Sustainable Lignin-Epoxy Compatibilizer Enables Synergistic Strengthening and Toughening in PBAT/PLA Blends

Abstract

Poly(butylene adipate-co-terephthalate) (PBAT) is a promising biodegradable polyester, but its low strength limits broader application. In principle, blending PBAT with polylactide (PLA) can combine toughness and stiffness, yet severe immiscibility usually leads to poor interfacial adhesion and unsatisfactory overall performance. Here, a bio-based lignin-epoxy composite compatibilizer (E-FL) was developed by premixing ethanol-fractionated lignin (FL) with a protocatechuic-acid-derived epoxy compound and introducing it into PBAT/PLA blends through reactive melt processing. Fractionation enriched lignin fractions with lower molecular weight and higher hydroxyl content, thereby improving reactivity and dispersibility. During melt blending, E-FL promoted interfacial reactions with PBAT and PLA end groups, increased melt torque and molecular weight, refined the dispersed PLA domains, and reduced the Tg gap between the two phases. At an E-FL loading of 3 wt%, the blend exhibited the best balance of performance, with a tensile strength of 36.1 MPa, an elongation at break of 1035%, and a fracture toughness of 238.3 MJ/m³. This work provides a sustainable strategy for converting lignin into a high-efficiency reactive compatibilizer and offers a practical route to high-performance PBAT-based biodegradable blends.

Keywords

Poly(butylene adipate-co-terephthalate) / Polylactide (PLA) / Lignin / Bio-based epoxy / Strengthening-toughening synergy

References

[1] Saxena P, Shukla P. A Green Approach to Sustainability: Biodegradable Polymers in Environmental and Energy Applications. ECS J. Solid State Sci. Technol. 2025, 14, 063005. DOI: 10.1149/2162—8777/ade341

[2] Wang J, Xu M, Yan J, Guo G, Wang Y, Zhang J, et al. Biodegradable poly(butylene adipate—co—terephthalate) (PBAT) modified by 1,4 cyclohexanedimethanol. Polymer 2024, 308, 127348. DOI: 10.1016/j.polymer.2024.127348

[3] Li W, Huang J, Liu W, Qiu X, Lou H, Zheng L . Lignin modified PBAT composites with enhanced strength based on interfacial dynamic bonds. J. Appl. Polym. Sci. 2022, 139, e52476. DOI: 10.1002/app.52476

[4] da Silva Pens CJ, Klug TV, Stoll L, Izidoro F, Flores SH, de Oliveira Rios A . Poly (lactic acid) and its improved properties by some modifications for food packaging applications: A review. Food Packag. Shelf Life 2024, 41, 101230. DOI: 10.1016/j.fpsl.2023.101230

[5] Venkatesan R, Mayakrishnan V, Alrashed MM, Kim S . Recent Advances in PBAT (Nano) Composite Materials for Food Packaging: A Comprehensive Review. J. Appl. Polym. Sci. 2025, 142, e57163. DOI: 10.1002/app.57163

[6] Yeh J, Tsou C, Huang C, Chen K, Wu C, Chai W . Compatible and Crystallization Properties of Poly(lactic acid)/Poly(butylene adipate—co—terephthalate) Blends. J. Appl. Polym. Sci. 2010, 116, 680-687. DOI: 10.1002/app.30907

[7] Su S. Prediction of the Miscibility of PBAT/PLA Blends. Polymers 2021, 13, 2339. DOI: 10.3390/polym13142339

[8] Bao RY, Jiang WR, Liu ZY, Yang W, Xie BH, Yang MB . Balanced strength and ductility improvement of in situcrosslinked polylactide/poly(ethylene terephthalate glycol) blends. RSC Adv. 2015, 5, 34821-34830. DOI: 10.1039/c5ra02575c

[9] Palsikowski PA, Kuchnier CN, Pinheiro IF, Morales AR . Biodegradation in Soil of PLA/PBAT Blends Compatibilized with Chain Extender. J. Polym. Environ. 2018, 26, 330-341. DOI: 10.1007/s10924—017—0951—3

[10] Arruda LC, Magaton M, Bretas RES, Ueki MM . Influence of chain extender on mechanical, thermal and morphological properties of blown films of PLA/PBAT blends. Polym. Test. 2015, 43, 27-37. DOI: 10.1016/j.polymertesting.2015.02.005

[11] Freitas ALPDL, Tonini Filho LR, Calvão PS, Souza AMCD . Effect of montmorillonite and chain extender on rheological, morphological and biodegradation behavior of PLA/PBAT blends. Polym. Test. 2017, 62, 189-195. DOI: 10.1016/j.polymertesting.2017.06.030

[12] Ma P, Cai X, Zhang Y, Wang S, Dong W, Chen M, et al. In— situcompatibilization of poly(lactic acid) and poly(butylene adipate—co—terephthalate) blends by using dicumyl peroxide as a free—radical initiator. Polym. Degrad. Stab. 2014, 102, 145-151. DOI: 10.1016/j.polymdegradstab.2014.01.025

[13] Kumar M, Mohanty S, Nayak SK, Rahail Parvaiz M . Effect of glycidyl methacrylate (GMA) on the thermal, mechanical and morphological property of biodegradable PLA/PBAT blend and its nanocomposites. Bioresour. Technol. 2010, 101, 8406-8415. DOI: 10.1016/j.biortech.2010.05.075

[14] Dong W, Zou B, Yan Y, Ma P, Chen M . Effect of Chain—Extenders on the Properties and Hydrolytic Degradation Behavior of the Poly(lactide)/Poly(butylene adipate—co—terephthalate) Blends. Int. J. Mol. Sci. 2013, 14, 20189-20203. DOI: 10.3390/ijms141020189

[15] Nunes EDD, de Souza AG, Rosa DD . Effect of the Joncryl® ADR Compatibilizing Agent in Blends of Poly(butylene adipate—co—terephthalate)/Poly(lactic acid). In Proceedings of the 14th Brazilian Congress on Polymers (CBPol), Aguas de Lindoia, Brazil, 22—26 October 2017.

[16] Sun C, Yu Z, Jia L, Zhang X, Zhao Y, Zhang Z . Lightweight and insulation polylactide/poly(butyleneadipate—co—terephthalate) foam with good cushioning performance prepared by supercritical CO₂. Ind. Crops Prod. 2025, 223, 120067. DOI: 10.1016/j.indcrop.2024.120067

[17] Mahdipour A, Golshan Ebrahimi N . Ultra—tough polylactic acid/poly(butylene adipate—co—terephthalate) blend for food packaging applications. J. Elastomers Plast. 2025, 57, 1387-1410. DOI: 10.1177/00952443251362821

[18] Han Y, Shi J, Mao L, Wang Z, Zhang L . Improvement of Compatibility and Mechanical Performances of PLA/PBAT Composites with Epoxidized Soybean Oil as Compatibilizer. Ind. Eng. Chem. Res. 2020, 59, 21779-21790. DOI: 10.1021/acs.iecr.0c04285

[19] Chen X, Hou J, Gu Q, Wang Q, Gao J, Sun J, et al. Corrigendum to “A non—bisphenol—a epoxy resin with high Tgderived from the bio—based protocatechuic acid: Synthesis and properties” [Polymer 195 (2020) 122443] . Polymer 2020, 205, 122726. DOI: 10.1016/j.polymer.2020.122726

[20] Chio C, Sain M, Qin W. Lignin utilization: A review of lignin depolymerization from various aspects. Renew. Sustain. Energy Rev. 2019, 107, 232-249. DOI: 10.1016/j.rser.2019.03.008

[21] Jiang ZH, Argyropoulos DS . Isolation and characterization of residual lignins in kraft pulps. J. Pulp Pap. Sci. 1999, 25, 25-29. Available online: https://pascal—francis.inist.fr/vibad/index.php?action=getRecordDetail&idt=1715976 (accessed on 1 January 2026)

[22] Smit AT, Dezaire T, Riddell LA, Bruijnincx PCA . Reductive Partial Depolymerization of Acetone Organosolv Lignin to Tailor Lignin Molar Mass, Dispersity, and Reactivity for Polymer Applications. ACS Sustain. Chem. Eng. 2023, 11, 6070-6080. DOI: 10.1021/acssuschemeng.3c00617

[23] Pang T, Wang G, Sun H, Sui W, Si C . Lignin fractionation: Effective strategy to reduce molecule weight dependent heterogeneity for upgraded lignin valorization. Ind. Crops Prod. 2021, 165, 113442. DOI: 10.1016/j.indcrop.2021.113442

[24] Gigli M, Crestini C . Fractionation of industrial lignins: opportunities and challenges. Green Chem. 2020, 22, 4722-4746. DOI: 10.1039/d0gc01606c

[25] Sadeghifar H, Wells T, Le RK, Sadeghifar F, Yuan JS, Jonas Ragauskas A. Fractionation of Organosolv Lignin Using Acetone: Water and Properties of the Obtained Fractions. ACS Sustain. Chem. Eng. 2017, 5, 580—587. DOI: 10.1021/acssuschemeng.6b01955

[26] Huang J, Wang H, Liu W, Huang J, Yang D, Qiu X, et al. Solvent—free synthesis of high—performance polyurethane elastomer based on low—molecular—weight alkali lignin. Int. J. Biol. Macromol. 2023, 225, 1505-1516. DOI: 10.1016/j.ijbiomac.2022.11.207

[27] Guo Y, Zuo X, Xue Y, Zhou Y, Yang Z, Chuang YC, et al. Correction to Enhancing Impact Resistance of Polymer Blends via Self—Assembled Nanoscale Interfacial Structures. Macromolecules 2018, 51, 3897—3910; Erratum in Macromolecules 2019, 52, 4785—4785. DOI: 10.1021/acs.macromol.9b01000

[28] Wang H, Wei B, Gu X, Lin T, Li Y . Determining the optimal molecular architecture for reactive splicing compatibilization: Toward a better understanding of reactive polymer processing. Polymer 2020, 208, 122948. DOI: 10.1016/j.polymer.2020.122948

[29] Ayan U, Nouranian S, Majdoub M, Al—Ostaz A, Ucak—Astarlioglu MG, Villacorta BS . Supertoughened Polylactic Acid/Polybutylene Adipate Terephthalate Blends Compatibilized with Ethylene—Methyl Acrylate—Glycidyl Methacrylate: Morphology and Mechanical Properties by the Response Surface Methodology. Acs Appl. Mater. Interfaces 2024, 16, 26833-26848. DOI: 10.1021/acsami.4c06452

[30] Zhang L, Goh SH, Lee SY . Miscibility and phase behavior of poly(D,L—lactide)/poly—(p—vinylphenol) blends. J. Appl. Polym. Sci. 1998, 70, 811-816. DOI: 10.1002/(SICI)1097—4628(19981024)70:4%3C811::AID—APP22%3E3.0.CO;2—Y