Study on shear transfer performance of modeled natural aggregate concrete

Abstract

This study investigates the shear failure behavior of modeled natural aggregate concrete (MNAC) through direct shear tests, with particle size (17, 23, and 30 mm) and aggregate quantity (1, 2, and 3) as key variables. In the course of testing, three distinct shear failure modes were identified: aggregate fracture (Type I), aggregate external envelope fracture (Type II), and interfacial transition zone (ITZ) failure (Type III). Specifically, Type I failure mode occurred only in specimens with a smaller quantity and particle size (MNA17-1 and MNA23-1), whereas the other specimens exhibited Type II, Type III, or a combination of Type II and Type III failure modes. Notably, both larger particle size and aggregate quantity enhanced shear capacity. For example, in single-aggregate specimens, increasing the particle size from 17 to 30 mm raised the pre-cracking peak strength (P₁) and post-cracking secondary peak strength (P₂) by 42.3% and 43.2%, respectively. Similarly, for specimens with a particle size of 17 mm, raising the quantity from 1 to 3 increased P₁ by 35.9% and P₂ by 93.2%. Collectively, these results clarify the role of mesoscale aggregate characteristics in governing macro-scale shear mechanisms, providing new insights into the shear resistance of concrete.

Keywords

Modeled natural aggregate concrete / Shear transfer performance / Particle size / Aggregate quantity / Failure mode

References

[1] Park R, Paulay TReinforced concrete structures, 1975Wiley

[2] Zhang, C., Li, D., Ma, J., Zhu, Q., Luo, P., Chen, Y., & Han, M. (2023). Dynamic shear fracture behavior of rocks: Insights from three-dimensional digital image correlation technique. Engineering Fracture Mechanics,277. https://doi.org/10.1016/j.engfracmech.2022.109010

[3] Mitchell, D., & Collins, M. P. (1974). Diagonal compression field theory—A rational model for structural concrete in pure torsion. ACI Journal Proceedings, 71(8). https://doi.org/10.14359/710310.14359/7103

[4] Liang, S., Shen, Y., Gao, X., Cai, Y., & Fei, Z. (2023). Symbolic machine learning improved MCFT model for punching shear resistance of FRP-reinforced concrete slabs. Journal of Building Engineering,69. https://doi.org/10.1016/j.jobe.2023.106257

[5] Muttoni A, Schwartz JBehavior of beams and punching in slabs without shear reinforcement. Journal of Structural Engineering, 2003, 129(3): 258-266.

[6] Xue, X., Xiu, B., Cheng, N., & Han, X. (2024). A shear strength prediction theory for box girder strengthened by external vertical prestressing reinforcements. KSCE Journal of Civil Engineering,28(10), 4408–4420. https://doi.org/10.1007/s12205-024-0646-y

[7] Kani, G. N. J. (1964). The riddle of shear failure and its solution. ACI Journal Proceedings, 61(4). https://doi.org/10.14359/7791

[8] Awad MJ, Rasheed MMShear behaviour in reinforced concrete beams: Mechanisms, failure modes, and predictive models: A review. Al Rafidain Journal of Engineering Sciences, 2024, 2(2): 210-227.

[9] American Concrete InstituteBuilding code requirements for structural concrete and commentary, 2019American Concrete Institute318-19

[10] Hua R, Wu Y, Jiang J, Xu WMesomechanical insights into ITZ volume fraction around realistic-morphological aggregates and elastic properties of concrete. Construction and Building Materials, 2025, 489(7142428

[11] Zheng JJ, Li CQ, Zhou XZThickness of interfacial transition zone and cement content profiles around aggregates. Magazine of Concrete Research, 2005, 57(7): 397-406.

[12] Meng Z, Liu Q, et al.Mechanical–transport–chemical modeling of electrochemical repair methods for corrosion-induced cracking in marine concrete. Computer-Aided Civil and Infrastructure Engineering, 2022, 37(14): 1854-1874.

[13] Trindade JC, Garcia SLG, Lacerda TN, Resende TLAnalysis of the shear behavior of reinforced recycled aggregate concrete beams based on shear transfer mechanisms. Engineering Structures, 2023, 293116616

[14] Bažant ZP, Gambarova PRough cracks in reinforced concrete. Journal of the Structural Division, 1980, 106(ST4): 819-842.

[15] Tassios TP, Vintzeleou ENConcrete-to-concrete friction. Journal of Structural Engineering, 1987, 113(4): 832-849.

[16] Walraven, J. C. (1980). Aggregate interlock: A theoretical and experimental analysis. PhD Thesis, Delft University of Technology.

[17] Li, B., & Maekawa, K. (1987). Contact density model for cracks in concrete. Proceedings of the IABSE Colloquium, 51–62.

[18] Li B, Maekawa K, Okamura HContact density model for stress transfer across cracks in concrete. Journal of the Faculty of Engineering, University of Tokyo, 1989, 40: 49-66

[19] Guidotti, R. (2010). Poinçonnement des planchers-dalles avec colonnes superposées fortement sollicitées. PhD Thesis, École Polytechnique Fédérale de Lausanne. https://doi.org/10.5075/epfl-thesis-4812

[20] Lilliu G, van Mier JGM3D lattice-type fracture model for concrete. Engineering Fracture Mechanics, 2003, 70(7–8): 927-941.

[21] Grassl P, Jirásek MMeso-scale approach to modelling the fracture process zone of concrete subjected to uniaxial tension. International Journal of Solids and Structures, 2010, 47(7–8): 957-968.

[22] Liu, Q., Cheng, A., Sun, C., Chen, K., Wang, Y., & Li, W. (2024). Effects of aggregate type and orientation on stress concentration and crack propagation of modeled concrete subjected to shear force. Journal of Building Engineering,95. https://doi.org/10.1016/j.jobe.2024.110340

[23] Zhang H, Li W, Gao Y, Hasan MA, Zhang X, Wang KNano- and microscopic investigation on the strengthening mechanism of ITZs using waste glass powder in modeled aggregate concrete. Journal of Materials in Civil Engineering, 2024, 36(4): 04024007.

[24] Zhou G, Xu Z3D mesoscale investigation on the compressive fracture of concrete with different aggregate shapes and interface transition zones. Construction and Building Materials, 2023, 393132111

[25] Zaitsev YB, Wittmann FHSimulation of crack propagation and failure of concrete. Matériaux et Constructions, 1981, 145):357-365.

[26] Shah S, Winter GInelastic behavior and fracture of concrete. ACI Journal Proceedings, 1966, 63: 925-930

[27] Choi S, Shah SPPropagation of microcracks in concrete studied with subregion scanning computer vision. ACI Materials Journal, 1999, 96(2): 255-260

[28] Wang S, Peng S, Sun C, Singh A, Cheng Z, Tian YCrack propagation and failure mechanism of modeled recycled concrete under shear stress. Sustainability, 2022, 14(95552

[29] Li H, Li X, Fu J, Gao Z, Chen P, Zhang ZResearch on acoustic emission multi-parameter characteristics in the failure process of imitation steel fiber reinforced concrete. Physics of Fluids, 2023, 3510107109

[30] Pan C, Zheng Z, Yang YCrack propagation phenomenon in gangue concrete using the digital image correlation method. Advances in Materials Science and Engineering, 2024, 2024: 1-14.

[31] Singh A, Anand K, Liu Q, Tam VWY, Goyal S, Reddy MSEnhancing interlayer bonding in 3-dimensional printed concrete using bacteria-based biomineralization. Cement and Concrete Composites, 2025, 164106258

[32] Sun, C., Zhao, H., Wu, X., Liu, Q., & Pan, F. (2025). Study on the shear failure characteristics of RAC push-off specimens with UHPC shear keys. Low-carbon Materials and Green Construction, 3(15). https://doi.org/10.1007/s44242-025-00075-9

[33] Xiao JZRecycled aggregate concrete structures, 2018Springer

[34] Taheri-Shakib J, Al-Mayah AApplications of X-ray computed tomography to characterize corrosion-induced cracking evolution in reinforced concrete: A review. Journal of Building Engineering, 2024, 90109420

[35] Li J, Wang T, Hong J, et al.Axial compressive performance of low-carbon high-strength recycled aggregate concrete. Low-Carbon Materials and Green Construction, 2024, 225.

[36] Wang Y, Yang S, Wu W, et al.Optimized design of ultra-high performance concrete matrix based on multifactor interaction. Low-Carbon Materials and Green Construction, 2025, 311.

[37] Mi R, Wang Y, Yu T, et al.Effects of carbon-sequestering coral aggregate on pore structures and compressive strength of concrete. Low-Carbon Materials and Green Construction, 2023, 121.

[38] Duan Z, Singh A, Xiao J, Hou SCombined use of recycled powder and recycled coarse aggregate derived from construction and demolition waste in self-compacting concrete. Construction and Building Materials, 2020, 254119323

[39] Tambusay A, Suryanto B, Suprobo PDigital image correlation for cement-based materials and structural concrete testing. Civil Engineering Dimension, 2020, 221): 6-12.

[40] Gehri N, Mata-Falcón J, Kaufmann WAutomated crack detection and measurement based on digital image correlation. Construction and Building Materials, 2020, 256119383

[41] Skarżyński Ł, Kozicki J, Tejchman JApplication of DIC technique to concrete—study on objectivity of measured surface displacements. Experimental Mechanics, 2013, 53(9): 1545-1559.

[42] Liu Q, Cheng X, Sun C, Jin C, Tam VWYImpact of carbonization and aggregate properties on modeled recycled concrete: Mechanical characteristics, stress concentration and damage evolution. Construction and Building Materials, 2025, 467140327

Funding

National Natural Science Foundation of China(52478187)

Rights & permissions

The Author(s)