Fabrication and properties of multilayer chitosan membrane loaded with tinidazole

Abstract

With the aim of providing effective periodontal disease therapeutic method, multilayer membranes which were loaded with drug for guided tissue regeneration were prepared using an immerse-precipitation phase inversion technique. Single layer, bi-layer and tri-layer membranes were fabricated with chitosan used as carrier and tinidazole as medicine model which was loaded on the membrane. The influence of layer on structure and properties of membrane were studied by SEM, UV spectrophotometer and mechanical test. Drug release properties of three types of layer membranes were also investigated. The results showed that release rate could be slown down in both bi-layer and tri-layer membranes (to 11 days and 14 days respectively) and tri-layer membrane lasted the longest. After a process of rapid release, the concentration of tinidazole which was released by the membrane was maintained at an efficient dosage level. Compared with single layer and bi-layer membranes, we found tri-layer membrane could play a role in controlling low-rate drug release especially at the early stage of release, and keep an efficient dosage at affected part for a long period of time. The loss of drug which loaded on membrane decreased from 84.6% for single layer to 13.04% for tri-layer. The mechanical strength of three types of membrane were detected and showed that it could meet the requiremens of clinical practice. The membranes especially with tri-layer could be more valuable in application.

Keywords

chitosan / membrane / multilayer / drug loss / release rate

References

[1] Gottlow J., Nyman S., Lindhe J., . 1986 New Attachment Formation in the Human Periodontium by Guided Tissue Regeneration: Case Reports[J]. J. Clin. Periodontal, 1986, 13: 604-616.

[2] Mukherjee D.P., Tunkle A.S., Roberts R.A., . An Animal Evaluation of a Paste of Chitosan Glutamate and Hydroxyapatite as a Synthetic Bone Graft Material[J]. J. Biomed. Mater. Res., 2003, 67B: 603-609.

[3] VandeVord P.J., Matthew H.W., DeSilva S.P., . Evaluation of the Biocompatibility of a Chitosan Scaffold in Mice[J]. J. Biomed. Mater. Res., 2002, 59: 585-590.

[4] Nsereko S., Amiji M. Localized Delivery of Paclitaxel in Solid Tumors from Biodegradable Chitin Microparticle Formulations. [J]. Biomaterials, 2002, 23: 2 723-2 731.

[5] Singla A.K., Chitosan C. M. Some Pharmaceutical and Biological Aspects-An Update[J]. J. Pharm Pharmacol, 2001, 53: 1 047-1 067.

[6] Senel S., Kremer M.J., Kas S., . Enhancing Effect of Chitosan on Peptide Drug Delivery across Buccal Mucosa[J]. Biomaterials, 2000, 21: 2 067-2 071.

[7] Madihally S.V., Matthew H.W. Porous Chitosan Scaffolds for Tissue Engineering[J]. Biomaterials, 1999, 20: 1 133-1 142.

[8] Park J.S., Choi S.H., Moon I.S., . Eight Week Histological Analysis on the Effect of Chitosan on Surgically Created One-wall Intrabony Defects in Beagle Dogs[J]. J. Clin Periodontol, 2003, 30: 443-453.

[9] Levina V. I., Trukhacheva L. A. Investigation of the No-donor Activity of the Antimicrobial Drug Tinidazole[J]. Pharmaceutical Chemistry Journal, 2004, 38(1): 15-18.

[10] Emshanova S. V., Zuev A. P. Composition and Technology of Tinidazole Core Tablets[J]. Pharmaceutical Chemistry Journal, 2004, 38(11): 628-631.

[11] Brook I., Frazier E.H., Thompson D.H. Aerobic and Anaerobic Microbiology of Periapical Abscess[J]. Oral Microbiol. Immunol., 1991, 6(1): 123-124.

[12] Xiu W. The Research of Periodontal Tissue Stress Distribution under the Orthoraedic Force and the Control of Orthoraedic Curve on the Tooth Moving[D], 2003. Nanjing: Dongnan University.