Thermally induced urea-assisted porous precursor film for efficient planar inverted water-based perovskite solar cells

Abstract

Planar inverted water-based perovskite solar cells (PIW-PSCs) can be fabricated without toxic organic solvents. However, in the aqueous deposition route, organic ammonium salts (OAS) must penetrate the precursor film while simultaneously driving phase conversion. This deposition method results in slow and nonuniform conversion. Here, urea is used as a water-compatible additive that improves precursor wetting and promotes further development of the internal porous structure by the subsequent thermal treatment. The resulting porous precursor provides more accessible transport pathways for OAS, thereby promoting more complete conversion of Pb(NO₃)₂ into perovskite. Consequently, the resulting perovskite film exhibits enlarged grains, reduced defect density, and reduced residual compressive stress. The corresponding PIW-PSC achieves a champion power conversion efficiency (PCE) of 20.39%, while the PIW-PSC device shows stable power output for 20 min at a fixed bias corresponding to its maximum-power-point voltage. Unencapsulated PUS-L devices retain 84% of their initial PCE after approximately 1,000 h of ambient storage (30%-35% relative humidity, ~25 °C) and 68% after 450 h of thermal aging at 80 °C under N₂. This strategy combines the water compatibility, Pb²⁺ coordination, and thermally induced transformation of urea to regulate precursor-film morphology and facilitate OAS transport during the nitrate-to-halide conversion of Pb(NO₃)₂ precursors.

Keywords

Urea decomposition / heat treatment / porous precursor film / aqueous processing / conversion kinetics

References

[1] Zhou J,Liu Y.Highly efficient and stable perovskite solar cells via a multifunctional hole transporting material.Joule2024;8:1691-706

[2] Lin X,Luo X.Efficiency progress of inverted perovskite solar cells.Energy Environ Sci2020;13:3823-47

[3] Cao F,Li L.Pushing the certified efficiency of inverted perovskite solar cells beyond 24%: a review.Rev Mater Res2025;1:100020

[4] Song S,Kim H,Kim G.Perovskite solar cells for low earth orbit space applications.Energy Mater2026;6:600019

[5] Galvao J,Tilley M,Duchen MR.Unexpected low-dose toxicity of the universal solvent DMSO.FASEB J2014;28:1317-30

[6] Lee KP,Culik R,Schneider PW.Toxicity of N-methyl-2-pyrrolidone (NMP): teratogenic, subchronic, and two-year inhalation studies.Fundam Appl Toxicol1987;9:222-35

[7] Hsieh TY,Wu KL,Miyasaka T.Efficient perovskite solar cells fabricated using an aqueous lead nitrate precursor.Chem Commun2015;51:13294-7

[8] Hsieh T,Ikegami M,Miyasaka T.Stable and efficient perovskite solar cells fabricated using aqueous lead nitrate precursor: interpretation of the conversion mechanism and renovation of the sequential deposition.Mater Today Energy2019;14:100125

[9] Irshad Z,Lee JK.Efficient planar heterojunction inverted perovskite solar cells with perovskite materials deposited using an aqueous non-halide lead precursor.Bulletin Korean Chem Soc2020;41:937-42

[10] Du C,Miao X.Polyvinylpyrrolidone as additive for perovskite solar cells with water and isopropanol as solvents.Beilstein J Nanotechnol2019;10:2374-82 PMCID:PMC6902891

[11] Zhai P,Zhang Y.Performance-limiting formation kinetics in green water-processed perovskite solar cells.Energy Environ Sci2023;16:3014-24

[12] Hoang MT,Yang Y.Lead (II) fluoride additive modulating grains growth of water-processed metal halide perovskites for enhanced efficiency in solar cells.Mater Futures2025;4:025103

[13] Zhai P,Li S,Li D.Light modulation strategy for highest-efficiency water-processed perovskite solar cells.Matter2022;5:4450-66

[14] Zhang Y,Zhai P.The synergistic effect of dry air and surfactants enables water to be a promising green solvent for stable and efficient perovskite solar cells.Energy Environ Sci2024;17:296-306

[15] Dai Z,Li M.Thermally assisted energy barrier engineering for high-performance planar inverted perovskite solar cells processed with aqueous green solvents.J Alloys Compd2025;1035:181462

[16] Dai Z,Jiang Z.How to construct efficient planar inverted aqueous-based perovskite solar cells using NiO_x hole transport layers?.ACS Sustainable Chem Eng2025;13:22005-15

[17] Huang Z,Ma Z.Lead iodide secondary growth and π-π stack regulation for sequential perovskite solar cells with 23.62% efficiency.Che Eng J2024;499:156684

[18] Zhang W,Zhou Y.Multiple roles of negative thermal expansion material for high-performance fully-air processed perovskite solar cells.Chem Eng J2023;457:141216

[19] Bu T,Li H.Lead halide-templated crystallization of methylamine-free perovskite for efficient photovoltaic modules.Science2021;372:1327-32

[20] Vijayan S,Prabhakaran K.A urea crystal templating method for the preparation of porous alumina ceramics with the aligned pores.J Eur Ceram Soc2013;33:1929-34

[21] Xiao W,Yin X.Effect of urea as pore-forming agent on properties of poly(vinylidene fluoride-co-hexafluoropropylene)-based gel polymer electrolyte.J Power Sources2014;252:14-20

[22] Li Y,Ding K.Localized lead-chelating insulator bottom contact for efficient and stable p-i-n perovskite solar cells.Adv Sci2025;12:e09816

[23] Porwal S,Ghosh S.Stress-induced stabilization of the photoactive FAPbI₃ phase under ambient conditions without using an additive approach.Energy Adv2024;3:894-903

[24] Feng Z,Si J.Multi-site lead passivation via spatial configuration modulation of additives for efficient perovskite solar cells.Adv Energy Mater2025;15:2502409

[25] Guo F,Wang X.Carbonyl-amine synergistic dual-site passivation for efficient and stable wide-bandgap perovskite solar cells.Adv Funct Mater2026;36:e00017

[26] Mukherjee C,Bhanumati S.Comparative study of ionic interactions of 1:1 and 1:2 electrolytes of nitrates salts solutions with water analysed with physicochemical data.Phys Chem Liq2012;50:617-29

[27] Frank HS.Structural approach to the solvent power of water for hydrocarbons; urea as a structure breaker.J Chem Phys1968;48:4746-57

[28] Zuo C,Dong H.Regulating solution spreading and intermediate phase evolution for large-area perovskite films and solar modules.Energy Environ Sci2025;18:10125-34

[29] Mo C,Chen J,Qiu C.Thermal decomposition process of urea in SCR system for diesel engine.J Combust Sci Technol2021;27:16-22https://jglobal.jst.go.jp/en/detail?JGLOBAL_ID=202102245927979018 (accessed 2026-09-09).

[30] Krum K,Christensen H.Kinetic modeling of urea decomposition and byproduct formation.Chem Eng Sci2021;230:116138

[31] Pothiklang C,Ruankham P.Synthesis of perovskite film by using lead nitrate as precursor for perovskite solar cell applications.Mater Today Proc2019;17:1224-30

[32] Ko H,Kim M.Predicting the morphology of perovskite thin films produced by sequential deposition method: a crystal growth dynamics study.Chem Mater2017;29:1165-74

[33] Ummadisingu A.Revealing the detailed path of sequential deposition for metal halide perovskite formation.Sci Adv2018;4:e1701402 PMCID:PMC5804582

[34] Khawam A.Solid-state kinetic models: basics and mathematical fundamentals.J Phys Chem B2006;110:17315-28

[35] Mrkyvkova N,Nádaždy P.Combined in situ photoluminescence and X-ray scattering reveals defect formation in lead-halide perovskite films.J Phys Chem Lett2021;12:10156-62

[36] Khan JI,Ugur E.Charge carrier recombination at perovskite/hole transport layer interfaces monitored by time-resolved spectroscopy.ACS Energy Lett2021;6:4155-64

[37] Yoon SJ,Kamat PV.How lead halide complex chemistry dictates the composition of mixed halide perovskites.J Phys Chem Lett2016;7:1368-73

[38] Huang T,Nuryyeva S.Performance-limiting formation dynamics in mixed-halide perovskites.Sci Adv2021;7:eabj1799 PMCID:PMC8580316

[39] Pool VL,Van Campen DG.Thermal engineering of FAPbI₃ perovskite material via radiative thermal annealing and in situ XRD.Nat Commun2017;8:14075 PMCID:PMC5247577

[40] Wang X,Gao F.In situ study of purified phase transition path for α-FAPbI₃ crystallization.Adv Energy Mater2024;14:2303949

[41] Shi B,Sunli Z.Halogen anion pre-homogenization of sequentially deposited wide bandgap perovskites for commercial textured perovskite/silicon tandem solar cells.Energy Environ Sci2025;18:6297-306

[42] He Z,Kou T.Decoupling photoinduced lattice evolution via grain spatial isolation for perovskite solar cells.Adv Mater2026;38:e11062

[43] Duan H,Liu X.Electron-donor/-acceptor ratio-guided molecular engineering for buried interface optimization in n-i-p perovskite solar cells.Energy Mater2026;6

[44] Zhang Z,Wu Z.Revealing bifunctional molecules induced adequate DMSO extraction in sequential crystallization toward efficient and robust flexible perovskite solar cells.Adv Funct Materials2026;36:e22596

[45] Sun X,Li X.Engineering the ligand reactivity through tailored electron-withdrawing effects for outdoor-stable perovskite solar cells and modules.Adv Energy Mater2026;16:e04572