Effects of process parameters and die geometry on longitudinal welds quality in aluminum porthole die extrusion process

Abstract

By using the rigid-visco-plasticity finite element method, the welding process of aluminum porthole die extrusion to form a tube was simulated based on Deform-3D software. The welding chamber height (H), back dimension of die leg (D), process velocity and initial billet temperature were used in FE simulations so as to determine the conditions in which better longitudinal welding quality can be obtained. According to K criterion, the local welding parameters such as welding pressure, effective stress and welding path length on the welding plane are linked to longitudinal welds quality. Simulation turns out that pressure-to-effective stress ratio (p/σ) and welding path length (L) are the key factors affecting the welding quality. Higher welding chamber best and sharper die leg give better welding quality. When H=10 mm and D=0.4 mm, the longitudinal welds have the best quality. Higher process velocity decreases welds quality. The proper velocity is 10 mm/s for this simulation. In a certain range, higher temperature is beneficial to the longitudinal welds. It is found that both 450 and 465 °C can satisfy the requirements of the longitudinal welds.

Keywords

aluminum alloy / longitudinal welds / porthole die / die geometry / extrusion process / K criterion

References

[1] DonatiL., TomesaniL., MinakG.. Characterization of seam weld quality in AA6082 extruded profiles [J]. Journal of Materials Processing Technology, 2007, 191: 127-131

[2] KimK. J., LeeC. H., YangD. Y.. Investigation into the improvement of welding strength in three-dimensional extrusion of tubes using porthole dies [J]. Journal of Materials Processing Technology, 2002, 130/131: 426-431

[3] AkeretR.. Properties of pressure welds in extruded aluminum alloy sections [J]. Journal of the Institute of Metals, 1972, 10: 202-210

[4] AKERET R. Extrusion welds-quality aspects are now center stage [C]// Proceedings of the Fifth International Aluminum Extrusion Technology Seminar. Chicago, ET, 1992: 319–336.

[5] PLATA M, PIWNIK J. Theoretical and experimental analysis of seam weld formation in hot extrusion of aluminum alloys [C]// Proceedings of the Seventh International Aluminum Extrusion Technology Seminar. Chicago, ET: 2000: 205–211.

[6] DonatiL., TomesaniL.. The prediction of seam welds quality in aluminum extrusion [J]. Journal of Material Processing Technology, 2004, 153/154: 366-373

[7] ValbergH.. Extrusion welding in aluminium extrusion [J]. Materials and Product Technology, 2002, 17(7): 497-556

[8] ValbergH., LoekenT., HvalM.. The extrusion of hollow profiles with a gas pocket behind the bridge [J]. Materials and Product Technology, 1995, 10(3/6): 222-267

[9] FangG., ZhouJ., DuszczykJ.. Extrusion of 7075 aluminium alloy through double-pocket dies to manufacture a complex profile [J]. Journal of Materials Processing Technology, 2009, 209: 3050-3059

[10] LiuG., ZhouJ., DuszczykJ.. FE analysis of metal flow and weld seam formation in a porthole die during the extrusion of a magnesium alloy into a square tube and the effect of ram speed on weld strength [J]. Journal of Materials Processing Technology, 2008, 200: 185-198

[11] LiL., ZhangH., ZhouJ., LiG. Y., ZhongZ. H.. Numerical and experimental study on the extrusion through a porthole die to produce a hollow magnesium profile with longitudinal weld seams [J]. Materials and Design, 2008, 29: 1190-1198

[12] DonatiL., TomesaniL.. The effect of die design on the production and seam weld quality of extruded aluminum profiles [J]. Journal of Materials Processing Technology, 2005, 164/165: 1025-1031

[13] BuffaG., DonatiL., FratiniL., TomesaniL.. Solid state bonding in extrusion and FSW: Process mechanics and analogies [J]. Journal of Materials Processing Technology, 2006, 177: 344-347

[14] ChenJ.-chun.Production and control of the welding mark at aluminium extrusion [D], 2006, Shenyang, Northeastern University

[15] JoH. H., JeongC. S., LeeS. K., KimB. M.. Determination of welding pressure in the non-steady-state porthole die extrusion of improved Al7003 hollow section tubes [J]. Journal of Materials Processing Technology, 2003, 139: 428-433

[16] JoH. H., LeeS. K., JungC. S., KimB. M.. A non-steady state FE analysis of Al tubes hot extrusion by a porthole die [J]. Journal of Materials Processing Technology, 2006, 173: 223-231