Investigation of the thermal decomposition properties of polyoxymethylene

Abstract

By testing the melt index (MI), tensile strength and breaking extension ratio, the thermal ageing rate of polyoxymethylene (POM) was analyzed and compared. The surface morphology and type of function group of POM surface were observed and analyzed by SEM and XPS. The results show that the MI value increases gradually with the ageing time at 120 °C, indicating that the thermal oxidation decomposition occurrs slowly. The effect of 20-day thermal ageing on the tensile strength and breaking extension ratio of POM is not obvious, showing that the ageing of POM is quite a long process. After 105-day, thermal ageing cracking and powdering occurr on the POM surface. XPS determination shows the C1s spectra of samples before and after ageing include two peaks of C-C and C-O, while after ageing the content of C-C decreases and the content of C-O increases, indicating that the thermal ageing of POM is mainly the breaking and decomposing of C-C bond. The O1s/C1s ratio of original samples is 56.98% and after 105-day thermal ageing the ratio is 72.92%.

Keywords

polyoxymethylene / surface / thermal decomposition

References

[1] Dou Q., Feng X., Lu X. Development and Application of Polyoxymethylene Self-lubricating Composite [J]. Polymer Materials Science and Engineering, 2003, 1: 36-40.

[2] Qu Q., Li X., Zhu J. Sliding Bearing Research of Universal Coupling of Automobile [J]. Lubrication and Sealing, 1996, 5: 58-60.

[3] Hu P., Huang C., Zheng H. Study on Application of Polyester Elastomer in Automobile Steering Systems [J]. Automobile Technology, 2003, 8: 32-34.

[4] Schweitzer C. E., Macdonal R. N., Punderson J. O. Thermally Stable High Molecular Weight Polyoxymethylenes [J]. Journal of Applied Polymer Science, 1959, 1(2): 158-163.

[5] Shi L. The Investigation About Degradation of POM [J]. Journal of Shangrao Teachers College, 2001, 3: 47-49.

[6] Yu J. The Ageing Behavior of POM in Boiling Water [J]. China Plastics, 1996, 1: 17-21.

[7] Zhou D., Xie G. The Ageing and Resistance Technology to Ageing of Plastics[M], 2002. Beijing: Chemical Industry Press.

[8] Ji K. Advances in XPS Applied to Surface Degradation of Polymers [J]. Polymer Materials Science and Engineering, 1994, 5: 12-17.

[9] Su C., Zhang D., Xu Z., . The Thermalgravimetric Investigation of Polyoxymethylene [J]. Functional Polymer, 1994, 2: 165-172.

[10] Stohler R., Berger k. Die Angewandte Makromolekulare Chemie [J]. Macromolecular Materials and Engineering, 1990, 176/177: 323

[11] Zhou D., Xie G. Plastics Ageing and Ageing Resistance Technology [M], 1998. Beijing: China Light Industry Press.

[12] Zhong S., Xu W., Wang G. Decomposition and Stability of Polymer [M], 2002. Beijing: China Chemical Industry Press.

[13] He C., Shi L. Wear Resistance Property of POM Etc [J]. Machine Design and Manutacturing Engineering, 1998, 6: 48-50.