Phosphate-tolerant PtCo alloys enabled by sulfur-doped carbon encapsulation for ultra-low-Pt-loading HT-PEMFCs

Abstract

High-temperature proton exchange membrane fuel cells (HT-PEMFCs) have garnered considerable interest owing to their superior tolerance toward CO impurities and the inherent advantages of facile water management. However, severe phosphoric acid poisoning of Pt catalysts necessitates markedly higher Pt loadings than in low-temperature proton exchange membrane fuel cells, thereby constraining their large-scale deployment. Herein, we present an additive-assisted impregnation approach to synthesize ultrafine PtCo alloy nanoparticles encapsulated by defect-rich S-doped carbon encapsulation layers (CELs). The use of short-chain sodium thioglycolate enables the formation of ultrafine PtCo nanoparticles (~2.82 nm) coated with ~0.4 nm-thick CELs, effectively suppressing metal sintering during high-temperature annealing and strengthening metal-support interactions. The S-doped CELs provide dual protection against phosphoric acid poisoning by physically isolating the PtCo alloys and introducing negatively charged carbon defects to electrostatically repel phosphate anions. Consequently, the optimized sodium thioglycolate-PtCo alloy electrocatalyst delivers a high mass activity of 0.695 A mg_Pt^-1 at 0.85 V along with enhanced durability in 0.1 M H₃PO₄ at 80 °C. It further maintains excellent phosphate tolerance and oxygen reduction reaction activity, even in concentrated 85 wt% H₃PO₄ at 120 °C. Remarkably, in HT-PEMFCs, it achieves superior peak power densities of 613 and 908 mW cm^-2 in H₂-air and H₂-O₂, respectively, with a low Pt loading of 0.3 mg_Pt cm^-2. Even at an ultra-low Pt loading of 0.1 mg_Pt cm^-2, it delivers a peak power density of 355 mW cm^-2 and an exceptional Pt-specific power density of 3.53 kW g_Pt^-1 in H₂-air cell, while sustaining stable operation over 100 h with minimal voltage decay. This study offers a versatile strategy to develop phosphate-resistant catalysts for high-performance HT-PEMFCs with low-Pt-loading.

Keywords

HT-PEMFCs / additive-assisted impregnation approach / carbon encapsulation layer / phosphoric acid poisoning / ultra-low Pt loading / S-doping

References

[1] Peng B,Sementa L.Embedded oxide clusters stabilize sub-2 nm Pt nanoparticles for highly durable fuel cells.Nat Catal2024;7:818-28

[2] Liu E.Tunable layered Mn oxides for oxygen electrocatalysis.Nat Catal2024;7:469-71

[3] Lee S,Jo Y.Self-assembled network polymer electrolyte membranes for application in fuel cells at 250 °C.Nat Energy2024;9:849-61

[4] Huang G,Li Y.Lattice hydrogen boosts CO tolerance of Pd anode catalysts in high-temperature proton exchange membrane fuel cells.Adv Funct Mater2025;35:2415358

[5] Liu S,Rahim Y.Influence of operating conditions on the degradation mechanism in high-temperature polymer electrolyte fuel cells.J Power Sources2019;439:227090

[6] Tang H,Wu L.Fuel cells with an operational range of -20 °C to 200 °C enabled by phosphoric acid-doped intrinsically ultramicroporous membranes.Nat Energy2022;7:153-62

[7] Zhang Z,Huang J.Uneven phosphoric acid interfaces with enhanced electrochemical performance for high-temperature polymer electrolyte fuel cells.Sci Ad2023;9:eade1194 PMCID:PMC9876549

[8] Xu C,Zheng Y.Performance enhancement from catalysts to membrane electrode assemblies for high-temperature proton exchange membrane fuel cells.Nano Energy2025;139:110931

[9] Haider R,Ma ZF.High temperature proton exchange membrane fuel cells: progress in advanced materials and key technologies.Chem Soc Rev2021;50:1138-87

[10] Yu J,Kim S.Active and stable PtP₂-based electrocatalysts solve the phosphate poisoning issue of high temperature fuel cells.J Mater Chem A2023;11:6413-27

[11] Wang S,Xv C.Performance failure mechanisms and mitigation strategies of high-temperature proton exchange membrane fuel cells.Prog Mater Sci2025;148:101389

[12] Li H,Wu W.Electrode binder design for high-power, low-Pt loading and durable high temperature fuel cells.Energy Environ Sci2024;17:3651-9

[13] Tang H,Aili D.Low Pt loading for high-performance fuel cell electrodes enabled by hydrogen-bonding microporous polymer binders.Nat Commun2022;13:7577 PMCID:PMC9732346

[14] Liang J,Lv H.Metal bond strength regulation enables large-scale synthesis of intermetallic nanocrystals for practical fuel cells.Nat Mater2024;23:1259-67

[15] Yan Y,Gilroy KD,Xia Y.Intermetallic nanocrystals: syntheses and catalytic applications.Adv Mater2017;29:1605997

[16] Li J.Intermetallic nanoparticles: synthetic control and their enhanced electrocatalysis.Acc Chem Res2019;52:2015-25

[17] Dai Y,Cao Z,Xia Y.The physical chemistry and materials science behind sinter-resistant catalysts.Chem Soc Rev2018;47:4314-31

[18] Li W,Liu T.Doping-modulated strain enhancing the phosphate tolerance on PtFe alloys for high-temperature proton exchange membrane fuel cells.Adv Funct Mater2022;32:2109244

[19] Hu Y,Zhao X.Combining structurally ordered intermetallics with N-doped carbon confinement for efficient and anti-poisoning electrocatalysis.Appl Catal B Environ2020;279:119370

[20] Chougule SS,Roy Chowdhury S.Antipoisoning catalysts for the selective oxygen reduction reaction at the interface between metal nanoparticles and the electrolyte.Carbon Energy2023;5:e293

[21] Huang G,Du S.Silica-facilitated proton transfer for high-temperature proton-exchange membrane fuel cells.Sci China Chem2021;64:2203-11

[22] Zhang D,Huang G.Defective g-C₃N₄ optimizes phosphate distribution in the catalytic layer and boosts the performance of high-temperature proton exchange membrane fuel cells.Sci China Mater2023;66:3468-74

[23] Zhang J,Luo L.Phosphoric acid sustained-release strategy boosting durability of high temperature proton exchange membrane fuel cells.Chem Eng J2025;518:164518

[24] Li G,Ji F,Wang X.Balancing proton and mass transfers in cathode catalyst layer of high-temperature proton exchange membrane fuel cell via gradient porous structure design.J Power Sources2024;593:233807

[25] Kwon SH,Kim H,Lee SG.Distribution characteristics of phosphoric acid and PTFE binder on Pt/C surfaces in high-temperature polymer electrolyte membrane fuel cells: molecular dynamics simulation approach.Int J Hydrogen Energy2021;46:17295-305

[26] Yoo TY,Kim S.Scalable production of an intermetallic Pt-Co electrocatalyst for high-power proton-exchange-membrane fuel cells.Energy Environ Sci2023;16:1146-54

[27] Sun T,Qiu C.B, N codoped and defect-rich nanocarbon material as a metal-free bifunctional electrocatalyst for oxygen reduction and evolution reactions.Adv Sci2018;5:1800036 PMCID:PMC6051395

[28] Jiang H,Hao J,Li W.N and P co-functionalized three-dimensional porous carbon networks as efficient metal-free electrocatalysts for oxygen reduction reaction.Carbon2017;122:64-73

[29] Xia L,Wu Y.Leveraging doping and defect engineering to modulate exciton dissociation in graphitic carbon nitride for photocatalytic elimination of marine oil spill.Chem Eng J2022;439:135668

[30] Yang CL,Yin P.Sulfur-anchoring synthesis of platinum intermetallic nanoparticle catalysts for fuel cells.Science2021;374:459-64

[31] Wan R,Wen J,Kang X.Pt-Co single atom alloy catalysts: accelerated water dissociation and hydrogen evolution by strain regulation.J Energy Chem2022;69:44-53

[32] Chen Y,Wu M.Enhancing oxygen reduction activity via tailoring microstrain in PdMo nanoalloy through repetitive hydrogen absorption-release.ACS Catal2024;14:9354-63

[33] Xiong Y,Zou L.N-doping induced tensile-strained Pt nanoparticles ensuring an excellent durability of the oxygen reduction reaction.J Catal2020;382:247-55

[34] Gan Z,Deng C,Huang B.Confinement of Pt NPs by hollow-porous-carbon-spheres via pore regulation with promoted activity and durability in the hydrogen evolution reaction.Nanoscale2021;13:18273-80

[35] Wan K,Wang J.Synergizing amino tethering and carbon shell confinement enables confinement synthesis of PtCo intermetallic catalysts for highly durable fuel cells.ACS Catal2024;14:10181-93

[36] Holzwarth U.The Scherrer equation versus the 'Debye-Scherrer equation'.Nat Nanotechnol2011;6:534

[37] Xie Y,Li Z.Unraveling the cause of strong metal-support interaction formation: disparities in metal nanoparticle anchoring mechanisms.Angew Chem Int Ed2025;64:e202505820

[38] Xu M,Tang H,Qiao B.Renaissance of strong metal-support interactions.J Am Chem Soc2024;146:2290-307

[39] Zhou M,Zhang N.Intrinsic carbon defects in nitrogen and sulfur doped porous carbon nanotubes accelerate oxygen reduction and sulfur reduction for electrochemical energy conversion and storage.ACS Appl Nano Mater2023;6:15147-58

[40] Li Z,Li B,Wang H.Construction of heteroatom-doped and three-dimensional graphene materials for the applications in supercapacitors: a review.J Energy Storage2021;44:103437

[41] Xiao W,Zhao Q,Yang X.Regulating electrocatalytic properties of oxygen reduction reaction via strong coupling effects between Co-NC sites and intermetallic Pt₃Co.Appl Catal B Environ Energy2024;346:123740

[42] Zeng Y,Li C.Regulating catalytic properties and thermal stability of Pt and PtCo intermetallic fuel-cell catalysts via strong coupling effects between single-metal site-rich carbon and Pt.J Am Chem Soc2023;145:17643-55

[43] Hu S,Tian N.A P-O functional group anchoring Pt - Co electrocatalyst for high-durability PEMFCs.Energy Environ Sci2024;17:3099-111

[44] Ye S,Ou Z.Harnessing the synergistic interplay between atomic-scale vacancies and ligand effect to optimize the oxygen reduction activity and tolerance performance.Angew Chem Int Ed2025;64:e202414989

[45] Bu L,Guo S.Biaxially strained PtPb/Pt core/shell nanoplate boosts oxygen reduction catalysis.Science2016;354:1410-4

[46] He Q,Nishijima M,Mukerjee S.Mitigating phosphate anion poisoning of cathodic Pt/C catalysts in phosphoric acid fuel cells.J Phys Chem C2013;117:4877-87

[47] He Q,Chen W,Koel B.Influence of phosphate anion adsorption on the kinetics of oxygen electroreduction on low index Pt(hkl) single crystals.Phys Chem Chem Phys2010;12:12544-55

[48] Lin H,Lim KH.High-temperature rotating disk electrode study of platinum bimetallic catalysts in phosphoric acid.ACS Catal2023;13:5635-42

[49] Lin L,Niu Y.H induced metal-insulation transition boosts the stability of high temperature polymer electrolyte membrane fuel cells.Angew Chem Int Ed2025;64:e202419919

[50] Chung YH,Jung N.Tailoring the electronic structure of nanoelectrocatalysts induced by a surface-capping organic molecule for the oxygen reduction reaction.J Phys Chem Lett2013;4:1304-9

[51] Wang L,Li Z.PAF-6 doped with phosphoric acid through alkaline nitrogen atoms boosting high-temperature proton-exchange membranes for high performance of fuel cells.Adv Mater2023;35:e2303535

[52] Hu Y,Pan C,Shypunov I.Immunity of the Fe-N-C catalysts to electrolyte adsorption: Phosphate but not perchloric anions.Appl Catal B Environ2018;234:357-64

[53] Park HY,Yoo SJ.Transition metal alloying effect on the phosphoric acid adsorption strength of Pt nanoparticles: an experimental and density functional theory study.Sci Rep2017;7:7186 PMCID:PMC5543171

[54] Yao D,Ma Q,Pasupathi S.Achieving high Pt utilization and superior performance of high temperature polymer electrolyte membrane fuel cell by employing low-Pt-content catalyst and microporous layer free electrode design.J Power Sources2019;426:124-33

[55] Su H,Barron O,Pasupathi S.Low platinum loading for high temperature proton exchange membrane fuel cell developed by ultrasonic spray coating technique.J Power Sources2014;267:155-9

[56] Martin S,Steenberg T.Binderless electrodes for high-temperature polymer electrolyte membrane fuel cells.J Power Sources2014;272:559-66

[57] Liang H,Pollet BG.Development of membrane electrode assembly for high temperature proton exchange membrane fuel cell by catalyst coating membrane method.J Power Sources2015;288:121-7

[58] Martin S,Jensen J.Lowering the platinum loading of high temperature polymer electrolyte membrane fuel cells with acid doped polybenzimidazole membranes.J Power Sources2015;293:51-6

[59] Liang H,Pollet BG,Pasupathi S.Membrane electrode assembly with enhanced platinum utilization for high temperature proton exchange membrane fuel cell prepared by catalyst coating membrane method.J Power Sources2014;266:107-13

[60] Su H,Bladergroen BJ,Pollet BG.Enhanced performance of polybenzimidazole-based high temperature proton exchange membrane fuel cell with gas diffusion electrodes prepared by automatic catalyst spraying under irradiation technique.J Power Sources2013;242:510-9

[61] Su H,Pasupathi S,Linkov V.A novel dual catalyst layer structured gas diffusion electrode for enhanced performance of high temperature proton exchange membrane fuel cell.J Power Sources2014;246:63-7

[62] Seselj N,Bompolaki E,Torres T.Catalyst development for high-temperature polymer electrolyte membrane fuel cell (HT-PEMFC) applications.Adv Mater2023;35:e2302207

[63] Chao G,Li R.Nitrogen heterocyclic polymers with different acidophilic properties as proton exchange membranes and binders for high-temperature fuel cells.J Membr Sci2024;692:122297

[64] Schmies H,Mueller-huelstede J.Reduction of platinum loading in gas diffusion electrodes for high temperature proton exchange membrane fuel cell application: Characterization and effect on oxygen reduction reaction performance.J Power Sources2022;529:231276

[65] Yuan H,Wei X.Internal polarization process revelation of electrochemical impedance spectroscopy of proton exchange membrane fuel cell by an impedance dimension model and distribution of relaxation times.Chem Eng J2021;418:129358

[66] Tian L,Xie Z.Enhanced performance and durability of high-temperature polymer electrolyte membrane fuel cell by incorporating covalent organic framework into catalyst layer.Acta Phys Chim Sin2020;37:2009049