Austenite formation during intercritical annealing in C-Mn cold-rolled dual phase steel

Abstract

Two different kinds of experimental techniques were used to in-situ study the austenite formation during intercritical annealing in C-Mn dual phase steel. The microstructure evolution was observed by confocal laser scanning microscope, and the austenite isothermal and non-isothermal transformation kinetics were studied by dilatometry. The results indicate that banded structure is produced for the reason of composition segregation and the competition between recrystallization and phase transformation. Austenite prefers to nucleate not only at ferrite/ferrite grain boundaries, but also inside the grains of ferrite. Furthermore, the austenitizing process is accomplished mainly via migration of the existing austenite/ferrite interface rather than nucleation of new grains. The incubation process can be divided into two stages which are controlled by carbon and manganese diffusion, respectively. During the incubation process, the nucleation rate of austenite decreases, and austenite growth changes from two-dimensional to one-dimensional. The partitioning coefficient, defined as the ratio of manganese content in the austenite to that in the adjacent ferrite, increases with increasing soaking time.

Keywords

dual phase steel / confocal laser scanning microscope / dilatometry / austenitizing / in situ observation

References

[1] KangY-l, HanQ-h, ZhaoX-m, CaiM-hui. Influence of nanoparticle reinforcements on the strengthening mechanisms of an ultrafine-grained dual phase steel containing titanium [J]. Materials and Design, 2013, 44: 331-339

[2] SpeichG R, DemarestV A, MillerR L. Formation of austenite during intercritical annealing of dual-phase steels [J]. Metallurgical Transactions A, 1981, 12: 1419-1428

[3] GarciaC I, DeardoA J. Formation of austenite in 1.5% Mn steels [J]. Metallurgical Transactions A, 1981, 12: 521-530

[4] SavranV I, OffermanS E, SietsmaJ. Austenite nucleation and growth observed on the level of individual grains by three-dimensional X-Ray diffraction microscopy [J]. Metallurgical and Materials Transactions A, 2010, 41: 583-591

[5] NouriA, SaghafianH, KheirandishS. Effects of silicon content and intercritical annealing on manganese partitioning in dual phase steels [J]. Journal of Iron and Steel Research International, 2010, 17(5): 44-50

[6] RajuS, GaneshB J, RaiA K, MythiliR, SarojaS, RajB. A study on martensitic phase transformation in 9Cr-1W-0.23V-0.063Ta-0.56Mn-0.09C-0.02N (wt.%) reduced activation steel using differential scanning calorimetry [J]. Journal of Nuclear Materials, 2010, 405: 59-69

[7] MartinD S, van DijkN H, BrückE, van der ZwaagS. The isothermal martensite formation in a maraging steel: A magnetic study [J]. Materials Science and Engineering A, 2008, 481/482: 757-761

[8] AndrésC G, CaballeroF G, CapdevilaC, ÁlvarezL F. Application of dilatometric analysis to the study of solid-solid phase transformations in steels [J]. Materials Characterization, 2002, 48: 101-111

[9] MartinD S, CastilloP E J R, AndrésC G. In situ study of austenite formation by dilatometry in a low carbon microalloyed steel [J]. Scripta Materialia, 2008, 58: 926-929

[10] LiuL, YangZ G, ZhangC, LiuW B. An in situ study on austenite memory and austenitic spontaneous recrystallization of a martensitic steel [J]. Materials Science and Engineering A, 2010, 527: 7204-7209

[11] ZhangD, TerasakiH, KomizoY. In situ observation of the formation of intragranular acicular ferrite at non-metallic inclusions in C-Mn steel [J]. Acta Materialia, 2010, 58: 1369-1378

[12] SchmidtE, SolteszD, RobertsS, BednarA, SridharS. The austenite/ferrite front migration rate during heating of IF steel [J]. ISIJ International, 2006, 46(10): 1500-1509

[13] OliveiraF L G, AndradeM S, CotaA B. Kinetics of austenite formation during continuous heating in a low carbon steel [J]. Materials Characterization, 2007, 58: 256-261

[14] ZhangX-h, ZhuG-h, MaoW-min. Effect of interaction between recrystallization and transformation on microstructure of dual phase steel [J]. Iron and Steel, 2009, 44(9): 86-89

[15] PeranioN, LiY J, RotersF, RaabeD. Microstructure and texture evolution in dual-phase steels: Competition between recovery, recrystallization, and phase transformation [J]. Materials Science and Engineering A, 2010, 527: 4161-4168

[16] ChenH, GamsjägerE, SchiderS, KhanbarehH, van der ZwaagS. In situ observation of austenite-ferrite interface migration in a lean Mn steel during cyclic partial phase transformations [J]. Acta Materialia, 2013, 61: 2414-2424

[17] ZhaoX-m, KangY-l, HanQ-hang. Austenite isothermal transformation kinetics of a 1000 MPa grade cold rolled dual phase steel [J]. Transactions of Materials and Heat Treatment, 2013, 34: 53-59

[18] KuangS, KangY-l, YuH, LiuR-dong. Simulation of austenization during intercritical annealing for Fe-C-Mn cold rolling dual phase steel [J]. Journal of University of Science and Technology Beijing, 2008, 8: 858-863

[19] YongQ-l, LiY-f, ZhaoK-yu. Isothermal transformation kinetics time exponent versus nucleation and growth mechanisms [J]. Journal of Yunnan Institute of Technology, 1990, 6(3): 1-8

[20] FarjasJ, RouraP. Modification of the Kolmogorov-Johnson-Mehl-Avrami rate equation for non-isothermal experiments and its analytical solution [J]. Acta Materialia, 2006, 54: 5573-5579

[21] HillertM, AgrenJ. On the definitions of paraequilibrium and orthoequilibrium [J]. Scripta Materialia, 2004, 50: 697-699

[22] SunS, PughM. Manganese partitioning in dual-phase steel during annealing [J]. Materials Science and Engineering A, 2000, 276: 167-174