Failure Characteristics of Rock-like Mortar Specimens with Arc-shaped Flaws under Freezing-thaw Cycles and Uniaxial Compression

Abstract

To investigate the freeze-thaw (F-T) damages and failure characteristics of rock mass with arc-shaped joints in cold regions, three types of cement mortar specimens with different central angles and prefabricated arc-shaped flaws are subjected to uniaxial compressive tests under different F-T cycles. Experimental observations show that the uniaxial compressive strength of specimens are significantly influenced by F-T cycles and their failure modes are mainly affected by the central angle a of the prefabricated flaws. Unlike the specimens with a central angle of 60°, the specimens with a central angle of 120° and 180° have greater curvature of flaws, so tensile cracks occur in the arc-top area of their prefabricated flaws. According to experimental images observed by environmental scanning electron microscope (ESEM), as the number of F-T cycles increases, the deterioration effect of the specimen becomes more obvious, which is specifically reflected in the increase of the mass loss, peak stress loss, and damage variables as a power function, and the peak strain decreases as a quadratic polynomial. According to numerical results using two-dimensional particle flow code (PFC2D), it is found that F-T cycles cause more damage to the specimen in the early stages than in the later ones. The area of the concentrated compressive stress zone in the middle is decreased due to the increased number of F-T cycles, while the area of the surrounding tensile-shear stress zone is increased. The models appear different failure modes due to the release of concentrated stress in different tensile-shear zones.

Keywords

cement mortar material / arc-shaped flaws / freeze-thaw cycle / failure pattern / PFC2D

References

[1] Liu HY, Yuan XP, Xie TC. A Damage Model for Frost Heaving Pressure in Circular Rock Tunnel under Freezing-Thawing Cycles[J]. Tunn. Undergr. Sp. Technol., 2019, 83: 401-408

[2] Mimouni T, Dupray F, Laloui L. Estimating the Geothermal Potential of Heat-Exchanger Anchors on A Cut-and-Cover Tunnel[J]. Geothermics, 2014, 51: 380-387

[3] Lai JX, Qiu JL, Fan HB, et al. Freeze-proof Method and Test Verification of a Cold Region Tunnel Employing Electric Heat Tracing[J]. Tunn. Undergr. Sp. Technol., 2016, 60: 56-65

[4] Wang Y, Gao SH, Li CH, et al. Energy Dissipation and Damage Evolution for Dynamic Fracture of Marble Subjected to Freeze-Thaw and Multiple Level Compressive Fatigue Loading[J]. Int. J. Fatigue, 2021, 142: 105927

[5] Liu QS, Huang SB, Kang YS, et al. Numerical and Theoretical Studies on Frost Heaving Pressure in a Single Fracture of Frozen Rock Mass under Low Temperature[J]. Chinese J. Geotech. Eng., 2015, 37(9): 1 572-1 580

[6] Hori M, Morihiro H. Micromechanical Analysis on Deterioration due to Freezing and Thawing in Porous Brittle Materials[J]. Int. J. Eng. Sci., 1998, 36(4): 511-522

[7] Altindag R, Alyildiz IS, Onargan T. Mechanical Property Degradation of Ignimbrite Subjected to Recurrent Freeze-Thaw Cycles[J]. Int. J. Rock Mech. Min. Sci., 2004, 41(6): 1 023-1 028

[8] Rempel AW. Formation of Ice Lenses and Frost Heave[J]. J. Geophys. Res-Earth., 2007, 112(2): 1-17

[9] Bobet A, Einstein HH. Fracture Coalescence in Rock-Type Materials under Uniaxial and Biaxial Ompression[J]. Int. J. Rock Mech. Min. Sci., 1998, 35(7): 863-888

[10] Sagong M, Bobet A. Coalescence of Multiple Flaws in a Rock-Model Material in Uniaxial Compression[J]. Int. J. Rock Mech. Min. Sci., 2002, 39(2): 229-241

[11] Gehle C, Kutter HK. Breakage and Shear Behaviour of Intermittent Rock Joints[J]. Int. J. Rock Mech. Min. Sci., 2003, 40(5): 687-700

[12] Zhang SJ, Lai YM, Zhang XF, et al. Study on the Damage Propagation of Surrounding Rock From A Cold-Region Tunnel under Freeze-Thaw Cycle Condition[J]. Tunn. Undergr. Sp. Technol., 2004, 19(3): 295-302

[13] Yang YZ, Zhao YS, Ma HL, et al. The Mechanical Characteristics and Damage Model of Helan Mountain Rock based on Acoustic Emission[J]. J. Wuhan Univ. Technol. -Metal. Sci. Ed., 2021, 36(6): 845-864

[14] Ke B, Zhou KP, Deng HW, et al. NMR Pore Structure and Dynamic Characteristics of Sandstone Caused by Ambient Freeze-Thaw Action[J]. Shock Vib., 2017, 2017: 15-18

[15] Lu YN, Li XP, Chan A. Damage Constitutive Model of Single Flaw Sandstone under Freeze-Thaw and Load[J]. Cold Reg. Sci. Technol., 2019, 159: 20-28

[16] Fang W, Jiang N, Luo XD. Establishment of Damage Statistical Constitutive Model of Loaded Rock and Method for Determining Its Parameters under Freeze-Thaw Condition[J]. Cold Reg. Sci. Technol., 2019, 160: 31-38

[17] Li JL, Kaunda RB, Zhou KP. Experimental Investigations on the Effects of Ambient Freeze-Thaw Cycling on Dynamic Properties and Rock Pore Structure Deterioration of Sandstone[J]. Cold Reg. Sci. Technol., 2018, 154: 133-141

[18] Qu DX, Li DK, Li XP, et al. Damage Evolution Mechanism and Constitutive Model of Freeze-Thaw Yellow Sandstone in Acidic Environment[J]. Cold Reg. Sci. Technol., 2018, 155: 174-183

[19] Ma GW, Dong QQ, Fan LF, et al. An Investigation of Non-Straight Fissures Cracking under Uniaxial Compression[J]. Eng. Fract. Mech., 2018, 191: 300-310

[20] Wright JS. The Spalling of Overgrowths during Experimental Freeze-Thaw of a Quartz Sandstone as a Mechanism of Quartz Silt Production[J]. Micron, 2000, 31(6): 631-638

[21] Martínez-Martínez J, Benavente D, Gomez-Heras M, et al. Non-linear decay of Building Stones during Freeze-Thaw Weathering Processes[J]. Constr. Build. Mater., 2013, 38: 443-454

[22] Jin M, Jiang LH, Lu MT, et al. Characterization of Internal Damage of Concrete Subjected to Freeze-Thaw Cycles by Electrochemical Impedance Spectroscopy[J]. Constr. Build. Mater., 2017, 152: 702-707

[23] Ng K, Dai QL. Numerical Investigation of Internal Frost Damage of Digital Cement Paste Samples with Cohesive Zone Modeling and Sem Microstructure Characterization[J]. Constr. Build. Mater., 2014, 50: 266-275

[24] Mousavi SZ, Tavakoli H, Moarefvand P, et al. Assessing the Effect of Freezing-Thawing Cycles on the Results of the Triaxial Compressive Strength Test for Calc-Schist Rock[J]. Int. J. Rock Mech. Min. Sci., 2019, 123: 104090

[25] Fang Y, Qiao L, Chen X, et al. Experimental Study of Freezing-Thawing Cycles on Sandstone in Yungang Grottos[J]. Rock Soil Mech., 2014, 35(9): 2 433-2 442

[26] Yang SQ, Huang YH, Ranjith PG, et al. Discrete Element Modeling on the Crack Evolution Behavior of Brittle Sandstone Containing Three Fissures under Uniaxial Compression[J]. Acta Mech Sinica-PRC, 2015, 31: 871-889

[27] Yang SQ, Tian WL, Huang YH, et al. Experimental and Discrete Element Modeling on Cracking Behavior of Sandstone Containing a Single Oval Flaw under Uniaxial Compression[J]. Eng. Fract. Mech., 2018, 194: 154-174

[28] Ren JH, Tian ZH, Bu JW. Simulating Tensile and Compressive Failure Process of Concrete with A User-Defined Bonded-Particle Model[J]. Int. J. Concr. Struct. Mater., 2018, 12(6): 56

[29] Song ZY, Konietzky H, Herbst M. Three-dimensional Particle Model Based Numerical Simulation on Multi-Level Compressive Cyclic Loading of Concrete[J]. Constr. Build. Mater., 2019, 225: 661-677

[30] Lin H, Lei DX, Yong R, et al. Analytical and Numerical Analysis for Frost Heaving Stress Distribution within Rock Joints under Freezing and Thawing Cycles[J]. Environ. Earth Sci., 2020, 79(12): 1-17

[31] Si Z, Du XQ, Huang LZ, et al. Meso-scale Failure of Freezing-Thawing Damage of Concrete under Uniaxial Compression[J]. Appl. Sci., 2020, 10(4): 1 252

[32] Lawn B, Wilshaw R. Indentation Fracture: Principles and Applications[J]. J. Mater. Sci., 1975, 10(6): 1 049-1 081

[33] Wong LNY, Einstein HH. Systematic Evaluation of Cracking Behavior in Specimens Containing Single Flaws under Uniaxial Compression[J]. Int. J. Rock Mech. Min. Sci., 2009, 46(2): 239-249

[34] Cho N, Martin CD, Sego DC. A Clumped Particle Model for Rock[J]. Int. J. Rock Mech. Min. Sci., 2007, 44(7): 997-1 010

[35] Yoon J. Application Of Experimental Design and Optimization to Pfc Model Calibration in Uniaxial Compression Simulation[J]. Int. J. Rock Mech. Min. Sci., 2007, 44(6): 871-889