Multi-scale Simulation on Bonding Mechanism of Solid-Liquid Cast-Rolling of Cu/Al Cladding Strip based on FEM and MD

Abstract

To explore the complex thermal-mechanical-chemical behavior in the solid-liquid cast-roll bonding (SLCRB) of Cu/Al cladding strip, numerical simulations were conducted from both macro and micro scales. In macro-scale, with birth and death element method, a thermo-mechanical coupled finite element model (FEM) was set up to explore the temperature and contact pressure distribution at the Cu/Al bonding interface in the SLCRB process. Taking these macro-scale simulation results as boundary conditions, we simulated the atom diffusion law of the bonding interface by molecular dynamics (MD) in micro-scale. The results indicate that the temperature in Cu/Al bonding interface deceases from 700 to 320 °C from the entrance to the exit of caster, and the peak of contact pressure reaches up to 140 MPa. The interfacial diffusion thickness depends on temperature and rolling reduction, higher temperature results in larger thickness, and the rolling reduction below kiss point leads to significant elongation deformation of cladding strip which yields more newborn interface with fresh metal and make the diffusion layer thinner. The surface roughness of Cu strip was found to be beneft to atoms diffusion in the Cu/Al bonding interface. Meanwhile, combined with the SEM-EDS observation on the microstructure and composition in the bonding interface of the experimental samples acquired from the cast-rolling bite, it is revealed that the rolling reduction and severe elongation deformation in the solid-solid contact zone below kiss point guarantee the satisfactory metallurgical bonding with thin and smooth diffusion layer. The bonding mechanisms of reactive diffusion, mechanical interlocking and crack bonding are proved to coexist in the SLCRB process.

Keywords

Cu/Al cladding strip / solid-liquid cast-roll bonding (SLCRB) / bonding / mechanism / finite element method (FEM) / molecular dynamics (MD)

References

[1] Liang H, Xue ZY, Wu CJ, et al. Research on Continuous Core-Filling Casting Forming Process of Copper-Clad Aluminum Bimetal Composite Material[J]. Acta Metallurgica Sinica (English Letters), 2010, 23(3): 206-214.

[2] Anand TJS, Kok Y-C, Jalar A. Micro-Structural Studies of Ther-mosonic Cu-Al Bonding Interface[J]. Advanced Materials Research, 2014, 925: 154-158.

[3] Yuan HU, Chen YQ, Li LI, et al. Microstructure and Properties of Al/Cu Bimetal in Liquid–Solid Compound Casting Process[J]. Transactions of Nonferrous Metals Society of China, 2016, 26(6): 1 555-1 563.

[4] Karlík M, Mánik T, Lauschmann H. Influence of Si and Fe on the Distribution of Intermetallic Compounds in Twin-Roll Cast Al-Mn-Zr alloys[J]. Journal of Alloys & Compounds, 2012, 515(515): 108-113.

[5] Lv Z, Du F, An Z, et al. Centerline Segregation Mechanism of Twin-Roll Cast A3003 Strip[J]. Journal of Alloys & Compounds, 2015, 643: 270-274.

[6] Bae JH, Rao AKP, Kim KH, et al. Cladding of Mg Alloy with Al by Twin-Roll Casting[J]. Scripta Materialia, 2011, 64(9): 836-839.

[7] Park J, Song H, Kim JS, et al. Three-Ply Al/Mg/Al Clad Sheets Fabricated by Twin-Roll Casting and Post-treatments (Homogenization, Warm Rolling, and Annealing)[J]. Metallurgical & Materials Transactions A, 2017, 48(1): 57-62.

[8] Grydin O, Gerstein G, Nürnberger F, et al. Twin-Roll Casting of Aluminum–Steel Clad Strips[J]. Journal of Manufacturing Processes, 2013, 15(4): 501-507.

[9] Nakamura R, Sawai M, Nakamura R, et al. Roll Casting of Three Layers Clad Strip[J]. Key Engineering Materials, 2010, 443: 128-133.

[10] Stolbchenko M, Grydin O, Samsonenko A, et al. Numerical Analysis of the Twin-Roll Casting of Thin Aluminum-Steel Clad Strips[J]. For-schung Im Ingenieurwesen, 2014, 78(3–4): 1-10.

[11] Huang HG, Ji C, Dong YK, et al. Thermal-Flow Coupled Numerical Simulation and Experimental Research on Bonding Mechanism of Cu/Al Composite Strip by Solid-Liquid Cast-Rolling[J]. The Chinese Journal of Nonferrous Metals, 2016 623-629.

[12] Park JJ. Numerical Analysis of Twin-Roll Casting to Fabricate a Laminated Sheet from Melts[J]. International Journal of Heat & Mass Transfer, 2016, 100: 590-598.

[13] China Mechanical Engineering, 2015, 26(11

[14] Li C, Li D, Tao X, et al. Molecular Dynamics Simulation of Diffusion Bonding of Al-Cu Interface[J]. Modelling and Simulation in Materials Science and Engineering, 2014, 22: 396-397.

[15] Chen S, Ke F, Min Z, et al. Atomistic Investigation of the Effects of Temperature and Surface Roughness on Diffusion Bonding between Cu and Al[J]. Acta Materialia, 2007, 55(9): 3 169-3 175.

[16] Zhang YX. Experiment Research of Transient Thermal Contact Resistance and its Application in Fast Roll Casting Process Parameter Simulation [D]. Thesis of Central South University, 2004

[17] Wang D Z C X G, et al. Heat Transfer Behavior of Top Side-Pouring Twin-Roll Casting[J]. Journal of Materials Processing Technology, 2014, 214(6): 1 275-1 284.

[18] Zhan LH. Rheological Behavior Research and Thermo-Mechanical Coupled Analysis of Aluminium Continuous Roll Casting Process[D]. Dissertation of Central South University, 2005

[19] Zhou XW, Wadley HNG, Johnson RA, et al. Atomic Scale Structure of Sputtered Metal Multilayers[J]. Acta Materialia, 2001, 49(19): 4 005-4 015.

[20] Tanaka Y, Kajihara M. Numerical Analysis for Migration of Interface between Liquid and Solid Phases during Reactive Diffusion in the Binary Cu-Al System[J]. Materials Science & Engineering A, 2007, 459(1): 101-110.

[21] Wang Z, Liu P, Liu XK, et al. Diffusion Layer Growth Kinetics Model of Copper Hot-Dipping Aluminum Coating[J]. Journal of Functional Materials, 2015, 46(2): 02 080-02 083.