Effect of PCEs with Different Functional Groups on the Performance of Cement Paste

Abstract

The adsorption behaviors and dispersing properties of polycarboxylate superplasticizer (PCE) with different functional groups were systematically analyzed to reveal the theory and methods of modifying PCE molecular structures and regulating PCE performances. By substituting carboxylic groups with sulfonic groups, ester groups or acylamino groups, respectively, modified PCEs with different functional groups were synthesized. Results show that introducing low amount of ester groups or sulfonic groups into the PCE molecules has no negative effects on the fluidity of cement paste, while introducing acylamino groups into PCE molecules significantly weakens the fluidity of cement paste. At low amount (when the molar ratio of sodium methallyl sulfonate to TPEG is lower than 0.4), the rapid adsorption of sulfonic groups onto the cement particles contributes to the high dispersing performance of the sulfonic group modified PCEs. When the substitution ratio of acrylic acid by sulfonic acid is higher than 0.4, the viscosity and the yield stress of cement paste increases sharply. Redundant sulfonic groups lead to the excessive charge density of the PCE, which contributes to the inhomogeneous adsorption on the cement grains and hence results in the decline of the dispersing performance. Substitution of carboxylic group by acylamino group or ester group slightly changes the viscosity as well as the yield stress of cement paste. Introducing sulfonic group into PCE molecule improves the adsorption behavior of PCEs, while introducing ester group or acylamino group into PCE depresses the adsorption properties.

Keywords

polycarboxylate superplasticizer / functional group / adsorption behavior / rheological properties / cement hydration