Effect of substrate movement speed by synchronous rolling-casting freeform manufacturing for metal on microstructure and mechanical property of ZL104 aluminum alloy slurry

Abstract

Synchronous rolling-casting freeform manufacturing for Metal (SRCFMM) means that the refined liquid metal is continuously pressed out from the bottom of crucible. There is a horizontal movable plate beneath the outlet. The clearance between the outlet and the plate is about several hundred micrometers. SRCFMM, similar to additive manufacturing, implies layer by layer shaping and consolidation of feedstock to arbitrary configurations, normally using a computer controlled movable plate. The primary dendritic crystal is easily crushed by movement of substrate in the rolling-casting area. ZL104 was used as the test materials, determining the control temperature by differential scanning thermal analysis (DSC), preparing a kind of samples by SR CFMM, then analyzing microstructures and mechanical property of the samples. Characteristics and distribution of the primary particles were assessed by optical microscopy (OM), scanning electron microscopy (SEM), energy dispersive spectrum (EDS) and image analysis software. Mechanical property of the samples was assessed by vickers hardness. The results show that the samples fabricated by SRCFMM have uniform structures and good performances with the velocity of the substrate controlled about 10 cm/s and temperature at about 580 °C.

Keywords

synchronous rolling-casting / additive manufacturing technology / temperature / substrate movement speed

References

[1] Orme M. Method for Droplet Stream Manufacturing[P]. US Patent 517136, 1992

[2] Orme M. On the Genesis of Droplet Stream Micro Speed Dispersions[J]. Physics of Fluids A-Fluid Dynamics, 1991, 3(12): 2936-2947.

[3] Orme M. A Novel Technique of Rapid Solidification Net-Form Materials Synthesis[J]. Journal of Materials Engineering and Performance, 1993, 2(3): 399-407.

[4] Rice C S, Mendez P F, Brown S B. Metal Solid Freeform Fabrication Using Semi-solid Slurries[J]. JOM, 2000, 52(12): 31-33.

[5] HAQUE M M, SHARIF A. Study on Wear Properties of Aluminiumsilicon Piston Alloy [J]. Journal of Materials Processing Technology, 2001, 118(1/3): 69-73.

[6] ATKINSON H V. Modelling the Semisolid Processing of Metallic Alloys [J]. Progress in Materials Science, 2005, 50(3): 341-412.

[7] YANG X-r, MAO W-m, PEI Sheng. Preparation of Semisolid A356 Alloy Feedstock Cast Through Vertical Pipe [J]. Materials Science and Technology, 2007, 23(9): 1049-1053.

[8] LUO S-j, TIAN W-t, XIE S-s, et al. Semi-solid Processing Technology and Application [J]. The Chinese Journal of Nonferrous Metals, 2000, 10(6): 765-769.

[9] YANG X-r, MAO W-m, PEI Sheng. Influence of Process Parameters on Microstructure of Semisolid A356 Alloy Slug Cast Through Vertical Pipe [J]. Transactions of Nonferrous Metals Society of China, 2008, 18(1): 99-103.

[10] LUKASSON M, APELIAN D, DASGUPTA R. Alloy Characterization for the New UBE Rheocasting Process [J]. AFS Transactions, 2002, 110: 271-284.

[11] LEGORETTA E C, ATKINSON H V, JONES H. Cooling Slope Casting to Obtain Thixotropic Feedstock. II: Observations with A356 Alloy [J]. Journal of Materials Science, 2008, 43(16): 5456-5469.

[12] Masoud Mohammadi R, Morteza T, Seyed Mohammad A B, et al. Characterization of the Graded Distribution of Primary Particles and Wear Behavior in the A390 Alloy Ring with Various Mg Contents Fabricated by Centrifugal Casting [J]. Materials & Design, 2014, 56: 105-111.

[13] Rahvard M M, Tamizifar M, Boutorabi M A, et al. Effect of Superheat and Solidified Layer on Achieving Good Metallic Bond Between A390/A356 Alloys Fabricated by Cast-decant-cast Process [J]. Transactions of Nonferrous Metals Society of China, 2014, 24(3): 665-672.

[14] Finke S, Feenstra F K. Solid Freeform Fabrication by Extrusion and Deposition of Semi-solid Alloys[J]. Journal of Materials Science, 2002, 37(15): 3101-3106.

[15] Flemings M C, Goodwin F E. Method for Making Alloy Compositions and Composition[P]. U S Patent, 4295896, 1981-10-20

[16] Kirkwood D H, Suery M, Kapranos P, et al. Semi-solid Processing of Alloys: Evolution of Microstructure in Semi-solid Alloys During Isothermal Holding [J]. Materials Science, 2010, 124: 23-34.

[17] Gupta M, Ling S. Microstructure and Mechanical Properties of Hypo/ Hyper-eutectic Al–Si [J]. Journal of Alloys and Compounds, 1999, 287: 284-294.

[18] Zhang Z, Li T, Yue H, et al. Study on the Preparation of Al–Si Functionally Graded Materials Using Power Ultrasonic Field [J]. Materials & Design, 2009, 30(3): 851-856.

[19] Samuel A M, Doty H W, Valtierra S, et al. Relationship Between Tensile and Impact Properties in Al-Si-Cu-Mg Cast Alloys and Their Fracture Mechanisms [J]. Materials & Design, 2014, 53: 938-946.

[20] Samuel A M, Doty H W, Valtierra S, et al. Defects Related to Incipient Melting in Al-Si-Cu-Mg Alloys [J]. Materials & Design, 2013, 52: 947-956.