Fabrication and visible light photocatalytic activity of Co-doped ZnO nanorods

Abstract

Co-doped ZnO nanorods were prepared by electrochemical deposition method in aqueous solution. To study the as-grown samples, several characterizations were carried out. The scanning electron microscopy(SEM) images show that the samples present a rod-like shape with hexagonal cross sections and roughened surface. There is a slight shift for (002) diffraction peak of Co-doped ZnO nanorods in XRD because Co²⁺ ions entered into the ZnO lattice. Energy-dispersive X-ray spectroscopy(EDS) and X-ray photoelectron spectroscopy(XPS) results also show the exist of Co in the sample. Photoluminescence(PL) spectra of the samples were observed at room temperature, the UV emission of Co-doped ZnO shows a slight red shift compared with that of undoped ZnO. Thus, we can reach the conclusion that Zn²⁺ ions have been substituted by Co²⁺ ions in the ZnO samples. In addition, photocatalysis property of Co-doped ZnO nanorods was investigated under the irradiation of visible light. It was found that the degradation rate of methyl orange is increased greatly by Co-doped ZnO nanorods in comparison to undoped ZnO nanorods.

Keywords

Co-doped ZnO / Nanorod / Electrochemical deposition / Visible light / Photocatalysis

References

[1] Wang W, Yuan Q, Chi Y, Shao C L, Li N, Li X T. Chem. Res. Chinese Universities, 2012, 28(4): 727.

[2] Ji T H, Liu Y, Dong L Y, Han P, Sun J Y. Chem. Res. Chinese Universities, 2012, 28(4): 721.

[3] Jing L Q, Xin B F, Wang D J, Yuan F L, Fu H G, Sun C C. Chem. J. Chinese Universities, 2005, 26(1): 111.

[4] Xu Y D, Zhang Z Y, Kong J L, Li G D, Xiong H M. Chem. J. Chinese Universities, 2013, 34(7): 1565.

[5] Liu X J, Pan L K, Li J L, Yu K, Sun Z, Sun C Q. J. Colloid Interface Sci., 2013, 404: 150.

[6] Zhang Y Y, Mu J. J. Colloid Interface Sci., 2007, 309: 478.

[7] Khanchandani S, Kundu S, Patra A, Ganguli A K. J. Phys. Chem. C, 2013, 117: 5558.

[8] Zhao L, Xia M S, Liu Y H, Zheng B J, Jiang Q, Lian J S. Mater. Trans., 2012, 53: 463.

[9] Borgohain C, Senapati K K, Sarma K C, Phukan P. J. Mol. Catal. A: Chem., 2012, 363: 495.

[10] Jaramillo T S, Baeck S H B, Shwarsctein A K, McFarland E W. Macromol. Rapid Commun., 2004, 25: 297.

[11] Liu H R, Shao G X, Zhao J F, Zhang Z X, Zhang Y, Liang J, Liu X G, Jia H S, Xu B S. J. Phys. Chem. C, 2012, 116: 16182.

[12] Lin D D, Wu H, Zhang R, Pan W. Chem. Mater., 2009, 21: 3479.

[13] Muruganandham M, Chen I S, Wu J J. J. Hazard. Mater., 2009, 172: 700.

[14] Sarkar S, Makhal A, Bora T, Baruah S, Dutta J, Pal S K. Phys. Chem. Chem. Phys., 2011, 13: 12488.

[15] Zhao J, Zou X X, Su J, Wang P P, Zhou L J, Li G D. Dalton Trans., 2013, 42: 4365.

[16] Min Y L, Zhang K, Chen Y C, Zhang Y G, Zhao W. Sep. Purif. Technol., 2012, 92: 115.

[17] Yayapao O, Thongtem T, Phuruangrat A, Thongtem S. Mater. Lett., 2013, 90: 83.

[18] Wang G, Chen D, Zhang H, Zhang J Z, Li J H. J. Phys. Chem. C, 2008, 112: 8850.

[19] Li D, Haneda H. J. Photochem. Photobiol., A: Chem., 2003, 155: 171.

[20] Su J, Zou X X, Li G D, Wei X, Yan C, Wang Y N, Zhao J, Zhou L J, Chen J S. J. Phys. Chem. C, 2011, 115: 8064.

[21] Yayapao O, Thongtem S, Phuruangrat A, Thongtem T. Ceram. Int., 2013, 39: 563.

[22] Fang F, Zhao D X, Li B H, Zhang Z Z, Zhang J Y, Shen D Z. J. Appl. Phys. Lett., 2008, 93: 233115.

[23] Lee M, Yong K J. Nanotechnology, 2012, 23: 194014.

[24] Li D, Haneda H, Ohashi N, Saito N, Hishita S. Thin Solid Films, 2005, 486: 20.

[25] Lu Y C, Lin Y H, Wang D J, Wang L L, Xie T F, Jiang T F. Nano Res., 2011, 4: 1144.

[26] Cao P, Li B H, Zhang J Y, Zhao D X, Lü Y M, Yao B, Shen D Z, Fan X W. Chin. J. Lum., 2006, 27: 949.

[27] Xu C, Cao L X, Su G, Liu W, Qu X F, Yu Y Q. J. Alloys Compd., 2010, 497: 373.