Cordierite Ceramics Prepared from Poor Quality Kaolin for Electric Heater Supports: Sintering Process, Phase Transformation, Microstructure Evolution and Properties

Abstract

To efficiently utilize the kaolin, an economical way of preparing cordierite ceramic with high performance for electric heater supports was put forward. In this study, sintering process, phase transformation, microstructure evolutions were systematically studied by heating microscope, X-ray diffraction, scanning electronic microscope and thermal analysis. Properties (physical properties, electrical properties and coefficient of thermal expansion (CTE)) were tested for comprehensive performance evaluation. The results showed that the utilization of poor quality kaolin broadened the firing range of cordierite ceramic which was from 1 200 to 1 380 °C. Microstructure becomes loose with increasing of the pore size, which had significant influence on bending strength and electrical properties. High content of K₂O in poor quality kaolin was the reason for liquid phase generation in sintering process, which further leads to microstructural changes. The cordierite ceramic sintered at 1 320 °C had the properties as follows: CTE of 1.98×10^-6 °C^-1 (500 °C), bending strength of 90 MPa, apparent porosity of 15.1%, dielectric constant of 7.5 (100 Hz), and volume resistivity of 1.05×10⁹ Ω·cm (100 Hz). The comprehensive properties are very suitable for use as electric heater supports.

Keywords

cordierite ceramic / poor quality kaolin / microstructure-final / electrical properties / electric heater supports

References

[1] Obradovic N, Filipovic S, Ðordevic N, et al. Effects of Mechanical Activation and Two-Step Sintering on the Structure and Electrical Properties of Cordierite-Based Ceramics[J]. Ceramics International, 2016, 42(12): 13909-13918.

[2] Acimovic Z, Pavlovic L, Trumbulovic L, et al. Synthesis and Characterization of the Cordierite Ceramics from Nonstandard Raw Materials for Application in Foundry[J]. Materials Letters, 2003, 57(18): 2651-2656.

[3] Bernier J C. Chemical Processing for Electronic Ceramics: a Challenge[J]. Materials Science & Engineering A, 1989, 109(2): 233-241.

[4] Kuscer D, Bantan I, Hrovat M, et al. The Microstructure, Coefficient of Thermal Expansion and Flexural Strength of Cordierite Ceramics Prepared from Alumina with Different Particle Sizes[J]. Journal of the European Ceramic Society, 2017, 37(2): 739-746.

[5] Naga S M, Sayed M, Elmaghraby H F, et al. Fabrication and Properties of Cordierite/Anorthite Composites[J]. Ceramics International, 2017, 43(8): 6024-6028.

[6] Miyake A. Effect of the Ionic Size on Thermal Expansion of Low Cordierite by Molecular Dynamics Simulation[J]. Journal of the American Ceramic Society, 2005, 88(1): 121-126.

[7] Shyam A, Lara-Curzio E, Pandey A, et al. The Thermal Expansion, Elastic and Fracture Properties of Porous Cordierite at Elevated Temperatures[J]. Journal of the American Ceramic Society, 2012, 95(5): 1682-1691.

[8] Sanad M M S, Rashad M M, Abdel-Aal E A, et al. Novel Cordierite Nanopowders of New Crystallization Aspects and Its Cordierite-Based Glass Ceramics of Improved Mechanical and Electrical Properties for Optimal Use in Multidisciplinary Scopes[J]. Materials Chemistry & Physics, 2015, 162: 299-307.

[9] Yamuna A, Johnson R, Mahajan Y R, et al. Kaolin-Based Cordierite for Pollution Control[J]. Journal of the European Ceramic Society, 2004, 24(1): 65-73.

[10] Fuji M, Shiroki Y, Menchavez R L, et al. Fabrication of Cordierite Filter by In-Situ Solidification for High Temperature Dust Collection[J]. Powder Technology, 2007, 172(1): 57-62.

[11] Jankovic-Castvan I, Lazarevic S, Jordovic B, et al. Electrical Properties of Cordierite Obtained by Non-hydrolytic Sol-Gel Method[J]. Journal of the European Ceramic Society, 2007, 27(13-15): 3659-3661.

[12] Malachevsky M T, Fiscina J E, Esparza D A. Preparation of Synthetic Cordierite by Solid-State Reaction via Bismuth Oxide Flux[J]. Journal of the American Ceramic Society, 2001, 84(7): 1575-1577.

[13] Ismail M G M U, Tsunatori H, Nakai Z. Preparation of Mullite Cordierite Composite Powders by the Sol-Gel Method: Its Characteristics and Sintering[J]. Journal of the American Ceramic Society, 1990, 73(3): 537-543.

[14] Xu X, Xu X, Wu J, et al. Fabrication and Characterization of Cordierite-Based Glass-Ceramic Adhesives for Bonding Solar Heat Transmission Pipelines[J]. Ceramics International, 2017, 43(1): 149-156.

[15] Banjuraizah J, Mohamad H, Ahmad Z A. Crystal Structure of Single Phase and Low Sintering Temperature of a-Cordierite Synthesized from Talc and Kaolin[J]. Journal of Alloys & Compounds, 2009, 482(1-2): 429-436.

[16] Xu X, Zhang Y, Wu J, et al. In Situ Synthesis of SiC-Bonded Cordierite-Mullite Ceramics for Solar Thermal Energy Storage[J]. Ceramics International, 2016, 42(15): 17503-17512.

[17] Oliveira F A C, Shohoji N, Fernandes J C, et al. Solar Sintering of Cordierite-based Ceramics at Low Temperatures[J]. Solar Energy, 2005, 78(3): 351-361.

[18] Kobayashi Y, Sumi K, Kato E. Preparation of Dense Cordierite Ceramics from Magnesium Compounds and Kaolinite without Additives[J]. Ceramics International, 2000, 26(26): 739-743.

[19] Shi Z M, Liang K M, Gu S R. Effects of CeO₂ on Phase Transformation towards Cordierite in MgO-Al₂O₃-SiO₂ System[J]. Materials Letters, 2001, 51(1): 68-72.

[20] Yalamaç E, Akkurt S. Additive and Intensive Grinding Effects on the Synthesis of Cordierite[J]. Ceramics International, 2006, 32(7): 825-832.

[21] Tang X, Guo L, Chen C, et al. The Analysis of Magnesium Oxide Hydration in Three-Phase Reaction System[J]. Journal of Solid State Chemistry, 2014, 213(5): 32-37.

[22] Lee S J, Kriven W M. Crystallization and Densification of Nano-Size Amorphous Cordierite Powder Prepared by a PVA Solution-Polymerization Route[J]. Journal of the American Ceramic Society, 1998, 81(10): 2605-2612.

[23] Zhang L, Olhero S, Ferreira J M F. Thermo-Mechanical and High-Temperature Dielectric Properties of Cordierite-Mullite-Alumina Ceramics[J]. Ceramics International, 2016, 42(15): 16897-16905.

[24] Chakraborty A K. Phase Transformation of Kaolinite Clay, 2014 India: Springer. 154-168.

[25] Salma M N, Sayed M, Elmaghraby H F, et al. Fabrication and Properties of Cordierite/Anorthite Composites[J]. Ceramics International, 2017, 43(8): 6024-6028.

[26] Kirat G, Aksan M A. Role of the Fe-Substitution in Dielectric Behavior of the Glass-Ceramic Cordierite Mg2Al4Si5O18 System[J]. Physica B Condensed Matter., 2014, 454(6): 131-134.

[27] Zhang Y, Wang W, Tan R, et al. The Solubility and Temperature Dependence of Resistivity for Aluminum-Doped Zinc Oxide Ceramic[J]. International Journal of Applied Ceramic Technology, 2012, 9(2): 374-381.

[28] Alford N M, Penn S J. Sintered Alumina with Low Dielectric Loss[J]. Journal of Applied Physics, 1996, 80(10): 5895-5898.

[29] Banjuraizah J, Mohamad H, Ahmad Z A. Thermal Expansion Coefficient and Dielectric Properties of Non-Stoichiometric Cordierite Compositions with Excess MgO Mole Ratio Synthesized from Mainly kaolin and Talc by the Glass Crystallization Method[J]. Journal of Alloys & Compounds, 2010, 494(1-2): 256-260.

[30] Gasparini E, Tarantino S C, Ghigna P, et al. Thermal Dehydroxylation of Kaolinite under Isothermal Conditions[J]. Applied Clay Science, 2013, 80-81(4): 417-425.

[31] Johnson S M, Pask J A, Moya J S. Influence of Impurities on High-Temperature Reactions of Kaolinite[J]. Journal of the American Ceramic Society, 2006, 65(1): 31-35.

[32] Wesolowski M. Thermal Decomposition of Talc: A Review[J]. Thermochimica Acta, 1984, 78(1-3): 395-421.

[33] Oliveira F A C, Dias S, Vaz M F, et al. Behaviour of Open-Cell Cordierite Foams under Compression[J]. Journal of the European Ceramic Society, 2006, 26(1-2): 179-186.

[34] Awano M, Takagi H, Kuwahara Y. Grinding Effects on the Synthesis and Sintering of Cordierite[J]. Journal of the American Ceramic Society, 2005, 75(9): 2535-2540.

[35] Shi Z M, Liang K M, Gu S R. Effects of CeO₂ on Phase Transformation towards Cordierite in MgO-Al₂O₃-SiO₂ System[J]. Materials Letters, 2001, 51(1): 68-72.

[36] Banjuraizah J, Mohamad H, Ahmad Z A. Synthesis and Characterization of x MgO-1.5Al₂O₃-5SiO₂, (x= 2.6-3.0) System Using Mainly Talc and Kaolin through the Glass Route[J]. Materials Chemistry & Physics, 2011, 129(3): 910-918.

[37] Wang H G, Herman H. Plasma-Sprayed Cordierite: Dielectric and Electrical Properties[J]. Surface & Coatings Technology, 1989, 37(3): 297-303.

[38] Hamzawy E M, El-Kheshen A A, Zawrah M F. Densification and Properties of Glass/Cordierite Composites[J]. Ceramics International, 2005, 31(3): 383-389.

[39] Jongprateep O, Palomas J. Effects of Mg Addition and Sintering Temperatures on Chemical Compositions, Microstructures, Densities and Dielectric Properties of Strontium Titanate[J]. Ceramics International, 2015, 41: S63-S68.

[40] Abidor I G, Li L H, Hui S W. Studies of Cell Pellets: I. Electrical Properties and Porosity[J]. Biophysical Journal, 1994, 67(1): 418-26.

[41] Zhou X H, Yang X S, Zhang Y Q, et al. Study on the Physics and Dielectric Property of K₂O–B₂O₃–SiO₂/Al₂O₃, Glass + Ceramic[J]. Journal of Materials Science: Materials in Electronics, 2015, 27(9): 1-7.