Microstructure and properties of gradient cemented carbide with Nano-TiN

Abstract

Gradient cemented carbides with nano-TiN were prepared by the common powder metallurgical procedure. The formation of gradient zone and the microstructure, properties of the alloys were investigated using scanning electron microscope(SEM), energy dispersive spectroscopy(EDS) and other performance testing apparatus. Moreover, the effect of nano-TiN on the gradient cemented carbide was studied. It is found that gradient zone width increases slightly with nano-TiN introduction. Both cobalt and titanium concentrations reach the maximum near the gradient border. Tungsten concentration shows fluctuation from the surface to the bulk. (Ti,W)C phase grains are refined for nitrogen introduction. Core-rim structure has been observed under the SEM back-scattered mode. The core appears as dark due to more titanium in it and the rim with more tungsten appears as grey. In addition, the hardness and transverse rupture strength of gradient cemented carbide are enhanced with nano-TiN introduced.

Keywords

gradient cemented carbide / cubic phase / nano-TiN / core-rim structure

References

[1] Liu Y, Wang H B, Yang J G, . Formation Mechanism of Cobalt-gradient Structure in WC-Co Hard Alloy[J]. J. Mater. Sci., 2004, 39: 4 397-4 399.

[2] Frykholm R, Jansson B, Andrén H O The Influence of Carbon Content on Formation of Carbo-nitride Free Surface Layers in Cemented Carbides[J]. Int. J. Refract Met. Hard. Mater., 2002, 20: 345-353.

[3] Suzuki H, Hayashi K, Taniguchi Y The Beta-free Layer Formed Near the Surface of Vacuum-sintered WC-beta-Co Alloys Containing Nitrogen[J]. Trans. Jpn. Inst. Metals, 1981, 22: 758-764.

[4] Schwarzkopf M, Exner H E, Fischmeister H F, . Kinetics of Compositional Modification of (W,Ti)C-WC-Co Alloy Surfaces[J]. Mater. Sci. Eng. A, 1988, 105–106: 225-231.

[5] Gustafson P, Östlund A Binder-phase Enrichment by Dissolution of Cubic Carbides[J]. Int. J. Refract Met. Hard. Mater., 1994, 12: 129-136.

[6] Frykholm R, Ekroth M, Jansson B, . Effect of Cubic Phase Composition on Gradient Zone Formation in Cemented Carbides[J]. Int. J. Refract. Met. Hard. Mater., 2001, 19: 527-538.

[7] Liu N, Xu Y D, Li H, . Effect of Nano-micro TiN Addition on the Microstructure and Mechanical Properties of TiC Based Cermets[J]. J. Eur. Ceram. Soc., 2002, 22: 2 409-2 414.

[8] Liu N, Xu Y D, Li H, . Cutting and Wearing Characteristics of TiCbased Cermets Cutters with Nano-TiN Addition[J]. J. Mater. Process. Technol., 2005, 161: 478-484.

[9] Wang Z A, Dai H Y, Zou Y Effects of Nano TiN Addition on the Microstructure and Mechanical Properties of TiC Based Steel Bonded Carbides[J]. Rare Met., 2008, 27(1): 5-8.

[10] Chen L M, Lengauer W, Ettmayer P Fundamentals of Liquid Phase Sintering for Modern Cermets and Functionally Graded Cemented Carbides (FGCC)[J]. Int. J. Refract Met. Hard. Mater., 2000, 18: 307-322.

[11] Li J R The Technology Study of the Depleted Cubic Phase Layer in Cemented Carbide[J]. Cemented Carbide, 2004, 21(4): 197-202.

[12] Frykholm R, Ekroth M, Jansson B, . A New Labyrinth Factor for Modelling the Effect of Binder Volume Fraction on Gradient Sintering of Cemented Carbides[J]. Acta Mater., 2003, 51: 1 115-1 121.

[13] Ekroth M, Frykholm R, Lindholm M, . Gradient Zones in WC-Ti(C,N)-based Cemented Carbides: Experimental Study and Computer Simulations[J]. Acta Mater., 2000, 48: 2 177-2 185.

[14] Liu Y, Wang H B, Long Z Y, . Enhancement on the Transverse Fracture Strength of Functional Graded Structure Cemented Carbides[J]. J. Mater. Sci., 2005, 40: 5 525-5 527.

[15] Xiong J, Guo Z X, Yang M, . Effect of Ultra-fine TiC_0.5N_0.5 on the Microstructure and Properties of Gradient Cemented Carbide[J]. J. Mater. Process. Technol., 2009, 209: 5 293-5 299.

[16] Chen L, Wu E X, Yin F, . Effects of Gradient Structure on the Microstructures and Properties of Coated Cemented Carbides[J]. J. Univ. Sci. Technol. Beijing, 2006, 13(4): 363-367.

[17] Liu N, Xu Y D, Li Z H, . Influence of Molybdenum Addition on the Microstructure and Mechanical Properties of TiC-based Cermets with Nano-TiN Modification[J]. Ceram. Int., 2003, 29(8): 919-925.

[18] Bolognini S, Feusier G, Mari D, . High Temperature Mechanical Behaviour of Ti (C,N)-Mo-Co Cermets[J]. Int. J. Refract Met. Hard. Mater., 1998, 16(4–6): 257-268.

[19] Andrén H O Microstructure Development during Sintering and Heattreatment of Cemented Carbides and Cermets[J]. Mater. Chem. Phys., 2001, 67: 209-213.

[20] Yoshimura H, Sugizawa T, Doi H Reaction Occurring during Sintering and the Characteristics of TiC-20TiN-15WC-10TaC-9Mo-55Ni-11Co. Cermet[J]. Int. J. Refract Met. Hard. Mater., 1983, 2(4): 170-174.

[21] Bhaumik S K, Upadhyaya G S, Vaidya M L Full Density Processing of Complex WC-based Cemented Carbides[J]. J. Mater. Process. Technol., 1996, 58: 45-50.

[22] Xiao J M Alloy Energetics[M], 1985 Shanghai Shanghai Science and Technology Press

[23] Xu Z M, Yi X J, Hu M Z, . Study of Ti(C, N) Nanopowder Reinforced-Ti(C, N) Based Cermets[J]. Trans. Mater. Heat Treat., 2003, 24(3): 41-45.

[24] Zhang W Z, Liu Y, He Y H, . Effect of Ti(CN) Content on the Gradient Structure and Properties of Cemented Carbides[J]. Rare Met. Cemented Carbides, 2005, 33: 28-30.