Mechanical properties and microstructure of blended cement containing modified quartz tailing

Abstract

The amount of inert quartz tailing used in concrete construction is limited due to the low strength development of cementitious materials that may be caused by the quartz tailing. We manage to increase the strength of blended cement by modifying quartz tailing through solid-phase reaction of quartz tailing with carbide slag at high temperature. The mineral composition and morphology of the modified quartz tailing were examined by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The mechanical properties and microstructure of blended cement mortars containing modified quartz tailing were investigated. Results showed that the strengths of blended cement mortars containing modified quartz tailing were close to those of the corresponding blended cement mortars containing quartz tailing at early age of 3 d, but increased significantly to be similar to that of plain Portland cement mortars at late ages of 90 d. This is attributed to the microstructure densification and the enhancement of interface between quartz tailing and cement paste due to the hydration of β-C₂S surface layer on modified quartz tailing.

Keywords

blended cement / modified quartz tailing / strength / microstructure

References

[1] Meyer C. The Greening of the Concrete Industry[J]. Cement and Concrete Composites, 2009, 31(8): 601-605.

[2] Jochen S. Recent Advances in the Field of Cement Hydration and Microstructure Analysis[J]. Cement and Concrete Research, 2011, 41(7): 666-678.

[3] Hubler MH, Thomas JJ, Jennings HM. Influence of Nucleation Seeding on the Hydration Kinetics and Compressive Strength of Alkali Slag Paste[J]. Cement and Concrete Research, 2011, 41(8): 842-846.

[4] Siddique R. Effect of Fine Aggregate Replacement with Class F Fly Ash on the Mechanical Properties of Concrete[J]. Cement and Concrete Research, 2003, 33(4): 539-547.

[5] Zhang YM, Sun W, Yan HD. Hydration of High-Volume Fly Ash Cement Pastes[J]. Cement and Concrete Composites, 2000, 22(6): 445-452.

[6] Lothenbach B, Scrivener K, Hooton RD. Supplementary Cementitious Materials[J]. Cement and Concrete Research, 2011, 41(12): 1244-1256.

[7] Aprianti E, Shafigh P, Bahri S, et al. Supplementary Cementitious Materials Origin from Agricultural Wastes-A Review[J]. Construction and Building Materials, 2015, 74: 176-187.

[8] Xu TY. On the Comprehensive Utilization of Quartz Tail-Sands[J]. Multipurpose Utilization of Mineral Resources, 2005, 6: 33-35.

[9] Xia PF, Wang PM, Li PJ, et al. Characteristics of Morphology on the Interface between Additions and Hardened Cement Paste[J]. Journal of the Chinese Ceramic Society, 1997, 25(6): 738-742.

[10] Yaniv K, Alva P, Ronen C. Influences of Limestone Particle Size Distributions and Contents on Blended Cement Properties[J]. Construction and Building Materials, 2014, 71: 26-34.

[11] Philippe L, Martin C, Erick R. Mineral Admixtures in Mortars Effect of Type, Amount and Fineness of Fine Constituents on Compressive Strength[J]. Cement and Concrete Research, 2005, 35(6): 1092-1105.

[12] Fernando PT, João CG, Said JL. Alkali-Activated Binders: A Review: Part 1. Historical Background Terminology, Reaction Mechanisms and Hydration Products[J]. Construction and Building Materials, 2008, 22(7): 1305-1314.

[13] Fernando PT, João CG, Said JL. Alkali-Activated Binders: A Review: Part 2. About Materials and Binders Manufacture[J]. Construction and Building Materials, 2008, 22(7): 1315-1322.

[14] Shen Y, Xu ZZ, Xie P, et al. A New Method of Enhancing Cement-Aggregate Interfaces, I. Ideal Aggregate and Its Effects on Interfacial Microstructures[J]. Cement and Concrete Research, 1992, 22(4): 612-620.

[15] Shen Y, Xu ZZ, Xie P, et al. A New Method of Enhancing Cement-Aggregate Interfaces, II. Mechanical Properties and Sulphate Attack Resistances of Mortars[J]. Cement and Concrete Research, 1992, 22(5): 769-773.

[16] Hao CW, Deng M, Mo LW, et al. Surface Modification of Fly Ashes with Carbide Slag and Its Effect on Compressive Strength and Autogenous Shrinkage of Blended Cement Pastes[J]. Journal of Wuhan University of Technology-Mater.Sci.Ed., 2012, 27(6): 1149-1153.

[17] Standards Press of China. Standard for Test Method of Cement Chemical Analysis[S]. 2008

[18] Standards Press of China. Standard for Test Methods for Water Requirement of Normal Consistency, Setting Time and Soundness of the Portland Cements[S]. 2001

[19] Shen Y. Ideal Structure of Interface between Cement Paste and Aggregate[D]. 1993 Nanjing: Nanjing Tech University.