Modeling the evolution of the deformation zone under various extrusion schemes

Abstract

Using the simulation results it was shown an optimal correlation of the size and porosity of powder compacts and also the amount of counterpressure recommended for the production of equal channel angular extrusion of workpieces with high-density of deformation zone that is large enough for subsequent direct extrusion powder of parts with high mechanical properties.The article defines the maximum depth of the cavity in direct extrusion through the research of plasticity resource. This paper describes the developed technology of manufacturing high-density parts of the "glass" type with the consistent application of the equalchannel angular and direct extrusion.

Keywords

powder compacts / equal channel angular extrusion / workpiece / direct extrusion / porosity / stress / deformation / counterpressure / density

References

[1] Евстратов В.А. Анализ процессов выдавливания с использованием модели вихревого течения / В.А. Евстратов, Г.А. Кротенко, В.Н. Левченко // Кузнечно-штамповочное производство. – 2010. – №4. – С. 3 – 10.

[2] Рябичева Л.А. К определению противодавления при прямом выдавливании порошковых пористых заготовок / Л.А. Рябичева, Д.А. Усатюк // Ресурсозберігаючі технології виробництва та обробки тиском матеріалів у машинобудуванні. – Луганськ: СНУ ім. В. Даля, 2012. №1 (13). – С. 211 – 219.

[3] Евстратов В.А. Принцип расширения очага пластической деформации/ В.А. Евстратов // Удосконалення процесів та обладнання обробки тиском в металургії і машинобудуванні: Зб. наук. пр. – Краматорськ, 2006. – С. 256 – 258.

[4] Штерн М.Б. Феноменологические теории прессования порошков / Штерн М.Б. [и др.] - К.: Наукова думка, 1982. – 140 с.

[5] Огородников В.А. Энергия. Деформации. Разрушение / В.А. Огородников, В.Б. Киселев, И.О. Сивак. – Винница: УНІВЕРСУМ – Вiнниця, 2005. –204 с.

RIGHTS & PERMISSIONS

Rjabicheva L.A., Usatjuk D.A.