Sulfate attack resistance of air-entrained silica fume concrete under dry-wet cycle condition

Abstract

Based on the erosion resistant coefficient, the effects of water-cement ratio, air-entrained, silica fume content and sand ratio on the sulfate attack resistance of air-entrained silica fume concrete were studied by orthogonal experiments in order to explore its sulfate attack resistance under dry-wet condition. A more significant model of concrete resistance to sulfate attack was also established, thus this work provided a strategy reference for quantitative design of sulfate attack resistant concrete. The experimental results show that dry-wet cycle deteriorates the concrete resistance to the sulfate attack, and leads to the remarkable declines of concrete strength and sulfate resistance. Air bubbles in the air-entrained silica fume concrete lower and delay the damage resulted from the crystallization sulfate salt. However this delay gradually disappears when most of the close bubbles are breached by the alternative running of the sulfate salt crystallization and the permeating pressure, and then the air bubbles are filled with sulfate salt crystallization. The concrete is provided with the strongest sulfate resistance when it is prepared with the 0.47 water-binder ratio, 6.0% air-entrained, 5% silica fume and 30% sand ratio. The erosion resistant coefficients K ₈₀ and K ₁₅₀ of this concrete are increased by 9%, 7%, 9%, and 5% respectively as compared with those of concretes without silica fume and air entraining.

Keywords

air-entrained silica fume concrete / sulfate attack / dry-wet cycles / erosion resistant coefficient / ratio of strength loss / erosion resistant model

References

[1] Zuo X, Sun W. Full Process Analysis of Damage and Failure of Concrete Subjected to External Sulfate Attack[J]. Journal of the Chinese Ceramic Society, 2009, 37(7): 1063-1067.

[2] Bensted J, Barnes P. Structure and Performance of Cements-Second Edition[M], 2000 London, Britain: Spon press.

[3] Ahcene M, Fattoum K. Pozzolan Concrete Durability on Sulphate Attack[J]. Procedia Engineering, 2015, 114: 832-837.

[4] Mathias M, De Belie N. Resistance of Concrete and Mortar Against Combined Attack of Chloride and Sodium Sulphate[J]. Cement and Concrete Composites, 2014, 53: 59-72.

[5] Jiang Z, Li W, Yuan Z. Influence of Mineral Additives and Environmental Conditions on the Self-healing Capabilities of Cementitious Materials[J]. Cement and Concrete Composites, 2015, 57: 116-127.

[6] Jiang L, Niu D, Yuan L, et al. Durability of Concrete under Sulfate Attack Exposed to Freeze-thaw Cycles[J]. Cold Regions Science and Technology, 2015, 112: 112-117.

[7] Oliveira I, Sergio HP, Antonio Aguado C. New Kinetic Model to Quantify the Internal Sulfate Attack in Concrete[J]. Cement and Concrete Research, 2013, 43: 95-104.

[8] Zuo X, Sun W, Yu C. Numerical Investigation on Expansive Volume Strain in Concrete Subjected to Sulfate Attack[J]. Construction and Building Materials, 2012, 36: 404-410.

[9] Jiang Z, Sun Z, Wang P. Autogenous Relative Humidity Change and Autogenous Shrinkage of High-performance Cement Pastes[J]. Cement and Concrete Research, 2005, 35(8): 1539-1545.

[10] Jiang Z, Sun Z, Wang P. Internal Relative Humidity Distribution in Cement Paste Due to Moisture Diffusion and Self-desiccation[J]. Cement and Concrete Research, 2006, 36(2): 320-325.

[11] Niels T, Sadananda S. Mechanism of Concrete Deterioration Due to Salt Crystallization[J]. Materials Characterization, 2004, 53: 123-127.

[12] Yang Q, Zhu B. Deterioration of Concrete Due to Action of Salt Crystallization[J]. Journal of Building Materials, 2007, 10(4): 392-396.

[13] Yang Q, Huang Sh. Characteristics of Air-entrained Concrete[J]. Concrete, 2008, 5: 5-6.

[14] Khan MI, Siddique R. Utilization of Silica Fume in Concrete: Review of Durability Properties[J]. Resources Conservation and Recycling, 2011, 57: 30-35.

[15] Neville A. The Confused World of Sulfate Attack Concrete[J]. Cement and Concrete Research, 2004, 34: 1275-1296.

[16] Han Y, Zhang J, Gao Y. Review of Sulfate Attack on Concrete[J]. Concrete, 2011, 1: 52-61.

[17] Flatt RJ. Salt Damage in Porous Materials: How High Super Saturations are Generated[J]. Journal of Crystal Growth, 2002, 242(3–4): 435-454.

[18] Li X, Lv Y, Ma B, et al. Utilization of Municipal Solid Waste Incineration Bottom Ash in Blended Cement[J]. Journal of Cleaner Production, 2012, 32: 96-100.