Catalytic graphitization of polyacrylonitrile-based carbon fibers coated with Prussian blue

Abstract

Prussian blue (PB) was used as catalyst to improve the extent of graphitization of polyacrylonitrile (PAN)-based carbon fibers. PB was deposited on carbon fibers by anodic electrodeposition and the thickness of PB coating (PB content) was controlled by adjusting the electrodeposition time. PAN-based carbon fibers with PB coating were heat-treated and the extent of graphitization was measured by X-ray diffractometry and Raman spectroscopy. The results indicate that the extent of graphitization of PAN-based carbon fibers is enhanced in the presence of the coating. When the PB-coated carbon fibers were heat-treated at 1 900 °C, interlayer spacing (d₀₀₂) and crystallite size (L_c) reach 0.336 8 and 21.2 nm respectively. Contrarily, the values of d₀₀₂ and L_c are 0.341 4 and 7.4 nm respectively when the bare carbon fibers were heat-treated at 2 800 °C. Compared with the bare carbon fibers, PB can make the heat treatment temperature (HTT) drop more than 500 °C in order to reach the same extent of graphitization. Furthermore, the research results show that PB content also has a certain influence on the extent of graphitization at the same HTT.

Keywords

carbon fibers / Prussian blue / extent of graphitization / catalyst / heat treatment / coating

References

[1] YiS.-j., FanZ., WuC., ChenJ.-hua.. Catalytic graphitization of furan resin carbon by yttrium [J]. Carbon, 2008, 46(2): 378-380

[2] XuB.-s., ZhangC.-y., YangY.-z., LiuX.-g., LuoQ.-ping.. FeCl₃-catalyzed growth of vapor-grown carbon fibers from deoiled asphalt [J]. New Carbon Mater, 2007, 22(3): 193-198

[3] FanN., MaX.-c., LiuX.-z., XuL.-q., QianY.-tai.. The formation of a layer of Fe₃O₄ nanoplates between two carbon films [J]. Carbon, 2007, 45(9): 1839-1846

[4] AntonR.. In situ TEM investigations of reactions of Ni, Fe and Fe-Ni alloy particles and their oxides with amorphous carbon [J]. Carbon, 2009, 47(3): 856-865

[5] DhakateS. R., MathurR. B., BahlO. P.. Catalytic effect of iron oxide on carbon/carbon composites during graphitization [J]. Carbon, 1997, 35(12): 1753-1756

[6] DerekF. L., ChengI. F.. Analysis of hydrogen peroxide and organic hydroperoxide via the electrocatalytic fenton reaction [J]. Microchemical Journal, 2009, 91(1): 78-81

[7] QiuJ.-d., DengM.-q., LiangR.-p., XiongMeng.. Ferrocene-modified multiwalled carbon nanotubes as building block for construction of reagentless enzyme-based biosensors [J]. Sensors and Actuators B, 2008, 135(1): 181-187

[8] ZhaoC.-z., WanL., JiangL., WangQ., JiaoKui.. Highly sensitive and selective cholesterol biosensor based on direct electron transfer of hemoglobin [J]. Analytical Biochemistry, 2008, 383(1): 25-30

[9] GaoP.-z., WuM.-j., LiB.-j., LiuY.-li.. Structure characterization and oxidation mechanism study of porous biomorphic carbon template derived from basswood [J]. Mater Res Bull, 2009, 44(3): 644-648

[10] GeraldA. Z., BerndS., NotburgaG., HerwigP., OskarP.. A reconsideration of the relationship between the crystallite size L_a of carbons determined by X-ray diffraction and Raman spectroscopy [J]. Carbon, 2006, 44(15): 3239-3246

[11] TzengS. S.. Catalytic graphitization of electroless Ni-P coated PAN-based carbon fibers [J]. Carbon, 2006, 44(10): 1986-1993

[12] IgnacioM. G., JoseV., JuanA. C., JoseL. G.. Differences between carbon nanofibers produced using Fe and Ni catalysts in a floating catalyst reactor [J]. Carbon, 2006, 44(8): 1572-1580