Comparison of chemical reactivity of bauxite-tailings pre- and post-calcinations and whitening bauxite-tailing

Abstract

Bauxite-tailings is aluminosilicate wastes and is used in polymer as fillers. But its intrinsic low-whiteness has limited its large-scale application in polymeric materials. Conventional methods for whitening bauxite-tailings were ineffective. A new method, which involved reactions with phosphoric acid and calcinations, was proposed to whiten bauxite-tailings. Two process routes were employed to whiten bauxitetailings, which were pre- and post-reaction calcination. While the process of pre-reaction calcination was able to achieve a whiteness of 87% from bauxite-tailings, it required high-energy post-treatment processes such as washing, milling and drying. The process of post-reaction calcination, on the other hand, resulted in an increase in whiteness of bauxite-tailings from 19% to 73%. This was achieved using 4.5% of added phosphorous, 40% acid concentration, reaction time of 2.5 hours and a calcination temperature of 600 °C. The resultant did not require any further processing, and was therefore industrially feasible. The whitened tailings consisted of corundum, anatase, and quartz. When compared to calcined tailings, whitened tailings possessed a higher content of amorphous material, the disappearance of red iron minerals, and the emergence of a new phase of AlPO₄.

Keywords

whiteness / bauxite tailings / fillers

References

[1] Awad W H, Beyer G, Benderly D, . Material Properties of Nanoclay PVC Composites[J]. Polymer, 2009, 50(8): 1 857-1 867.

[2] Matusik J, Stodolak E, Bahranowski K Synthesis of Polylactide / Clay Composites Using Structurally Different Kaolinites and Kaolinite Nanotubes[J]. Applied Clay Science, 2011, 51(1): 102-109.

[3] Jubete E, Liauw C M, Jacobson K, . Degradation of Carboxylated Styrene Butadiene Rubber Based Water Born Paints. Part 1: Effect of Talc Filler and Titania Pigment on UV Stability[J]. Polymer Degradation and Stability, 2007, 92(8): 1 611-1 621.

[4] Gorna K, Hund M, Vučak M, . Amorphous Calcium Carbonate in Form of Spherical Nanosized Particles and Its Application as Fillers for Polymers[J]. Materials Science and Engineering: A, 2008, 477(1): 217-225.

[5] Park S J, Jun B R Improvement of Red Mud Polymer-Matrix Nanocomposites by Red Mud Surface Treatment[J]. Surface Treatment, 2005, 284(1): 204-209.

[6] Chaowasakoo T, Sombatsompop N Mechanical and Morphological Properties of Fly Ash/Epoxy Composites using Microwave and Conventional Thermal Curing Methods[J]. Composites Science and Technology, 2007, 67(11): 2 282-2 291.

[7] Gök A, Omastová M, Prokeš J Synthesis and Characterization of Red Mud/Polyaniline Composites: Electrical Properties and Thermal Stability[J]. European Polymer Journal, 2007, 43(6): 2 471-2 480.

[8] Chandrasekhar S, Ramaswamy S Influence of Mineral Impurities on the Properties of Kaolin and Its Thermally Treated Products[J]. Applied Clay Science, 2002, 21(4): 133-142.

[9] Chandrasekhar S, Ramaswamy S Iron Minerals and Their Influence on the Optical Properties of Two Indian Kaolins[J]. Applied Clay Science, 2006, 33(3): 269-277.

[10] Ambikadevi V R, Lalithambika M Effect of Organic Acids on Ferric Iron Removal From Iron-stained Kaolinite[J]. Applied Clay Science, 2000, 16(3): 133-145.

[11] González J A, Ruiz M d C Bleaching of Kaolins and Clays by Chlorination of Iron and Titanium[J]. Applied Clay Science, 2006, 33(3): 219-229.

[12] Oliveira D, Ortiz N, Paulo S, . Process for Whitening Kaolin, 1993

[13] de Mesquita L M S, Rodrigues T, Gomes S S Bleaching of Brazilian Kaolins Using Organic Acids and Fermented Medium[J]. Minerals Engineering, 1996, 9(9): 965-971.

[14] Wang Y, Lan Y, Hu Yuehua Adsorption Mechanisms of Cr(VI) on the Modified Bauxite Tailings[J]. Minerals Engineering, 2008, 21(12): 913-917.

[15] Huo c, Liu M, Zhao W, . Deep Processing of Tailings from the Bauxite Beneficiation and Its Application in PVC Plastics[J]. Metal Mine, 2010, 9: 177-181.

[16] Patermarakis G, Paspaliaris Y The Leaching of Iron Oxides in Boehmitic Bauxite by Hydrochloric Acid[J]. Hydrometallurgy, 1989, 23(1): 77-90.

[17] Yuan M, Zhao G, Hu Yuehua Acidic Dissolution Behavior of Iron in the Floated Tails of Complicated Bauxite[J]. The Chinese Journal of Process Engineering, 2004, 4(1): 12-15.

[18] Li X, Zhou Q, Peng Z, . Study on the Kinetics of Digesting Roasted Diaspore in the Sweetening Process[J]. Journal of Central South University Technology, 2000, 31(3): 219-221.

[19] Zhao H, Li X, Liu P, . Improvement of Diasporic Bauxite’s Digestion Through Bayer Process[J]. Conservation and Utilization of Mineral Resources, 1997, 5: 45-50.

[20] Zhao T, Ju X, Zhai J, . Researches on Relationship Between the Acid Digestibilities and the Mineral Constitutions for Some Important Aluminium-Containing Minerals in China[J]. Journal of Zhengzhou University, 1997, 29(1): 89-93.