Physical properties of Al-doped ZnO and Ga-doped ZnO thin films prepared by direct current sputtering at room temperature

Abstract

Al-doped zinc oxide (AZO) and Ga-doped zinc oxide (GZO) thin films with the same doping concentration (3.6 at%) were deposited on glass substrates at room temperature by direct current (DC) magnetron sputtering. Consequently, we comparatively studied the doped thin films on the basis of their structural, morphological, electrical, and optical properties for optoelectronic applications. Both thin films exhibited excellent optical properties with more than 85% transmission in the visible range. The GZO thin film had better crystallinity and smoother surface morphology than the AZO thin film. The conductivity of the GZO thin film was improved compared to that of the AZO thin film: the resistivity decreased from 1.01 × 10^-3 to 3.5 × 10^-4 Ω cm, which was mostly due to the increase of the carrier concentration from 6.5 ×10²⁰ to 1.46 × 10²¹ cm^-3. These results revealed that the GZO thin film had higher quality than the AZO thin film with the same doping concentration for optoelectronic applications.

Keywords

room temperature / ZnO / thin films / sputtering / electrical properties

References

[1] Kim J P, Bae J S, Hong T E, et al. Optical and Electrical Properties of ZnO Films, Codoped with Al and Ga Deposited at Room Temperature by an RF Sputtering Method[J]. Thin Solid Films, 2010, 518: 6179-6183.

[2] He L, Li Z, Zhang Z. Rapid, Low-Temperature Synthesis of Single-Crystalline Co₃O₄ Nanorods on Silicon Substrates on a Large Scale[J]. Nanotechnology, 2008, 19: 155606.

[3] Zhang D H, Yang T L, Ma J, et al. Preparation of Transparent Conducting ZnO:Al Films on Polymer Substrates by R. F. Magnetron Sputtering[J]. Appl. Surf. Sci., 2000, 158: 43-48.

[4] Wang X, Zeng X, Huang D, et al. The Properties of Al Doped ZnO Thin Films Deposited on Various Substrate Materials by RF Magnetron Sputtering[J]. J. Mater. Sci. Mater. Electron., 2012, 23: 1580-1586.

[5] Anura P S, Luís M F R, Vitor G, et al. Cohesive Strength of Nanocrystalline ZnO:Ga Thin Films Deposited at Room Temperature[J]. Nanoscale. Res. Lett., 2011, 6: 309.

[6] Elmas S, Korkmaz S. Deposition of Al Doped ZnO Thin Films on the Different Substrates with Radio Frequency Magnetron Sputtering[J]. J. Non-Cryst. Solids, 2013, 359: 69-72.

[7] Tian J, Zhang Q, Uchaker E, et al. SnO-Nanocluster Modified Anatase TiO₂ Photocatalyst: Exploiting the Sn(II) Lone Pair for a New Photocatalyst Material with Visible Light Absorption and Charge Carrier Separation[J]. J. Mater. Chem. A, 2013, 1: 6770-6677.

[8] Wang Z A, Chu J B, Zhu H B, et al. Growth of ZnO:Al Films by RF Sputtering at Room Temperature for Solar Cell Applications[J]. Solid-State. Electron., 2009, 53: 1149-1153.

[9] Jin C G, Yu T, Wu Z F, et al. Room-Temperature Deposition of Transparent Conductive Al-doped ZnO Thin Films Using Low Energy Ion Bombardment[J]. Appl. Phys. A., 2012, 106: 961-966.

[10] Mohanty B C, Yeon D H, Yun J H, et al. RF Power Dependence of Refractive Index of RoomTemperature Sputtered ZnO:Al Thin Films[J]. Appl. Phys. A, 2014, 115: 347-351.

[11] Abduev A K, Akhmedov A K, Asvarov A S. The Structural and Electrical Properties of Ga-doped ZnO and Ga, B-codoped ZnO Thin Films: The Effects of Additional Boron Impurity[J]. Sol. Energ. Mat. Sol. C, 2007, 91: 258-260.

[12] Kwak D J, Park M W, Sung Y M. Discharge Power Dependence of Structural and Electrical Properties of Al-doped ZnO Conducting Film by Magnetron Sputtering (for PDP)[J]. Vacuum, 2009, 83: 113-118.

[13] Tao K, Sun Y, Cai H, et al. Deposition Ga-doped ZnO Films on PEN Substrate at Room Temperature for Thin Film Silicon Solar Cells[J]. Appl. Surf. Sci., 2012, 258: 5943-5946.

[14] Pei Z L, Zhang X B, Zhang G P, et al. Transparent Conductive ZnO:Al Thin Films Deposited on Flexible Substrates Prepared by Direct Current Magnetron Sputtering[J]. Thin Solid Films, 2006, 497: 20-23.

[15] Guillén C, Herrero J. Structure, Optical and Electrical Properties of Al:ZnO Thin Films Deposited by DC Sputtering at Room Temperature on Glass and Plastic Substrates[J]. Phys. Status Solidi A, 2009, 206: 1531-1536.

[16] Lee B T, Kim T H, Jeong S H. Growth and Characterization of Single Crystalline Ga-doped ZnO Films Using RF Magnetron Sputtering[J]. J. Phys. D: Appl. Phys., 2006, 39: 957-961.

[17] Jun M C, Park S U, Koh J H. Comparative Studies of Al-doped ZnO and Ga-doped ZnO Transparent Conducting Oxide Thin Films[J]. Nanoscale. Res. Lett., 2012, 7: 639.

[18] Lennon C, Tapia R, Kodama R, et al. Effects of Annealing in a Partially Reducing Atmosphere on Sputtered Al-doped ZnO Thin Films[J]. J. Electron. Mater., 2009, 38: 1568-1573.

[19] Zhu K, Yang Y, Wei T F, et al. Effects of Post-rapid Thermal Annealing on Structural, Electrical and Optical Properties of Hydrogenated Aluminum Doped Zinc Oxide Thin Films[J]. J. Mater. Sci: Mater. Electron., 2013, 24: 3844-3849.

[20] Kim J M, Thiyagarajan P, Rhee S W. Direct Growth of Large Grain Polycrystalline Silicon Films on Aluminum-induced Crystallization Seed Layer Using Hot-Wire Chemical Vapor Deposition[J]. Thin Solid Films, 2010, 518: 5860-5865.

[21] Zhu K, Yang Y, Wei T F, et al. Room Temperature DC Magnetron Sputtering Deposition of Hydrogenated Aluminum Doped Zinc Oxide Thin Films on Polyethylene Terephthalate Substrates[J]. Mater. Lett., 2013, 106: 363-365.

[22] Jullien M, Horwat D, Manzeh F, et al. Influence of the Nanoscale Structural Features on the Properties and Electronic Structure of Aldoped ZnO Thin Films: an X-ray Absorption Study[J]. Sol. Energ. Mat. Sol. C, 2011, 95: 2341-2346.

[23] Fang G, Lia D, Yao B L. Fabrication and Vacuum Annealing of Transparent Conductive AZO Thin Films Prepared by DC Magnetron Sputtering[J]. Vacuum, 2003, 68: 363-372.

[24] Yue H, Wu A, Feng Y, et al. Structures and Properties of the Aldoped ZnO Thin Films Prepared by Radio Frequency Magnetron Sputtering[J]. Thin Solid Films, 2011, 519: 5577-5581.

[25] Burstein E. Anomalous Optical Absorption Limit in InSb[J]. Phys. Rev., 1954, 93: 632-633.

[26] Moss T S. The Interpretation of the Properties of Indium Antimonide[J]. Proc. Phys. Soc. B, 1954, 67: 775.