Fabrication of in situ Ti₂AlN/TiAl composites by reaction hot pressing and their properties

Abstract

Ti₂AlN/TiAl composites with different volume fractions of reinforcement were successfully fabricated by hot-pressing sintering method (reaction hot pressing) using Ti, Al and TiN powders as starting materials. The synthesis process includes four stages: first, the reactions between Al and Ti powers and between Al and TiN powders respectively occur and result in TiAl₃ phase; secondly, Al powders in the sample are exhausted; the remaining Ti cores react with TiAl₃ layer to form Ti-Al intermetallics; moreover, a few Ti₂AlN particles precipitate from the TiAl₃ phase; thirdly, Ti-Al intermetallics react with the remaining Ti cores to form Ti₃Al and TiAl phases. TiAl phase and original TiN powers are in direct contact each other; finally, the residual TiN powers react with TiAl phase and result in a plenty of Ti₂AlN phase. Compared with TiAl matrix, the hardness, elastic modulus and high-temperature compressive strength of Ti₂AlN/TiAl composite are improved obviously and they are all enhanced with increasing the volume fraction of Ti₂AlN phase.

Keywords

composites / titanium aluminides / mechanical properties / sintering / electron microscopy / transmission

References

[1] Tetsui T Development of a TiAl Turbocharger for Passenger Vehicles [J]. Materials Science and Engineering A, 2002, 329–331: 582-588.

[2] Gebauer K Performance, Tolerance and Cost of TiAl Passenger Car Valves[J]. Intermetallics, 2006, 14(4): 355-360.

[3] Wu XH Review of Alloy and Process Development of TiAl Alloys [J]. Intermetallics, 2006, 14(10–11): 1 114-1 122.

[4] Appel F, Wagner R Microstructure and Deformation of Two-Phase γ-Titanium Aluminides[J]. Materials Science and Engineering R, 1998, 22(5): 187-268.

[5] Bohn R, Klassen T, Bormann R Mechanical Behavior of Submicrongrained γ-TiAl-based Alloys at Elevated Temperatures [J]. Intermetallics, 2001, 9(7): 559-569.

[6] Djanarthany S, Viala JC, Bouix J Development of SiC/TiAl Composites: Processing and Interfacial Phenomena[J]. Materials Science and Engineering A, 2001, 300(1–2): 211-218.

[7] Shih DS, Amato RA Interface Reaction between Gamma Titanium Aluminide Alloys and Reinforcements[J]. Scripta Metall., 1990, 24(11): 2 053-2 058.

[8] Lin ZJ, Zhuo MJ, Li MS, . Synthesis and Microstructure of Layered-Ternary Ti₂AlN Ceramic[J]. Scripta Materialia, 2007, 56(12): 1 115-1 118.

[9] Tian WH, Nemoto M Precipitation Behavior of Nitrides in L10-Ordered TiAl[J]. Intermetallics, 2005, 13(10): 1 030-1 037.

[10] Rastkar AR, Bell T Tribological Performance of Plasma Nitrided Gamma Based Titanium Aluminides[J]. Wear, 2002, 253(11–12): 1 121-1 131.

[11] Hsiung LM, Nieh TG Microstructures and Properties of Powder Metallurgy TiAl Alloys[J]. Materials Science and Engineering A, 2004, 364(1–2): 1-10.

[12] Wang T, Zhang J Thermoanalytical and Metallographical Investigations on the Synthesis of TiAl₃ from Elementary Powders [J]. Materials Chemistry and Physics, 2006, 99(1): 20-25.

[13] Ramaseshan R, Kakitsuji A, Seshadri SK Microstructure and some Properties of TiAl-Ti₂AlC Composites Produced by Reactive Processing [J]. Intermetallics, 1999, 7(5): 571-577.

[14] Bertolino N, Monagheddu M, Tacca A, . Ignition Mechanism in Combustion Synthesis of Ti-Al and Ti-Ni Systems[J]. Intermetallics, 2003, 11(1): 41-49.