Synthesis of n-alkane mixture microcapsule and its application in low-temperature protective fabric

Abstract

We investigated synthesis and characterization of melamine-urea-formaldehyde (MUF) microcapsules containing n-alkane mixture as phase change core material for thermal energy storage and low- temperature protection. The phase change microcapsules (microPCMs) were prepared by an in situ polymerization using sodium dodecyl sulfate (SDS) and polyvinyl alcohol (PVA) as emulsifiers. Surface morphology, particle size, chemical structure, and thermal properties of microPCMs were, respectively, characterized by using scanning electron microscopy (SEM), field emission scanning electron microscopy (FESEM), Fourier transform infrared spectroscopy (FT-IR), differential scanning calorimetry (DSC), and thermal gravimetric analysis (TGA). Low-temperature resistance performances were measured at -15, -30, -45, and -60 °C after microPCMs were coated on a cotton fabric by foaming technology. The results showed that spherical microPCMs had 4.4 μm diameter and 100 nm wall thickness. The melting and freezing temperatures and the latent heats of the microPCMs were determined as 28.9 and 29.6 °C as well as 110.0 and 115.7 J/g, respectively. Encapsulation of n-alkane mixture achieved 84.9 %. TGA analysis indicated that the microPCMs had good chemical stability below 250 °C. The results showed that the microencapsulated n-alkane mixture had good energy storage potential. After the addition of 10 % microPCMs, low-temperature resistance duration was prolonged by 126.9%, 145.5%, 128.6%, and 87.5% in environment of -15, -30, -45 and -60 °C, respectively as compared to pure fabric. Based on the results, phase change microcapsule plays an effective role in lowtemperature protection field for the human body.

Keywords

low-temperature resistance / phase change microcapsules / thermal property / melamine-ureaformaldehyde resin

References

[1] Mobllor P, Capablanca L, Gisbert J, et al. Improvement of Microcapsule Adhesion to Fabrics[J]. Textil. Res. J., 2010, 80: 631-635.

[2] Zhang P, Ma ZW, Wang RZ. An Overview of Phase Change Material Slurries: MPCS and CHS[J]. Renew. Sust. Energ. Rev., 2010, 14: 598-614.

[3] Jin ZG, Wang YD, Liu JG, et al. Synthesis and Properties of Paraffin Capsules as Phase Change Materials[J]. Polymer, 2008, 49: 2903-2910.

[4] Mondal S. Phase Change Materials for Smart Textiles-an Overview[J]. Appl. Therm. Eng., 2007, 8: 1-15.

[5] Chen MZ, Zheng SP, Wu SP, et al. Melting Intercalation Method to Prepare Lauric Acid/Organophilic Montmorillonite Shape-Stabilized Phase Change Material[J]. J. Wuhan. Univ. Technol., 2010, 25(4): 674-677.

[6] Meng D, Wang LJ. Characterization and Thermal Conductivity of Modified Graphite/Fatty Acid Eutectic/PMMA Form-Stable Phase Change Material[J]. J. Wuhan. Univ. Technol., 2013, 28(3): 586-597.

[7] Zhang L, Dong XP, Zhang H. Application Research on Self-Healing Technology with Microcapsules for Automobile Brake Pad[J]. J. Wuhan. Univ. Technol., 2009, 24(1): 91-94.

[8] Ji HX, Sellan Daniel P, Pettes Michael T, et al. Enhanced Thermal Conductivity of Phase Change Materials with Ultrathin-Graphite Foams for Thermal Energy Storage[J]. Energ Environ. Sci., 2014, 7: 1185-1192.

[9] Zhang ZG, Zhang N, Peng J, et al. Preparation and Thermal Energy Storage Properties of Paraffin/Expanded Graphite Composite Phase Change Material[J]. Appl. Energ., 2012, 91(1): 426-431.

[10] Xin CZ, Tian YC, Wang TW, et al. A Effect of Curing Temperature on the Performance of Microencapsulated Low Melting Point Paraffin Using Urea-Formaldehyde Resin as a Shell[J]. Text. Res. J., 2013 1-9.

[11] Shan XL, Wang JP, Zhang XX, et al. Formaldehyde-Free and Thermal Resistant Microcapsules Containing N-octadecane[J]. Thermochim. ACTA, 2009, 494: 104-109.

[12] Li G, Feng YQ, Gao P, et al. Preparation of Mono-Dispersed Polyurea- Urea Formaldehyde Double Layered Microcapsules[J]. Polym. Bull., 2008, 60(5): 725-731.

[13] Su JF, Wang LX, Ren L. Fabrication and Thermal Properties of MicroPCMs: Used Melamine-Formaldehyde Resin as Shell Material[J]. J. Appl. Polym. Sci., 2006, 101: 1522-1528.

[14] Tong XM, Zhang M, Wang MS, et al. Effects of Surface Modification of Self-Healing Poly (Melamine-Urea-Formaldehyde) Microcapsules on the Properties of Unsaturated Polyester Composites[J]. J. Appl. Polym. Sci., 2013, 127(5): 3954-3961.