Mechanical Properties and ITZ Microstructure of Recycled Aggregate Concrete Using Carbonated Recycled Coarse Aggregate

Abstract

The effect of carbonation treatment and mixing method on the mechanical properties and interfacial transition zone (ITZ) properties of recycled aggregate concrete (RAC) was investigated. Properties of recycled concrete aggregate (RCA) were tested firstly. Then, five types of concretes were made and slump of fresh concrete was measured immediately after mixing. Compressive strength and splitting tensile strength of hardened concrete were measured at 28 d. Meanwhile, the microstructure of RAC was analyzed by backscattered electron (BSE) image. It was found that the water absorption ratio of carbonated recycled concrete aggregate (CRCA) was much lower when compared to the untreated RCA. Comparatively, the apparent density of CRCA was not significantly modified. The concrete strength results indicate that the mix CRAC-2 prepared with CRCA by adopting two-stage mixing approach shows the highest compressive strength value compared to the other mixes. The microstructural analysis demonstrate that the mix CRAC-2 has a much denser old ITZ than the untreated RAC because of the chemical reaction between CO₂ and the hydration products of RCA. This study confirms that the ITZ microstructure of RAC can be efficiently modified by carbonation treatment of RCA and encourages broadening the application of construction and demolition wastes.

Keywords

recycled aggregate concrete / compressive strength / interfacial transition zone / carbonation treatment / two-stage mixing approach / back scattered electron

References

[1] Xiao J Z, Li W G, Poon C S. Recent Studies on Mechanical Properties of Recycled Aggregate Concrete in China-A Review[J]. Science China Technological Sciences, 2012, 55(6): 1463-1480.

[2] Tabsh S W, Abdelfatah A S. Influence of Recycled Concrete Aggregates on Strength Properties of Concrete[J]. Constr. Build. Mater., 2009, 23: 1163.

[3] Du T, Li H Q, Wu X G, et al. The Compression-deformation Behavior of Concrete with Various Modified Recycled Aggregates[J]. Journal of Wuhan University of Technology-Mater. Sci. Ed., 2005, 20: 127-129.

[4] Li Q Y, Quan H, Qin Y. Performance and Application Technology of Recycled Concrete, 2010 Beijing: Chinese Building Materials Industry Publication.

[5] Kou S C, Poon C S. Properties of Concrete Prepared with PVA-impregnated Recycled Concrete Aggregates[J]. Cement Concrete Composite, 2010, 32(8): 649-654.

[6] Shi C, Li Y, Zhang J, et al. Performance Enhancement of Recycled Concrete Aggregate–A Review[J]. Journal of Cleaner Production, 2016, 112: 466-472.

[7] Kou S C, Zhan B J, Poon C S. Use of a CO₂ Curing Step to Improve the Properties of Concrete Prepared with Recycled Aggregates[J]. Cement and Concrete Composites, 2014, 45: 22-28.

[8] Zhang J, Shi C, Li Y, et al. Performance Enhancement of Recycled Concrete Aggregates through Carbonation[J]. Journal of Materials in Civil Engineering, 2015, 27(11): 04015029

[9] Zhang J, Shi C, Li Y, et al. Influence of Carbonated Recycled Concrete Aggregate on Properties of Cement Mortar[J]. Construction and Building Materials, 2015, 98: 1-7.

[10] Zhan B, Poon C S, Liu Q, et al. Experimental Study on CO₂ Curing for Enhancement of Recycled Aggregate Properties[J]. Construction and Building Materials, 2014, 67: 3-7.

[11] Thiery M, Villain G, Dangla P, et al. Investigation of the Carbonation Front Shape on Cementitious Materials: Effects of the Chemical Kinetics[J]. Cement Concrete Research, 2007, 37(7): 1047-1058.

[12] Tam VWY, Gao XF, Tam CM. Microstructural Analysis of Recycled Aggregate Concrete Produced from Two-stage Mixing Approach[J]. Cement Concrete Research, 2005, 35(6): 1195-1203.

[13] Standardization Committee of the People’s Republic of China. Pebble and Crushed Stone for Construction[S]. Beijing: Standards Press of China, 2011, GB14685-2011

[14] Lothenbach B, Durdzinski P, De Weerdt K. Chapter 5: Thermogravimetric Analysis. A Practical Guide to Microstructural Analysis of Cementitious Materials, 2015 Oxford: Taylor & Francis Group.

[15] Scrivener K, Bazzoni A, Mota B, et al. Chapter 8: Electron Microscopy. A Practical Guide to Microstructural Analysis of Cementitious Materials, 2015 Oxford: Taylor & Francis Group.

[16] Li W, Xiao J Z, Sun Z, et al. Interfacial Transition Zones in Recycled Aggregate Concrete with Different Mixing Approaches[J]. Construction and Building Materials, 2012, 35: 1045-1055.

[17] Leite M B, Monteiro P J M. Microstructural Analysis of Recycled Concrete Using X-ray Micro Tomography[J]. Cement and Concrete Research, 2016, 81: 38-48.

[18] Vivian W T, Tam CM, Wang Y. Optimization on Proportion for Recycled Aggregate in Concrete Using Two-stage Mixing Approach[J]. Construction and Building Materials, 2007, 21(10): 1928-1939.

[19] Zhan B, Poon C, Shi C. CO₂ Curing for Improving the Properties of Concrete Blocks Containing Recycled Aggregates[J]. Cement and Concrete Composites, 2013, 42: 1-8.

[20] Zhu P H, Zhang X X, Wu J Y, et al. Performance Degradation of the Repeated Recycled Aggregate Concrete with 70% Replacement of Three-generation Recycled Coarse Aggregate[J]. Journal of Wuhan University of Technology-Mater. Sci. Ed., 2016, 31(5): 989-995.

[21] Scrivener K L. The Interfacial Transition Zone (ITZ) between Cement Paste and Aggregate in Concrete[J]. Interface science, 2004, 12: 411-421.

[22] Guedes M, Evangelista L, De Brito J, et al. Microstructural Characterization of Concrete Prepared with Recycled Aggregates[J]. Microscopy and Microanalysis, 2013, 19(5): 1222-1230.