Controlled Synthesis of Core-Shell Nickel Microspheres with Solid Core and Porous Shell by Precipitation and Thermal Decomposition Method

Abstract

Nickel oxalate micro-spheres with core-shell structure of solid core and radiate shell were synthesized by precipitation method in a mixed water solution, with oxalic acid and nickel acetate as raw materials, through dropping ammonium hydroxide to adjust the solution pH value to about 8.0. Nickel microspheres with core-shell structure of solid core and porous shell were prepared by decomposing of nickel oxalate microspheres precursor at about 340 °C in argon atmosphere. The analyses of infrared spectroscopy (IR) indicates that the composition of the powders is nickel oxalate. The analyses of atomic absorption spectrometry (AAS) and organic elemental analysis (OEA) indicate that the molar ratio of (C₂O₄)²⁻/Ni²⁺ is about 1.02, close to the theoretical value of 1.0. The results of the thermo-gravimetric and differential thermal gravity analyses (TG-DTG) indicate that the molar ratio of (C₂O₄)²⁻/Ni²⁺ is about 1.06, also close to the theoretical value of 1.0. The analysis of X-ray diffraction (XRD) indicates that the composition of black powders as-prepared is nickel, which has a face-centered cubic crystal structure with average crystal grain size about 16.87 nm. The images of scanning electron microscopy (SEM) indicate that the morphology of nickel oxalate microspheres is a core-shell structure with solid core and radiate shell. The diameter of nickel oxalate microspheres is about 3 μm, and the shell consists of a large number of thin nanorods. The images of SEM also indicate that the morphology of nickel microspheres is a core-shell structure with solid core and porous shell. The diameter of nickel microspheres is about 2 μm, and the shell consists of a large number of nickel grains, surface holes and through holes. The diameter of nickel grains is about 50–100 nm, and the diameter of holes is about 50–200 nm.

Keywords

nickel oxalate / nickel / core-shell / porous / precipitation / thermal-decomposition

References

[1] You B, Liu X, Liu X, et al. Effcient H₂ Evolution Coupled with Oxi-dative Refning of Alcohols via A Hierarchically Porous Nickel Bifunc-tional Electrocatalyst[J]. ACS Catal., 2017, 7: 4 564-4 570.

[2] Smith R D, Prévot M S, Fagan R D, et al. Photochemical Route for Accessing Amorphous Metal Oxide Materials for Water Oxidation Catalysis[J]. Science, 2013, 340: 60-63.

[3] Peng J, Gong M, Kenney MJ, et al. Nickel-Coated Silicon Photo Cathode for Water Splitting in Alkaline Electrolytes[J]. Nano Res., 2015, 8: 1577-1583.

[4] Xu W, Lu Z, Wan P, et al. High-Performance Water Electrolysis System with Double Nanostructured Super Aerophobic Electrodes[J]. Small, 2016, 12: 2492-2498.

[5] Lu X, Zhao C. Electrodeposition of Hierarchically Structured Three-Dimensional Nickel-Iron Electrodes for Effcient Oxygen Evolution at High Current Densities[J]. Nat. Commun., 2015, 6: 6 616.

[6] Ni S, Li T, Lv X, et al. Designed Constitution of NiO/Ni Nanostruc-tured Electrode for High Performance Lithium Ion Battery[J]. Electrochim. Acta, 2013, 91: 267-274.

[7] Rahman MA, Wen C. A Study of the Capacity Fade of Porous NiO/Ni Foam as Negative Electrode for Lithium Ion Batteries[J]. Ionics, 2016, 22: 173-184.

[8] Tracey VA. Production of Porous Nickel for Alkaline-Battery and Fuel-Cell Electrodes: Practical and Economic Considerations[J]. Powder Metal., 2014, 8: 241-255.

[9] Fan H, Cheng M, Wang Z, et al. Layer-Controlled Pt-Ni Porous Na-nobowls with Enhanced Electro-Catalytic Performance[J]. Nano Res., 2017, 10: 187-198.

[10] Feng G, Kuang Y, Li Y, et al. 3D porous Superaerophobic Nickel Nanofower Electrodes for High-Performance Hydrazine Oxidation[J]. Nano Res., 2015, 8: 3 365-3 371.

[11] Kim SG, Yoon SP, Han J, et al. Mechanical Strength of Porous Nickel Plates Containing Lithium and Their Performance as the Cathode for MCFC[J]. J. Power Sources, 2002, 110: 80-85.

[12] Zheng X, Wang H, Wang C, et al. 3D Interconnected Macro-Meso Porous Electrode with Self-Assembled NiO Nanodots for High-Performance Supercapacitor-Like Li-Ion Battery[J]. Nano Energy, 2016, 22: 269-277.

[13] Zhang J, Liu F, Cheng JP, et al. Binary Nickel-Cobalt Oxides Electrode Materials for High Performance Supercapacitors: Infuence of its Composition and Porous Nature[J]. ACS Appl. Mater. Interfaces, 2015, 7: 17 630-17 640.

[14] Wei W, Chen W, Ding L, et al. Construction of Hierarchical Three-Dimensional Interspersed Flower-Like Nickel Hydroxide for Asymmetric Supercapacitors[J]. Nano Res., 2017, 10: 3 726-3 742.

[15] Xanthopoulou G, Thoda O, Metaxa ED, et al. Influence of Atomic Structure on the Nano-Nickel-Based Catalyst Aactivity Produced by Solution Combustion Synthesis in the Hydrogenation of Maleic Ccid[J]. J. Catal., 2017, 348: 9-21.

[16] Lua AC, Wang HY. Decomposition of Methane Over Unsupported Porous Nickel and Alloy Catalyst[J]. Appl. Catal., B: Environ., 2013, 132: 469-478.

[17] Bell T T-, Murciano L. H₂ Production via Ammonia Decomposition Using Non-Noble Metal Catalysts: A Review[J]. Top. Catal., 2016, 59: 1438-1457.

[18] Kumar A, Ashok A, Bhosale RR, et al. In Situ DRIFTS Studies on Cu, Ni and CuNi Catalysts for Ethanol Decomposition Reaction[J]. Catal. Lett., 2016, 146: 778-787.

[19] Chen C, Kang Y, Huo Z, et al. Highly Crystalline Multimetallic Nanof-rames with Three-Dimensional Electrocatalytic Surfaces[J]. Science, 2014, 343: 1339-1343.

[20] Golubina EV, Lokteva ES, Maslakov KI, et al. Peculiarities of the Structure and Catalytic Behavior of Nanostructured Ni Catalysts Prepared by Laser Electrodispersion[J]. Nanotechnol. Russ., 2017, 12: 19-26.

[21] Li S, Chien CL, Searson PC. Fabrication of Nanoporous Nickel by Electrochemical Dealloying[J]. Chem. Mater., 2004, 16: 3 125-3 129.

[22] Li T, Liu Y, Ma G. Preparation of Submicro-Porous Nickel Wafers by Molding-Decomposition-Sintering Method Using Nickel Oxalate Na-norods as Precursors[J]. Rare Met. Mater. Eng., 2016, 45: 1396-1400.

[23] Lai M, Riley DJ. Templated Electrosynthesis of Nanomaterials and Porous Structures[J]. J. Colloid Interface Sci., 2008, 323: 203-212.

[24] Wu Y, Wang D, Zhou G, et al. Sophisticated Construction of Au Islands on Pt-Ni: An Ideal Trimetallic Nanoframe Catalyst[J]. J. Am. Chem. Soc., 2014, 136: 11 594-11 597.