Enhanced Thermoelectric and Mechanical Properties of p-type Bi_0.5Sb_1.5Te₃ Bulk Alloys by Composite Electroless Plating with Ni&Cu

Abstract

In order to improve the thermoelectric and mechanical properties of p-type Bi₂Te₃ thermoelectric material, Bi_0.5Sb_1.5Te₃/Ni&Cu core/shell powders were electroless plated with the same content of Ni and different content of Cu, and then reduced by hydrogen, and finally sintered into bulk by spark plasma sintering. After composite electroless plating with Ni&Cu, for the bulk sample with 0.3 wt% Ni and 0.15 wt% Cu, the power factor rises significantly and the highest value increases from 25 to 33 µW·cm⁻¹·K⁻² at room temperature. Meanwhile, the thermal conductivity decreases to about 0.80 W·m⁻¹·K⁻¹ at 623 K. Therefore, the composite electroless plating with Ni&Cu can obviously improve the electrical and thermal transport performance of p-type Bi₂Te₃ based thermoelectric materials. Thus, the ZT value enhances significantly and the highest value increases over 3 times, from 0.35 to 1.16 at 473 K in Bi_0.5Sb_1.5Te₃ with 0.3 wt% Ni and 0.15 wt% Cu bulk sample. At the same time, the mechanical properties have also been improved after composite electroless plating with Ni&Cu.

Keywords

Bi₂Te₃ / electroless plating / thermoelectric properties / mechanical properties

References

[1] He J, Tritt T M. Advances in Thermoelectric Materials Research: Looking Back and Moving Forward[J]. Science, 2017, 357(6358): eaak9 997

[2] Leija J, Lucero C D. Thermoelectric Module[J]. International Journal of Innovations in Engineering and Science, 2018, 3(10): 2 456-3 463.

[3] Tesfaye F, Moroz M. An Overview of Advanced Chalcogenide Thermoelectric Materials and Their Applications[J]. Journal of Electronic Research and Application, 2018, 2(2): 28-41.

[4] Jiang W. Overview of Semiconductor Thermoelectric Power Generation Technology[C]. 5th International Conference on Energy Science and Applied Technology (Esat 2019), 2020

[5] Lee K H, Kim H S, Choo S S, et al. Improved Carrier Transport Properties by I-doping in N-type Cu_0.008Bi₂Te_2.7Se_0.3 Thermoelectric Alloys[J]. Scripta Materialia, 2020, 186: 357-361.

[6] El-Asfoury Mohamed S. Enhanced Thermoelectric Performance of Bi₈₅Sb₁₅-graphene Composite by Modulation Carrier Transport and Density of State Effective Mass[J]. Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics, 2018, 745: 331-340.

[7] Rabih A, Hwang J, Lin C C, et al. Ultralow Lattice Thermal Conductivity and Enhanced Thermoelectric Performance in SnTe:Ga Materials[J]. Chemistry of Materials, 2017, 29(2): 612-620.

[8] Zhao L D, Zhang B P, Li J F, et al. Thermoelectric and Bi₂Te₃ Fabricated by Mechanical Alloying and Spark Plasma Sintering[J]. Journal of Alloys and Compounds, 2008, 455(1): 259-264.

[9] Hong M, Chen Z G, Zou J. Fundamental and Progress of Bi₂Te₃-based Thermoelectric Materials[J]. Chinese Physics B, 2018, 27(4): 50-74.

[10] Dharmaiah P, Hong S J. Thermoelectric Properties of Bi₂Te₃ Nanocrystals with Diverse Morphologies Obtained via Modified Hydrothermal Method[J]. Journal of Electronic Materials, 2017, 46: 3 012-3 019.

[11] Wu F, Wang W, Hu X, et al. Thermoelectric Properties of I-doped N-type Bi₂Te₃-based Material Prepared by Hydrothermal and Subsequent Hot Pressing[J]. Progress in Natural Science: Materials International, 2017, 27(2): 203-207.

[12] Bolghanabadi N, Sajjadi S A, Babakhani A, et al. Effects of Synthesis Parameters and Thickness on Thermoelectric Properties of Bi₂Te₃ Fabricated Using Mechanical Alloying and Spark Plasma Sintering[J]. Journal of Electronic Materials, 2021, 50: 1 331-1 339.

[13] Izumi O. Electrochemistry of Electroless Plating[J]. Materials Science & Engineering A, 1991, 146: 33-49.

[14] Loto C A. Electroless Nickel Plating — A Review[J]. Silicon, 2016, 8(2): 177-186.

[15] Dai X, Yu Y, Zu F Q, et al. Effect of Chemical Plating with Ni Content on Thermoelectric and Mechanical Properties of p-type Bi_0.5Sb_0.15Te₃ Bulk Alloys[J]. Materials Science Forum, 2016, 847: 177-183.

[16] Dai X, Huang Z, Yu Y, et al. Effects of Electroless Plating with Cu Content on Thermoelectric and Mechanical Properties of p-type Bi_0.5Sb_0.15Te₃ Bulk Alloys[J]. Journal of Wuhan University of Technology-Mater. Sci. Ed., 2018, 33(4): 797-801.

[17] Zhu J, Luo M, Li M, et al. First-principles Study of Divalent IIA and Transition IIB Metals Doping into Cu₂O[J]. Journal of Wuhan University of Technology-Mater. Sci. Ed., 2015, 30(3): 458-462.

[18] Bhame S D, Pravarthana D, Prellier W, et al. Enhanced Thermoelectric Performance in Spark Plasma Textured Bulk N-type Bi₂Te_2.7Se_0.3 and P-type Bi_0.5Sb_1.5Te₃[J]. Applied Physics Letters, 2013, 102(21): 211 901.1-211 901.5.

[19] Samanta M, Pal K, Waghmare U V, et al. Intrinsically Low Thermal Conductivity and High Carrier Mobility in Dual Topological Quantum Material, N-type BiTe[J]. Angewandte Chemie International Edition, 2020, 59(12): 4 822-4 829.

[20] Dai X, Huang Z, Zu F. Enhanced Thermoelectric and Mechanical Properties of n-type Bi₂Te_2.7Se_0.3 Bulk Alloys by Electroless Plating with Cu[J]. Journal of Wuhan University of Technology-Mater. Sci. Ed., 2019, 34(4): 840-844.