Correlative mechanism of hydraulic-mechanical property in cemented paste backfill

Abstract

Hydraulic characteristic is a good indication of binder hydration, which determines the strength development of cemented paste backfill (CPB). Therefore, the hydraulic characteristic should be communicated with the mechanical property to provide an advanced knowledge that can help mine workers make a rational strategy and reduce the mining cycle. An experimental program was performed to obtain the hydraulic (monitored by suction and volumetric water content) and mechanical properties (unconfined compressive strength (UCS) test) of CPB at the 28 days curing age. According to the monitoring and testing results, the relationships between the hydration reaction rate and volumetric water content (VWC), suction and VWC, suction and UCS were established. The hydration degree showed a liner rise as the VWC decreased. Curves of the VWC and UCS were featured with a nonlinear reduction and nonlinear growth (both are exponential functions) as the suction rising, respectively. These established relationships validated the strong correlative mechanism of hydraulic and mechanics behavior for CPB. Also, the results of the present research indicated that the hydraulic characteristics and mechanical property were strongly coupled. These correlations and couplings will be of great importance to understand the hardening process of CPB and bring to a safe CPB field operation.

Keywords

cemented paste backfill / mine / hydraulic / volumetric water content / suction / strength

References

[1] Franks D M, Boger D V, Cte C M, et al. Sustainable Development Principles for the Disposal of Mining and Mineral Processing Wastes[J]. Resources Policy, 2011, 36: 114-122.

[2] Sivakugana N, Rankineb R M, Rankinea K J, et al. Geotechnical Considerations in Mine Backfilling in Australia[J]. Journal of Cleaner Production, 2006, 14: 1168-1175.

[3] Nasir O, Fall M. Modeling the Heat Development in Hydrating CPB Structures[J]. Computers and Geotechnics, 2009, 36: 1207-1218.

[4] Yin S H, Wu A X, Hu K J, et al. The Effect of Solid Components on the Rheological and Mechanical Properties of Cemented Paste Backfill[J]. Minerals Engineering, 2012, 35: 61-66.

[5] Coussy S, Benzaazoua M, Blanc D, et al. Arsenic Stability in Arsenopyrite-rich Cemented Paste Backfills: A Leaching Test-based Assessment[J]. Journal of Hazardous Materials, 2011, 185: 1467-1476.

[6] Henriquez J, Simms P. Dynamic Imaging and Modelling of Multilayer Deposition of Gold Paste Tailings[J]. Minerals Engineering, 2009, 22: 128-139.

[7] Reid C, Becaert V, Aubertin M, et al. Life Cycle Assessment of Mine Tailings Management in Canada[J]. Journal of Cleaner Production, 2009, 17: 471-479.

[8] Doucet J, Paradis R. Thickening/mud Stacking Technology—an Environmental Approach to Residue Management[C]. Richard Jewell, Andy Fourie. Proceedings of the 13th International Seminar on Paste and Thickened Tailings, 2010 Canada: Australian Centre For Geomechanics.

[9] Abdul-hussain N, Fall M. Thermo-hydro-mechanical Behaviour of Sodium Silicate-cemented Paste Tailings in Column Experiments[J]. Tunnelling and Underground Space Technology, 2012, 29: 85-93.

[10] Abdul-hussain N. Engineering Properties of Gelfill, 2010 Ottawa: University of Ottawa.

[11] Zhang M, Zhang H Y, Zhou L, et al. Temperature Effects on Unsaturated Hydraulic Property of Bentonite-Sand Buffer Backfilling Mixtures[J]. Journal of Wuhan University of Technology-Mater. Sci. Ed., 2013, 28(3): 487

[12] Helinski M, Fourie A, Fahey M. Mechanics of Early Age Cemented Paste Backfill[C]. Proceedings of the 9th International Seminar on Paste and Thickened Tailings, Paste, 2006

[13] Ghirian A, Fall M. Coupled Thermo-Hydro-Mechanical–chemical Behaviour of Cemented Paste Backfill in Column Experiments. Part I: Physical, Hydraulic and Thermal Processes and Characteristics[J]. Engineering Geology, 2013, 164: 195-207.

[14] Abdul-hussain N, Fall M. Unsaturated Hydraulic Properties of Cemented Tailings Backfill that Contains Sodium Silicate[J]. Engineering Geology, 2011, 123: 288-301.

[15] Vergne J. Rules of Thumb for the Hard Rock Mining Industry. Hard Rock Miner’s Handbook, 2000 Tempe: McIntosh Engineering Inc..

[16] Fall M, Celestin J, Pokharel M, et al. A Contribution to Understanding the Effects of Curing Temperature on the Mechanical Properties of Mine Cemented Tailings Backfill[J]. Engineering Geology, 2010, 114: 397-413.

[17] ASTM International. Standard Test Method for Slump of Hydraulic Cement Concrete, 2010

[18] ASTM International. Standard Test Method for Compressive Strength of Cylindrical Concrete Specimens, 2012

[19] Ghirian A, Fall M. Coupled Thermo-hydro-mechanical–chemical Behaviour of Cemented Paste Backfill in Column Experiments. Part II: Mechanical, Chemical and Microstructural Processes and Characteristics[J]. Engineering Geology, 2014, 170: 11-23.

[20] Wang Y, Fall M, Wu A X. Initial Temperature-dependence of Strength Development and Self-desiccation in Cemented Paste Backfill that Contains Sodium Silicate[J]. Cement and Concrete Composites., 2016, 67: 101-110.

[21] Zeng J J, Shui Z H, Wang G M, et al. The Early Hydration and Strength Development of High-strength Precast Concrete with Cement/metakaolin Systems[J]. Journal of Wuhan University of Technology-Mater. Sci. Ed., 2010, 25(4): 712-716.

[22] Li F X, Chen Y Z, Long S Z, et al. Properties and Microstructure of Marine Concrete with Composite Mineral Admixture[J]. Journal of Wuhan University of Technology-Mater. Sci. Ed., 2009, 24(3): 497-501.

[23] Pane I, Hansen W. Concrete Hydration and Mechanical Properties Under Nonisothermal Conditions[J]. ACI Materials Journal, 2002, 99(6): 534-422.

[24] Schindler A K. Effect of Temperature on Hydration of Cementitious Materials[J]. ACI Materials Journal, 2004, 1–2: 72-81.

[25] Hansen T C. Physical Structure of Hardened Cement Paste[J]. Materials and Structures, 1986, 19: 423-436.

[26] Mills R H. Factors Influencing Cessation of Hydration in Water-cured Cement Pastes. Proceeding of the Symposium on the Structure of Portland Cement Paste and Concrete, 1996

[27] Kjellsen K O, Detwiler R J, Gjórv O E. Development of Microstructures in Plain Cement Pastes Hydrated at Different Temperatures[J]. Cement and Concrete Research, 1991, 21: 179-189.

[28] Schindler A K, Folliard K J. Influence of Supplementary Cementing Materials on the Heat of Hydration of Concrete. Advanced in Cement and Concrete IX Conference, 2004

[29] Wu D, Fall M, Cai S J. Coupled Modeling of Temperature Distribution and Evolution in Cemented Tailings Backfill Structures that Contain Mineral Admixtures[J]. Geotechnical and Geological Engineering, 2012, 30: 935-961.