Effect of diatomite additive on the mechanical and dielectric properties of porous SiO₂-Si₃N₄ composite ceramics

Abstract

Porous SiO₂-Si₃N₄ composite ceramics with high porosity and excellent mechanical properties were fabricated by pressureless-sintering at relatively low temperature of 1 500 °C using diatomite as pore forming agent. The effects of diatomite on flexural strength, fracture toughness, shrinkage, porosity and phase transformation of the porous ceramics were investigated in detail. Compared with that of the ceramic without adding diatomite, the porosity of the ceramic with 10% diatomite is increased by about 27.4%, the flexural strength and fracture toughness reaches 78.04 MPa and 1.25 MPa·m^1/2, respectively. As the porosity increases, the dielectric constant of porous SiO₂-Si₃N₄ ceramic decreases obviously from 3.65 to 2.95.

Keywords

silicon nitride / diatomite / porosity / mechanical property / dielectric constant

References

[1] Pyzik AJ, Beaman DR. Microstructure and Properties of Self-reinforced Silicon Nitride[J]. J. Am. Ceram. Soc., 1993, 76(11): 2737-2744.

[2] Chen DY, Zhang BL, Zhuang HR, et al. Combustion Synthesis of Network Silicon Nitride Porous Ceramics[J]. Ceram. Int., 2003, 29(4): 363-364.

[3] Fukasawa T, Deng ZY, Ando M, et al. Synthesis of Porous Silicon Nitride with Unidirectionally Aligned Channels Using Freeze-drying Process[J]. J. Am. Ceram. Soc., 2002, 85(9): 2151-2155.

[4] Takahashi M, Fa-Zhi Z, Kato T, et al. Gelcasting Fabrication of Porous Ceramics Using a Continuous Process[J]. J. Eur. Ceram. Soc., 2006, 26(4-5): 667-671.

[5] Sepulveda P, Binner JGP. Processing of Cellular Ceramics by Foaming and In Situ Polymerisation of Organic Monomers[J]. J. Eur. Ceram. Soc., 1999, 19(12): 2059-2066.

[6] Diaz A, Hampshire S. Characterisation of Porous Silicon Nitride Materials Produced with Starch[J]. J. Eur. Ceram. Soc., 2004, 24(2): 413-419.

[7] Zhang RB, Fang DN, Pei YM, et al. Microstructure, Mechanical and Dielectric Properties of Highly Porous Silicon Nitride Ceramics Produced by A New Water-based Freeze Casting[J]. Ceram. Int., 2012, 38(5): 4373-4377.

[8] Jia DC, Zhou Y, Lei TC. Ambient and Elevated Temperature Mechanical Properties of Hot-pressed Fused Silica Matrix Composite[J]. J. Eur. Ceram. Soc., 2003, 23(5): 801-808.

[9] Kicevic D, Gasic M, Markovic D. A Statistical Analysis of the Influence of Processing Conditions on the Properties of Fused Silica[J]. J. Eur. Ceram. Soc., 1996, 16(8): 857-864.

[10] Lyons JS, Starr TL. Strength and Toughness of Slip-cast Fused-silica Composites[J]. J. Am. Ceram. Soc., 1994, 77(6): 1673-1675.

[11] Li XM, Yin XW, Zhang LT, et al. Mechanical and Dielectric Properties of Porous Si₃N₄-SiO₂ Composite Ceramics[J]. Mat. Sci. Eng. a-Struct., 2009, 500(1-2): 63-69.

[12] Xia YF, Zeng YP, Jiang DL. Dielectric and Mechanical Properties of Porous Si₃N₄ Ceramics Prepared via Low Temperature Sintering[J]. Ceram. Int., 2009, 35(4): 1699-1703.

[13] Martinovic S, Vlahovic M, Boljanac T, et al. Preparation of Filter Aids Based on Diatomites[J]. International Journal of Mineral Processing, 2006, 80(2-4): 255-260.

[14] Lu Y, Yang J, Lu W, et al. Synthesis of Porous Silicon Nitride Ceramics from Diatomite[J]. Mater. Manuf. Process., 2010, 25(9): 998-1000.

[15] Hadjar H, Hamdi B, Jaber M, et al. Elaboration and Characterisation of New Mesoporous Materials from Diatomite and Charcoal[J]. Micropor. Mesopor. Mat., 2008, 107(3): 219-226.

[16] Wu JH, Guo JK, Li BS. Preparation and Properties of SiO₂ Matrix Composites Doped with AlN Particles[J]. J. Mater. Sci., 2000, 35(19): 4895-4900.

[17] Shan SY, Yang JF, Gao JQ, et al. Porous Silicon Nitride Ceramics Prepared by Reduction-nitridation of Silica[J]. J. Am. Ceram. Soc., 2005, 88(9): 2594-2596.