Relationships between modified methylene blue value of microfines in manufactured sand and concrete properties

Abstract

To better understand and assess the effect of microfines on concrete properties, the synergetic effect of methylene blue value and content of microfines on properties of low and high strength concrete was studied and then the relationships between the index of modified methylene blue value (MMBV) and concrete properties were investigated. The results show that relationships between MMBV and fresh and hardened properties of concrete can be fully established, and the correlation between MMBV and C60 concrete property is higher than the correlation between MMBV and C30 concrete. With the increase of MMBV, concrete workability and frost resistance decrease while drying shrinkage decreases; however, compressive strength and chloride-ion penetration resistance of C30 concrete have not been negatively affected whereas those of C60 concrete are significantly deteriorated when MMBV exceeds 100. To make use of microfines without remarkably damaging concrete quality, it is suggested that MMBV of microfines in MS used in C30 and C60 concrete be no more than 100.

Keywords

microfines / manufactured sand / modified methylene blue / low and high strength / concrete

References

[1] Quiroga PN, Ahn N, Fowler DF. Concrete Mixture with High Microfines[J]. ACI Mater. J., 2006, 103(4): 258-264.

[2] Koehler EP, Fowler DW. Dust-of-fracture Aggregate Microfines in Selfconsolidating Concrete[J]. ACI Mater. J., 2008, 105(2): 165-173.

[3] Neville AM. Properties of Concrete[M], 1995 New York: John Wiley and Sons, Inc..

[4] General Administration of Quality Supervision InspectionQuarantine of the People’s Republic of China. Sand for Construction[S], 2011

[5] American Association of State Highway Transportation Officials. Standard Method of Test for the Qualitative Detection of Harmful Clays of the Smectite Group in Aggregates Using Methylene Blue[S], 2007

[6] European Committee for Standardization. Tests for Geometrical Properties of Aggregates-Part 9: Assessment of Fines-Methylene Blue Test [S], 2009

[7] Norvell JK, Stewart JG, Juenger MCG, et al. Influence of Clay and Clay-sized Particles on Concrete Performance[J]. J Mater. Civil. Eng., 2007, 19(12): 1053-1059.

[8] Li BX, Zhou MK, Wang JL. Effect of the Methylene Blue Value of Manufactured Sand on Performance of Concrete[J]. Constr. Build. Mater., 2011, 9(2): 127-132.

[9] Courard L, Michel F, Pierard J. Influence of Clay in Limestone Fillers for Self-compacting Cement Based Composites[J]. Constr. Build. Mater., 2011, 25(3): 1356-1361.

[10] Hu B, Liu JP, Liu JZ. Study on the Relationship between Clay Content, MB Value and Drying Shrinkage of Mortar[J]. Concrete, 2010, 4: 107-109.

[11] Hosking JR, Pike DC. The Methylene Blue Dye Adsorption Test in Relation to Aggregate Drying Shrinkage[J]. J. Chen. Technol. Biotechnol, 1985, 35(4): 185-194.

[12] Yool AIG, Lees TP, Fried A. Improvements to the Methylene Blue Dye Test for Harmful Clay in Aggregates for Concrete and Mortar[J]. Cem. Concr. Res., 1998, 28(10): 1417-1428.

[13] Ramirez JL, Barcena JM, Urreta JI. Proposal for Limitation and Control of Fines in Calcareous Sands Based upon Their Influence in Some Concrete Properties[J]. Mater. Struct., 1990, 23(4): 277-288.

[14] Topcu IB, Demir A. Relationship between Methylene Blue Values of Concrete Aggregates Fines and Some Concrete Properties[J]. Can. J. Civ. Eng., 2008, 35(4): 379-383.

[15] Muñoz JF, Tejedor MI, Anderson MA, et al. Detection of Aggregate Clay Coatings and Impacts on Concrete[J]. ACI Mater. J., 2010, 107(4): 387-395.

[16] Ministry of Construction of the People’s Republic of China. Standard for Test Method of Performance on Ordinary Fresh Concrete[S], 2002

[17] Ministry of Construction of the People’s Republic of China. Standard for Test Method of Mechanical Properties on Ordinary Concrete[S], 2002

[18] Ministry of HousingUrban-Rural Development of the People’s Republic of China. Standard for Test Methods of Long-term Performance and Durability of Ordinary Concrete[S], 2009

[19] Ng S, Plank J. Interaction Mechanisms between Na Montmorillonite Clay and MPEG-based Polycarboxylate Superplasticizers[J]. Cem. Concr. Res., 2012, 42(6): 847-854.

[20] Fernandes VA, Purnell P, Still GT, et al. The Effect of Clay Content in Sands Used for Cementitious Materials in Developing Countries[J]. Cem. Concr. Res., 2007, 37(5): 751-758.

[21] Felekoglu B. A Comparative Study on the Performance of Sands Rich and Poor in Fines in Self-compacting Concrete[J]. Constr. Build. Mater., 2008, 22(4): 646-654.

[22] ASTM International. Standard Test Method for Electrical Indication of Concrete’s Ability to Resist Chloride Ion Penetration[S], 2005

[23] Fagerlund G. The Critical Degree of Saturation Method of Assessing the Freeze/Thaw Resistance of Concrete[J]. Mater. Struct., 1977, 10(58): 379-382.

[24] China Civil Engineering Society. Guide to Durability Design and Construction of Concrete Structures[S], 2004

[25] Topcu IB, Ugurlu A. Effect of the Use of Mineral Filler on the Properties of Concrete[J]. Cem. Concr. Res., 2003, 33(7): 1071-1075.

[26] Li BX, Wang JL, Zhou MK. Effect of Limestone Fines Content in Manufactured Sand on Durability of Low-and High-strength Concrete[J]. Constr. Build. Mater., 2009, 23(8): 2846-2850.

[27] Celik T, Marar K. Effect of Crushed Stone Dust on Some Properties of Concrete[J]. Cem. Concr. Res., 1993, 26(7): 1124-1130.