Exsolved nickel sites for methane decomposition to hydrogen and carbon

Abstract

Hydrogen production via catalytic decomposition of methane (CDM) offers a CO₂-free route for simultaneous hydrogen and solid carbon generation. However, practical implementation remains limited by catalyst deactivation, metal contamination in the carbon product, and inefficient post-reaction purification. In this work, Ni-promoted (La_0.75Ca_0.25)(Cr_0.5Mn_0.5)O_3-δ (Ni-LCCM) perovskite catalysts prepared via a nitrate-based route were evaluated for CDM. Under thermal CDM at 750 °C without pre-reduction, 050Ni-LCCM achieved a Ni-normalized carbon productivity of up to 11.53 g_C·g_Ni^-1. A non-monotonic dependence of intrinsic carbon productivity on Ni loading was observed, with local maxima for 050Ni-LCCM and 150Ni-LCCM. These two experimental compositions were represented by the 2Ni-LCCM and 6Ni-LCCM models in the density functional theory (DFT) calculations. The 2Ni-LCCM and 6Ni-LCCM models showed lower relative rate-limiting activation barriers than those of neighboring configurations. Together with structural characterization, these results suggest that methane decomposition activity is strongly influenced by local Ni configuration, Ni reducibility, and site accessibility rather than by total Ni loading alone. Carbon characterization showed the formation of predominantly nanocrystalline graphitic carbon, including mixed carbon nanostructures such as carbon nanotubes, carbon nanofibers, and carbon nano-onions. Post-reaction purification using 5 M HNO₃ reduced the residual inorganic content to 4.20% and 1.41% for carbon products from 050Ni-LCCM and 150Ni-LCCM, respectively, corresponding to thermogravimetric analysis (TGA)-based carbon contents of approximately 95.8% and 98.6%. Overall, the results demonstrate that Ni-LCCM is an effective catalyst system for CDM, in which composition-dependent Ni configurations influence intrinsic carbon productivity while enabling recovery of high-carbon-content solid products after mild acid treatment.

Keywords

Catalytic methane decomposition / Ni-LCCM perovskite catalyst / non-monotonic carbon productivity / density functional theory / carbon purification

References

[1] Ishaq H,Crawford C.A review on hydrogen production and utilization: Challenges and opportunities.Int J Hydrogen Energy2022;47:26238-64

[2] Hermesmann M.Green, turquoise, blue, or grey? Environmentally friendly hydrogen production in transforming energy systems.Prog Energy Combust Sci2022;90:100996

[3] Tong S,Zhang W,Chan SH.Optimization of methane catalytic decomposition in a fluidized bed reactor: a computational approach.Energy Convers Manag2023;297:117719

[4] Zainal BS,Mohamed H.Recent advancement and assessment of green hydrogen production technologies.Renew Sustain Energy Rev2024;189:113941

[5] Shokrollahi M,Ashrafi O,Khojasteh-salkuyeh Y.Methane pyrolysis as a potential game changer for hydrogen economy: techno-economic assessment and GHG emissions.Int J Hydrogen Energy2024;66:337-53

[6] Qian JX,Enakonda LR,Basset J.Methane decomposition to pure hydrogen and carbon nano materials: State-of-the-art and future perspectives.Int J Hydrogen Energy2020;45:15721-43

[7] Pinilla J,Lázaro M,Suelves I.Ni- and Fe-based catalysts for hydrogen and carbon nanofilament production by catalytic decomposition of methane in a rotary bed reactor.Fuel Process Technol2011;92:1480-8

[8] Lua AC.Decomposition of methane over unsupported porous nickel and alloy catalyst.Appl Catal B Environ2013;132-133:469-78

[9] Moghaddam AL,Fattahi M.Methane pyrolysis for hydrogen production: navigating the path to a net zero future.Energy Environ Sci2025;18:2747-90

[10] Sun E,Kim D.A semi-continuous process for co-production of CO₂-free hydrogen and carbon nanotubes via methane pyrolysis.Cell Rep Phys Sci2023;4:101338

[11] Bayat N,Rezaei M.Thermocatalytic decomposition of methane to CO_x-free hydrogen and carbon over Ni-Fe-Cu/Al₂O₃ catalysts.Int J Hydrogen Energy2016;41:13039-49

[12] Ahmad A,Srinivasakannan C,Hossain MM.Catalytic cracking of methane to hydrogen and carbon: scale-up perspective.Int J Hydrogen Energy2024;54:1212-30

[13] Ahmed H,Fakeeha AH.Hydrogen production via methane decomposition over alumina doped with titanium oxide-supported iron catalyst for various calcination temperatures.ChemistryOpen2024;13:e202300173

[14] Feng F,Xiao J,Pisupati SV.Carbon deposition on Ni-based catalyst with TiO₂ as additive during the syngas methanation process in a fluidized bed reactor.Fuel2019;235:85-91

[15] Busillo E,De Filippis P.Methane pyrolysis in molten media: the interplay of physical properties and catalytic activity on carbon and hydrogen production.J Anal Appl Pyrolysis2024;183:106752

[16] Sanyal A,Bandulasena H.Review of the production of turquoise hydrogen from methane catalytic decomposition: optimising reactors for sustainable hydrogen production.Int J Hydrogen Energy2024;72:694-715

[17] Polo-garzon F,Liu X.Understanding the impact of surface reconstruction of perovskite catalysts on CH₄ activation and combustion.ACS Catal2018;8:10306-15

[18] Neagu D,Miller DN,Irvine JT.In situ growth of nanoparticles through control of non-stoichiometry.Nat Chem2013;5:916-23

[19] Jardiel T,Moser F,Gauthier G.New SOFC electrode materials: the Ni-substituted LSCM-based compounds (La_0.75Sr_0.25)(Cr_0.5Mn_0.5-xNi_x)O_3-δ and (La_0.75Sr_0.25)(Cr_0.5-xNi_xMn_0.5)O_3-δ.Solid State Ionics2010;181:894-901

[20] Sun H,Huang X.Modification of LSCM structure by anchoring alloy nanoparticles for efficient CO₂ electrolysis.Energy Fuels2024;38:3436-44

[21] Neagu D,Miller DN.Nano-socketed nickel particles with enhanced coking resistance grown in situ by redox exsolution.Nat Commun2015;6:8120 PMCID:PMC4579408

[22] Yu J,Zhong M.Suppression of Sr segregation in La_0.6Sr_0.4Co_0.2Fe_0.8O_3-δ oxygen electrode via Ca doping for enhanced performance stability of reversible solid oxide cell.ACS Appl Mater Interfaces2026;18:11409-20

[23] Koo B,Kim JK,Han JW.Sr segregation in perovskite oxides: why it happens and how it exists.Joule2018;2:1476-99

[24] Zhang L,Poh CK.Catalytic decomposition of methane: Ni-promoted perovskite oxide catalysts for turquoise hydrogen and carbon nanomaterials Co-production.Energy Mater2025;5:500023

[25] Perdew JP,Ernzerhof M.Generalized gradient approximation made simple.Phys Rev Lett1996;77:3865-8

[26] Monkhorst HJ.Special points for Brillouin-zone integrations.Phys Rev B1976;13:5188-92

[27] Jónsson H,Jacobsen KW.Nudged elastic band method for finding minimum energy paths of transitions. In Classical and Quantum Dynamics in Condensed Phase Simulations, LERICI, Villa Marigola, July 7-18, 1997; Berne B. J.; Ciccotti, G.; Coker, D. F.; Eds.; World Scientific, 1997; pp 385-404

[28] Henkelman G,Jónsson H.A climbing image nudged elastic band method for finding saddle points and minimum energy paths.J Chem Phys2000;113:9901-4

[29] Vera E,Metaouaa J.Comparative study of exsolved and impregnated Ni nanoparticles supported on nanoporous perovskites for low-temperature CO oxidation.ACS Appl Mater Interfaces2024;16:7219-31

[30] Flores-lasluisa J,Cazorla-amorós D.LaNi_1-xCo_xO₃ perovskites for application in electrochemical reactions involving molecular oxygen.Energy2023;273:127256

[31] Khan UM,Anwar M.Synthesis of cobalt loaded double perovskite Sr₂TiFeO_6‐δ (STF) as a stable catalyst for enhanced hydrogen production via methane decomposition.Int J Energy Res2021;45:20073-88

[32] Rudolph B,Ehrhardt B.Nanoparticle exsolution from nanoporous perovskites for highly active and stable catalysts.Adv Sci2023;10:e2205890 PMCID:PMC9951582

[33] Piazzolla F,Figueiredo SS.Exsolution of Ni nanoparticles from La_0.4Sr_0.4Ti_0.8Ni_0.2O_3-δ perovskite for ethanol steam reforming.Catal Today2025;444:115011

[34] Qiao L.Direct observation of Ni³⁺ and Ni²⁺ in correlated LaNiO_3-δ films.EPL2011;93:57002

[35] Whitten A,Tezel E,Nikolla E.Deconvoluting XPS spectra of La-containing perovskites from first-principles.JACS Au2024;4:3104-17 PMCID:PMC11350717

[36] Barreau M,Zhang J.Uncovering the critical function of lanthanum in CH₄ production from CO₂ using exsolved LaNiO₃ perovskite catalysts.J Mater Chem A2024;12:7605-21

[37] Vargas NFC,Eiras JA,Lente MH.Sintering‐driven effects on the band gap of (Pb,La)(Ti,Ni)O₃ photovoltaic ceramics.J Am Ceram Soc2021;104:2600-9

[38] Sun Z,Cheng D.Reinforcing hydrogen and carbon nanotube co-production via Cr-O-Ni catalyzed methane decomposition.J Mater Chem A2024;12:4893-902

[39] Sunding M,Diplas S,Norby T.XPS characterisation of in situ treated lanthanum oxide and hydroxide using tailored charge referencing and peak fitting procedures.J Electron Spectrosc Relat Phenom2011;184:399-409

[40] Soltani N,Bahrami A.Structural changes in NiO-Ce_0.8Sm_0.2O_2-x anode under reducing atmosphere.Mater Charact2019;150:8-12

[41] Ning X,Zhang Z.Fermi level shifting, charge transfer and induced magnetic coupling at La_0.7Ca_0.3MnO₃/LaNiO₃ interface.Sci Rep2015;5:8460 PMCID:PMC4327574

[42] Hillebrecht FU,Bennett PA,Freiburg C.Electronic structure of Ni and Pd alloys. II. X-ray photoelectron core-level spectra.Phys Rev B1983;27:2179-93

[43] Cao P,Bekheet MF.Atomic-scale insights into nickel exsolution on LaNiO₃ catalysts via in situ electron microscopy.J Phys Chem C2022;126:786-96

[44] Wei Y,Hu Y.Controlling the cation exsolution of perovskite to customize heterostructure active site for oxygen evolution reaction.ACS Appl Mater Interfaces2022;14:25638-47

[45] Anjaneyulu C,Kumar VV,Rao TV.Influence of rare earth (La, Pr, Nd, Gd, and Sm) metals on the methane decomposition activity of Ni-Al catalysts.ACS Sustainable Chem Eng2015;3:1298-305

[46] Garbarino G,Riani P.Improvement of Ni/Al₂O₃ catalysts for low-temperature CO₂ methanation by vanadium and calcium oxide addition.Ind Eng Chem Res2021;60:6554-64

[47] Zhang T,Zhu Y.Dry reforming of methane on Ni-Fe-MgO catalysts: influence of Fe on carbon-resistant property and kinetics.Appl Catal B Environ2020;264:118497

[48] Osti A,Rizzato L,Glisenti A.Photothermal activation of methane dry reforming on perovskite-supported Ni-catalysts: impact of support composition and Ni loading method.Catal Today2025;449:115200

[49] Helveg S,Sehested J.Atomic-scale imaging of carbon nanofibre growth.Nature2004;427:426-9

[50] Bossert D,Maceroni M.A hydrofluoric acid-free method to dissolve and quantify silica nanoparticles in aqueous and solid matrices.Sci Rep2019;9:7938 PMCID:PMC6538650