIFA. Construction and Building Materials, 2024, 415. 135032

[49] Wang M, Xu J, Zhang X, Tan L, Mei Y. Mechanical performance optimization and microstructural mechanism study of alkali-activated steel slag–slag cementitious materials. Buildings, 2024, 1451204

[50] Wu P, Wei C, Liu X, Zhang Z, Xue Y, Liu X. Impact of hematite in red mud on hydration characteristics and environmental performance of cementitious materials. Cement and Concrete Composites, 2025, 160. 106035

[51] Liu W, Du R, Zhao Z, Zhang R, Wan Y, Li H. Development of lead smelting slag-based ecological mine backfill material: Performance control and heavy metals solidification. Construction and Building Materials, 2023, 367. 130310

[52] Lv Q, Jiang L, Ma B, Zhao B, Huo Z. A study on the effect of the salt content on the solidification of sulfate saline soil solidified with an alkali-activated geopolymer. Construction and Building Materials, 2018, 176: 68-74.

Funding

Hainan Province “Nanhai New Star” project funding(202309008)

Natural Science Foundation of Sichuan Province, China(2025YFHZ0321)

National Natural Science Foundation of China(52261045)

Innovative Research Projects for Postgraduate Students in Hainan Province(Qhys2024-59)

Rights & permissions

The Author(s)