Mesostructured Pt alloy nanotubes with synergistic edge sites as bifunctional electrocatalysts for direct ethanol fuel cells

Abstract

Direct ethanol fuel cells are considered indispensable and prospective energy storage devices due to their high volumetric energy density. Platinum (Pt) and Pt-based alloys are regarded as the most effective catalysts for both oxygen reduction reaction (ORR) and ethanol oxidation reaction. To further enhance the catalytic performance of the catalyst, it is necessary to improve the mass activity and utilization efficiency of Pt. In this work, we report a strategy for fabricating ordered mesostructured platinum-palladium alloy nanotubes (MPPNs) with high hierarchical porosity (68%) and abundant exposed active edge sites. MPPNs exhibit excellent catalytic activity and stability for ORR, with a mass activity approximately 7.4 times higher than that of the commercial Pt/C catalyst. After 20 k cycles of accelerated durability test for ORR, MPPNs demonstrate impressive retention of their original mass activity, maintaining a value of 93.9%. Furthermore, they display superior catalytic activity and stability for ethanol oxidation reactions, with a mass activity about 2.4 times higher than that of commercial Pt/C. After the 2,000 scan cycles, the mass activity remains at 84.5% of initial performance. Both experimental and theoretical studies reveal that the synergistic effect of neighboring (111) and (100) facets on the edge sites plays a critical role in enhancing the electrocatalytic selectivity, activity and stability.

Keywords

Mesoporous PtPd nanotubes / ethanol oxidation reaction / oxygen reduction reaction / bifunctional electrocatalysts / edge sites

References

[1] Chang J,Li C.Rational design of septenary high-entropy alloy for direct ethanol fuel cells.Joule2023;7:587-602

[2] Fuku X.Performance of BiCu₂O modified Pd/C as an anode electrocatalyst for direct ethanol fuel cell system.Catal Today2024;425:114305

[3] Fajardo S,Rodríguez J.Co supported on N and S dual-doped reduced graphene oxide as highly active oxygen-reduction catalyst for direct ethanol fuel cells.Chem Eng J2023;461:142053

[4] Ao W,Cheng C.Mesoporous PtPb nanosheets as efficient electrocatalysts for hydrogen evolution and ethanol oxidation.Angew Chem Int Ed2023;62:e202305158

[5] Xiao L,Yang Z.Engineering of amorphous PtO_x interface on Pt/WO₃ nanosheets for ethanol oxidation electrocatalysis.Adv Funct Mater2021;31:2100982

[6] Yoon YS,Kilic ME.Novel GaPtMnP alloy based anodic electrocatalyst with excellent catalytic features for direct ethanol fuel cells.Adv Funct Mater2022;32:2111272

[7] Wang Z,Liu S.Energy transfer-mediated multiphoton synergistic excitation for selective C(sp³)-H functionalization with coordination polymer.Nat Commun2024;15:8813 PMCID:PMC11470074

[8] Zhang Y,Liu T.Rhombohedral Pd-Sb nanoplates with Pd-terminated surface: an efficient bifunctional fuel-cell catalyst.Adv Mater2022;34:e2202333

[9] Wang H.Adsorbed enolate as the precursor for the C-C bond splitting during ethanol electrooxidation on Pt.J Am Chem Soc2023;145:6330-8

[10] Sun B,Ai X,Li F.Engineering low-coordination atoms on RhPt bimetallene for 12-electron ethanol electrooxidation.Energy Environ Sci2024;17:2219-27

[11] Kim KH,Steinberg KJ.Confinement effects of hollow structured Pt-Rh electrocatalysts toward complete ethanol electrooxidation.ACS Nano2023;17:14176-88

[12] Han C,Wang S.Noncovalent interactions on the electrocatalytic oxidation of ethanol on a Pt/C electrocatalyst.Carbon Energy2023;5:e339

[13] Liang C,Chen T.Recent approaches for cleaving the C-C bond during ethanol electro-oxidation reaction.Adv Sci2024;11:e2308958 PMCID:PMC11022732

[14] Peng K,Bhuvanendran N,Xu Q.Efficient one-dimensional Pt-based nanostructures for methanol oxidation reaction: an overview.Int J Hydrogen Energy2023;48:29497-517

[15] Yu R,Ning F.Electronic and geometric effects endow PtRh jagged nanowires with superior ethanol oxidation catalysis.Small2024;20:e2305817

[16] Wang Q,Deng P.Rhodium decorated stable platinum nickel nanowires for effective ethanol oxidation reaction.Sci China Mater2023;66:679-85

[17] Gao L,Chen X.Identifying the distinct roles of dual dopants in stabilizing the platinum-nickel nanowire catalyst for durable fuel cell.Nat Commun2024;15:508 PMCID:PMC10787824

[18] Zhao X,Yoshida Y.Roles of structural defects in polycrystalline platinum nanowires for enhanced oxygen reduction activity.Appl Catal B Environ2023;324:122268

[19] Zhou Z,Feng X,Ma Z.Progress of Pt and iron-group transition metal alloy catalysts with high ORR activity for PEMFCs.J Electroanalytical Chem2024;959:118165

[20] Liu X,Liang J.Inducing covalent atomic interaction in intermetallic Pt alloy nanocatalysts for high-performance fuel cells.Angew Chem Int Ed2023;62:e202302134

[21] Xia T,Zhu Y.Mixed-dimensional Pt-Ni alloy polyhedral nanochains as bifunctional electrocatalysts for direct methanol fuel cells.Adv Mater2023;35:e2206508

[22] Nie M,Luo L,Gan W.One-pot synthesis of ultrafine trimetallic PtPdCu alloy nanoparticles decorated on carbon nanotubes for bifunctional catalysis of ethanol oxidation and oxygen reduction.J Colloid Interface Sci2023;643:26-37

[23] Liu Y,Wu M.Controllable synthesis of PtIrCu ternary alloy ultrathin nanowires for enhanced ethanol electrooxidation.ACS Appl Mater Interfaces2023;15:3934-40

[24] Carvalho LL,Colmati F.Palladium-platinum electrocatalysts for the ethanol oxidation reaction: comparison of electrochemical activities in acid and alkaline media.J Solid State Electrochem2018;22:1471-81

[25] Qian K,Wei S.Synthesis of well-dispersed Pt-Pd nanoparticles stabilized by silsesquioxanes with enhanced catalytic activity for formic acid electrooxidation.J Solid State Electrochem2017;21:297-304

[26] Luo W,Fu C,Gao N.Preparation and characterization of porous sponge-like Pd@Pt nanotubes with high catalytic activity for ethanol oxidation.Mater Lett2016;173:43-6

[27] Zhang Y,Shang Z.Electronic and coordination effect of PtPd nanoflower alloys for the methanol electrooxidation reaction.ACS Sustain Chem Eng2023;11:8958-67

[28] Li B,Kaelin J.Carbon-supported and shape-controlled PtPd nanocrystal synthesis in flowing deep eutectic solvents for the methanol oxidation reaction.ACS Appl Nano Mater2023;6:3184-90

[29] Ding K,Yang H.Electrocatalytic activity of multi-walled carbon nanotubes-supported Pt_xPd_y catalysts prepared by a pyrolysis process toward ethanol oxidation reaction.Electrochim Acta2013;100:147-56

[30] Perdew JP,Ernzerhof M.Generalized gradient approximation made simple.Phys Rev Lett1996;77:3865-8

[31] Blöchl PE.Projector augmented-wave method.Phys Rev B Condens Matter1994;50:17953-79

[32] Lee Y,Kim D,Park K.Octahedral Pt-Pd alloy catalysts with enhanced oxygen reduction activity and stability in proton exchange membrane fuel cells.RSC Adv2012;2:1119-25

[33] Bai Z,Ming D,Xu H.High active and durable N-doped carbon spheres-supported flowerlike PtPd nanoparticles for electrochemical oxidation of liquid alcohols.Electrochim Acta2020;356:136794

[34] Ying J,Chen J.Fractal design of hierarchical PtPd with enhanced exposed surface atoms for highly catalytic activity and stability.Nano Lett2023;23:7371-8

[35] Cheng Y,Saunders M.Core-shell structured PtRuCo_x nanoparticles on carbon nanotubes as highly active and durable electrocatalysts for direct methanol fuel cells.Electrochim Acta2015;177:217-26

[36] Shao C,Zhang L.Boosting propane purification on Pt/ZrOSO₄ nanoflowers: insight into the roles of different sulfate species in synergy with Pt.Sep Purif Technol2023;304:122367

[37] Ho VT,Rick J,Hwang BJ.Nanostructured Ti_0.7Mo_0.3O₂ support enhances electron transfer to Pt: high-performance catalyst for oxygen reduction reaction.J Am Chem Soc2011;133:11716-24

[38] Ando F,Tanabe T.Enhancement of the oxygen reduction reaction activity of pt by tuning Its d-band center via transition metal oxide support interactions.ACS Catal2021;11:9317-32

[39] Li J,Bai R.Construction of Pd/Ni₂P-Ni foam nanosheet array electrode by in-situ phosphatization-electrodeposition strategy for synergistic electrocatalytic hydrodechlorination.Chem Eng J2022;435:134932

[40] Chen H,Lin W.Tuning interfacial electronic properties of palladium oxide on vacancy-abundant carbon nitride for low-temperature dehydrogenation.ACS Catal2021;11:6193-9

[41] Tian N,Sun SG,Wang ZL.Synthesis of tetrahexahedral platinum nanocrystals with high-index facets and high electro-oxidation activity.Science2007;316:732-5

[42] Xu X,Sun H.Synthesis of Pt-Ni alloy nanocrystals with high-index facets and enhanced electrocatalytic properties.Angew Chem Int Ed2014;53:12522-7

[43] Zhao ZL,Du H,An HM.Sub-15 nm Pd@PtCu concave octahedron with enriched atomic steps as enhanced oxygen reduction electrocatalyst.J Power Sources2019;434:226742

[44] Hu S,Ali A,Kang Shen P.Large-scale synthesis of porous Pt nanospheres/three-dimensional graphene hybrid materials as a highly active and stable electrocatalyst for oxygen reduction reaction.ChemistrySelect2021;6:2080-4

[45] Wang M,Wu X.Realizing efficient electrochemical overall water electrolysis through hierarchical CoP@NiCo-LDH nanohybrids.Nano Energy2023;114:108681

[46] Yang Y,He HL.Covalently connected Nb₄N_5-xO_x-MoS₂ heterocatalysts with desired electron density to boost hydrogen evolution.ACS Nano2020;14:4925-37

[47] He D,Li W.Active electron density modulation of Co₃O₄-based catalysts enhances their oxygen evolution performance.Angew Chem Int Ed2020;59:6929-35

[48] Luo S,Liao Y.A tensile-strained Pt-Rh single-atom alloy remarkably boosts ethanol oxidation.Adv Mater2021;33:e2008508