Influence of rare earth (Ce and La) addition on the performance of Al-3.0 wt%Mg alloy

Abstract

The influences of rare earth elements (cerium and lanthanum) on the microstructure and phases of Al-3.0 wt%Mg alloys used for electromagnetic shielding wire were characterized by scanning electron microscopy (SEM), energy-dispersive spectroscopy (EDS), X-ray diffraction (XRD) and differential scanning calorimetry (DSC). The mechanical properties and electrical resistivity were also investigated. The results indicated that a certain content of rare earth could improve the purification of the aluminum molten, enhance the strength, and reduce the electrical resistivity of Al-3.0 wt%Mg alloys. The strength reached the top value when RE content was 0.3 wt% while the alloy with 0.2 wt% RE addition had the smallest electrical resistivity. The elongation varied little when RE addition was no more than 0.2 wt%. But the excessive addition of rare earth would be harmful to the microstructure and properties of Al-3.0 wt%Mg alloys.

Keywords

Al-3.0 wt%Mg alloy / Ce and La additions / microstructure / mechanical property / electrical resistivity

References

[1] Jiang S X, Guo R H. Electromagnetic Shielding and Corrosion Resistance of Electroless Ni-P/Cu-Ni Multilayer Plated Polyester Fabric[J]. Surf. Coat. Tech., 2011, 205(17–18): 4274-4279.

[2] Chen X H, Liu J, Zhang Z H, et al. Effect of Heat Treatment on Electromagnetic Shielding Effectiveness of ZK60 Magnesium Alloy[J]. Mater. Des., 2012, 42: 327-333.

[3] Dou Z Y, Wu G H, Huang X L, et al. Electromagnetic Shielding Effectiveness of Aluminum Alloy-fly Ash Composites[J]. Compos. Part. A-Appl. S, 2007, 38(1): 186-191.

[4] Rubeiené V, Baltušnikaité J, Varnaité-Zuravliova S. Development and Investigation of Electromagnetic Shielding Fabrics with Different Electrically Conductive Additives[J]. J. Electrostat., 2015, 75: 90-98.

[5] Chung D D L. Electromagnetic Interference Shielding Effectiveness of Carbon Materials[J]. Carbon., 2001, 39(2): 279-285.

[6] Yang S Y, Lozano K, Lomel A, et al. Electromagnetic Interference Shielding Effectiveness of Carbon Nanofiber/LCP Composites[J]. Compos. Part. A-Appl. S, 2005, 36(5): 691-697.

[7] Kim B R, Lee H K, Park S H. Electromagnetic Interference Shielding Characteristics and Shielding Effectiveness of Polyaniline-coated Films[J]. Thin Solid Film, 2011, 519(11): 3492-3496.

[8] Massimo D E. Drawing Aluminum & Alloy Wires: To Meet Growth in the Aluminum Wire Sector, Wire Drawing Machines Must Offer a Variety of Updated Features Designed to Ensure High Reliability and Trouble-free Operation[J]. Wire & Cable Technology International, 2005, 33(3): 28-29.

[9] Huang X. Progress in the Grain Refinement Technology on 5154 Aluminum Magnesium Alloy Wire[J]. Special Casting & Nonferrous Alloys, 2014, 34(4): 364-366.

[10] Yan H H, Zhang K F. Superplasticity and Fracture Behavior of Fine Grained 5083 Al Alloy[J]. J. Wuhan University of Technology-Mater. Sci. Ed., 2009, 24(5): 800-804.

[11] Huang X, Yan H. Effect of Trace La Addition on the Microstructure and Mechanical Property of As-cast ADC12 Al-Alloy[J]. J. Wuhan University of Technology-Mater. Sci. Ed., 2013, 28(1): 202-205.

[12] Wei X Y, Huang H, Chen Z Y, et al. Microstructure and Mechanical Properties of Al-Mg-Mn-Zr-Er Weld Joints Filled with Al-Mg-Mn-Zr and Al-Mg-Mn-Zr-Er Weld Wires[J]. J. Rare Earth, 2010, 28(4): 627-630.

[13] Aguirre-De la Torre E, Pérez-Bustamante R, Camarillo-Cisneros J, et al. Mechanical Properties of the A356 Aluminum Alloy Modified with La/Ce[J]. J. Rare Earth, 2013, 31(8): 811-816.

[14] Wang X, Chen G Q, Li B. Effect of Sc, Zr and Ti on the Microstructure and Properties of Al alloys with High Mg Content[J]. Rare Metals, 2010, 29(1): 66-71.

[15] Fazeli F, Poole W J, Sinclair C W. Modeling the Effect of Al3Sc Precipitates on the Yield Stress and Work Hardening of an Al-Mg-Sc Alloy[J]. Acta Mater., 2008, 56(9): 1909-1918.

[16] Liu J H, Liang X, Li S M. Study of Microbiologically Induced Corrosion Action on Al-6Mg-Zr and Al-6Mg-Zr-Sc[J]. J. Rare Earth, 2007, 25(5): 609-614.

[17] He Z B, Yin Z M, Lin S, et al. Preparation, Microstructure and Properties of Al-Zn-Mg-Sc Alloy Tubes[J]. J. Rare Earth, 2010, 28(4): 641-646.

[18] Bethencourt M, Botana F J, Calvino J J. Lanthanide Compounds as Environmental Friendly Corrosion Iinhibitiors of Aluminum Alloy[J]. Corro. Sci., 1998, 40(11): 1803-1819.

[19] Duan R B, Bai P K, Yang J, et al. Influence of Rare Earth Modification and Homogenization on the Microstructure and Mechanical Properties of Recycled Can 3004 Aluminum[J]. J. Wuhan University of Technology-Mater. Sci. Ed., 2014, 29(2): 264-268.

[20] Zhang G X, Ma Q C, Guan S K, et al. Effect of Rare Earth Element on Fluidity and Purification of 5052 Aluminum Alloy[J]. Transactions of Materials and Heat Treatment, 2008, 29(4): 83-86.

[21] ASTM. Standard Test Methods for Tension Testing of Metallic Materials, 2004

[22] Cui Z Q, Wu R G. Phase Diagram and Properties of Ternary Al-Mg-Ce Alloys[J]. Acta. Metal. Sin., 1984, 20: 323-331.

[23] Schuster J C, Perring L, Righter K W. The Binary System RE-Al[J]. J. Alloy. Compd., 2001, 320: 224-227.

[24] Popovic M, Romhanji E. Characterization of Micro-structural Changes in an Al-6.8 wt% Mg Alloy by Electrical Resistivity Measurements[J]. Mater. Sci. Eng. A, 2008, 492: 460-467.

[25] Jun Y, Cheng C. Gallium Induced Magnesium Enrichment on Grain Boundary and the Gallium Effect on Degradation of Tensile Properties of Aluminum Alloys[J]. Metal. Mater Tran. A, 2006, 37(7): 2133-2145.